Preparation method of water-based deodorizing inorganic coating

An inorganic coating, water-based technology, applied in the field of coatings, can solve problems such as difficult to meet multi-function, single function, etc., to meet multi-functional requirements, good antibacterial effect, and improve stability

Inactive Publication Date: 2016-11-09
佛山市高明区尚润盈科技有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing water-based inorganic coatings have a single function, and it is difficult to meet the multi-functional characteristics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-based deodorizing inorganic coating
  • Preparation method of water-based deodorizing inorganic coating
  • Preparation method of water-based deodorizing inorganic coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of porous graphene loaded silver / titanium dioxide antibacterial composite material, it comprises the following steps:

[0032] (1) Preparation of graphene quantum dot suspension: weigh 0.5g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 3g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 5 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was p...

Embodiment 2

[0039] A kind of preparation method of porous graphene loaded silver / titanium dioxide antibacterial composite material, it comprises the following steps:

[0040] (1) Preparation of graphene quantum dot suspension: weigh 0.6g of C60 powder, measure 50-100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, At the same time, stir at a speed of 500rpm to obtain a mixed solution; weigh 1g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 7 hours; quickly add 200ml of pure water, filtered, and then dialyzed with a dialysis bag with a molecular weight cut-off of 1000 for 3 days to obtain a suspension of graphene quantum dots; stir the suspension of graphene quantum dots at a speed of 100rpm, and irradiate the laser for 45min a...

Embodiment 3

[0047] A kind of preparation method of porous graphene loaded silver / titanium dioxide antibacterial composite material, it comprises the following steps:

[0048] (1) Preparation of graphene quantum dot suspension: Weigh 0.8g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 0.5g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 8 hours; quickly add 100ml Pure water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000, to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of water-based deodorizing inorganic coating. The preparation method comprises the following steps: (1) dispersing diatomite in an aqueous solution, and dropwise adding an antibacterial compound aqueous dispersion; standing, carrying out suction filtering, washing, and drying to obtain a diatomite / antibacterial compound; (2) mixing and stirring water with a defoaming agent, adding pigments, a filling agent and a diatomite / inorganic oxide, and stirring to obtain a solution A; (3) mixing silicon sol with a polymer solution, and sufficiently stirring; adding the diatomite / antibacterial compound, and stirring to obtain a solution B; (4) adding a film-forming additive and a thickening agent into the solution B, and sufficiently stirring to obtain a solution C; and (5) dropwise adding the solution C into the solution A, and sufficiently stirring and filtering. By reasonably matching the diatomite / inorganic oxide and diatomite / antibacterial composite material and by virtue of synergistic effect of functional additives, the inorganic coating has excellent antibacterial property and formaldehyde resistance, meets the multifunctional requirement and further widens the application of the inorganic coating.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a preparation method of a water-based deodorizing inorganic coating. Background technique [0002] Inorganic coatings mainly refer to coatings prepared by using silicate and phosphate compounds as binders, adding various pigments, fillers, additives, and curing agents. Among them, silicate polymer compounds can be divided into alkali metal Silicates and silica sols. This kind of coating with inorganic binder as the film-forming substance has low film-forming temperature, excellent weather resistance, very stable under the action of ultraviolet light, good heat resistance, non-combustible in case of fire, and good resistance to heat. Pollution, not easy to absorb dust, can maintain a bright decorative effect, no volatile organic compounds are produced during production and use, will not pollute the environment, rich raw material resources, low cost and other advantages, so it ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/14C09D7/12
CPCC09D1/00C09D5/14
Inventor 陆庚
Owner 佛山市高明区尚润盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com