Carbon-containing slag suppression cold-bonded pellet and utilization method thereof

A technology for cold-solidifying pellets and metallurgical waste, applied in the field of steelmaking, can solve the problem of high cost and achieve the effects of reducing iron consumption, efficient utilization and low cost

Active Publication Date: 2016-11-23
王虎
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Converter duplex process is to add thermal coal slag to the converter at

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon-containing slag suppression cold-bonded pellet and utilization method thereof
  • Carbon-containing slag suppression cold-bonded pellet and utilization method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0005] The embodiment of the present invention selects two technical schemes to make pellets A and pellets B. Into the ball transported to the steel mill. When the converter is about to stop the blowing gun, add 2-10 kg / ton steel into the converter from the high-level silo. The specific addition amount depends on the carbon content of the pellets. Generally, steel with C≤1.5 kg / ton is added into the pellets. Then tap the steel. The specific examples of pellet A and pellet B are as follows:

Embodiment

[0007] Pellet A

[0008] Iron-containing raw materials: rolling oil sludge TFe 50-55%, [gas ash, gas mud] TFe 38%-45, C 30-35%;

[0009] Additives: waste paper pulp, expanded graphite, bentonite.

[0010] Proportion: gas ash: waste paper pulp: steel rolling sludge: bentonite: expanded graphite = 65:15:18:1.5:0.5

[0011] Pelletizing steps: first dry the steel rolling oil sludge and mix it with bentonite in proportion, then put it into the mill for grinding with waste paper pulp, gas ash and expanded graphite in proportion for 30 minutes, mix evenly, the moisture content of the mixture is 9%, and after cooling The compression molding machine is pressed into balls under a pressure of 200 tons, and then left for 48 hours, the dry ball compressive strength is 2680N. The processed cold-solidified pellets contain 38.2% of TFe, 21.5% of C, 11.5% of volatile matter, and the balance is CaO and SiO 2 、Al 2 o 3 , MgO, ZnO, K 2 O, Na 2 O etc., specific gravity 2.59 g / cm 3 .

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carbon-containing slag suppression cold-bonded pellet and a utilization method thereof. In the carbon-containing slag suppression cold-bonded pellet, the TFe content is smaller than or equal to 45%, the carbon content is larger than or equal to 5%, the content of volatile components (including decomposable gas) is larger than or equal to 10%, and the specific gravity is smaller than or equal to 3.5 g/cm<3>. The pellet is added into a converter from a high bin while lance lifting is about to be finished through blowing in the dephosphorization stage of the converter or when lance lifting is about to be finished through the blowing end point of the converter, and then deslagging or tapping is carried out. The carbon-containing slag suppression cold-bonded pellet and the utilization method have the beneficial effects that iron and carbon in gas dust sludge or other iron and carbon containing metallurgy dust sludge can be efficiently utilized, and waste paper pulp, tar slag and other waste are used as additives for pelletizing; the process is simple, and cost is low; the pellet is only used as slag, heat energy of the slag is fully utilized, and the influence of the temperature of molten steel is extremely low; foam slag can be suppressed effectively, and deslagging or tapping in the dephosphorization stage is facilitated; and by means of reduction of FeO in the pellet and FeO in the slag, the yield of the molten steel is increased, consumption of a deoxidizing agent and an alloy is reduced, and slag-splashing furnace protection work is facilitated.

Description

technical field [0001] The invention relates to the field of steelmaking, in particular to cold solidified pellets of metallurgical dust and mud and their utilization in steelmaking. technical background [0002] Metallurgical dust contains a large amount of iron and carbon elements, and the use of it to make carbon-containing pellets has many applications in ironmaking and steelmaking. This kind of carbon-containing pellets can undergo self-reduction reaction to generate CO bubbles, and can make the slag foam when reacting in the slag, which can be used to make foam slag in the electric arc furnace; it can be used as a coolant and a cosolvent in the converter. For example, the one used in the converter has a carbon content of 5-15%, contains TFe50-60%, and has a larger proportion of pellets. The carbon-containing pellets are added during the converter smelting process. When it is added into the furnace as a coolant 1.5-3 minutes before the end point, the TFe content in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/248C21C5/28
CPCY02P10/20
Inventor 王虎
Owner 王虎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap