Glass fiber-containing sheet honeycomb ceramic and production method thereof

A technology of glass fiber and honeycomb ceramics, which is applied in the field of ceramic materials, can solve the problems of increased use cost, waste of resources, and insufficient heat resistance of ceramic carriers, and achieve the effects of cost saving, prolonging service life, broad application prospects and market value

Inactive Publication Date: 2016-12-07
BENGBU NANZI INSTR
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Zhu Jie used cordierite honeycomb ceramics as the carrier in his master's thesis "Study on the Catalytic Performance of Cordierite Honeycomb Ceramics Loaded La-Sr-Co-O on Automobile Exhaust Gas", La-Sr-Co-O perovskite composite oxidation As the active component of the catalyst, a monolithic automobile exhaust catalyst has been prepared, but the heat resistance of the prepared ceramic carrier is not high enough, and once the monolithic catalyst is damaged, it needs to be replaced as a whole, which wastes resources and increases the cost of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0020] A sheet-like honeycomb ceramic containing glass fibers, characterized in that it is made of the following raw materials in parts by weight:

[0021] Basalt fiber 5, cordierite 40, clay 3, glass fiber 5, ZrO 2 Powder 10, CrO 2 powder 10, talc powder 15, magnesium carbonate-5, silane coupling agent KH550 10, sodium carbonate 8, stearic acid 3, 1 mol / L HNO 3 Appropriate amount of solution, nano-alumina sol 60, 1mol / L La(NO 3 ) 3 3, 1 mol / L Sr(NO 3 ) 2 2,1 mol / L Co(NO 3 ) 2 1. 1 mol / L citric acid 6, deionized water 200;

[0022] The solid content of the nano-alumina sol is 20%-25%.

[0023] The described sheet-like honeycomb ceramics containing glass fiber and its preparation method are characterized in that it comprises the following steps:

[0024] a. Preparation of flake honeycomb ceramics:

[0025] Take basalt fiber, cordierite, clay, glass fiber, ZrO 2 Powder, CrO 2 Powder, talcum powder, magnesium carbonate and sodium carbonate are ball milled, mixed, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber-containing sheet honeycomb ceramic and a production method thereof. The glass fiber-containing sheet honeycomb ceramic is produced from, by weight, 3-5 parts of basalt fibers, 40-50 parts of iolite, 1-3 parts of clay, 3-5 parts of glass fibers, 5-10 parts of ZrO2 powder, 5-10 parts of CrO2 powder, 10-15 parts of talcum powder, 3-5 parts of magnesium carbonate, 5-10 parts of a silane coupling agent KH550, 4-8 parts of sodium carbonate, 1-3 parts of stearic acid, a proper amount of a 1 mol / L HNO3 solution 50-60 parts of nano-alumina sol, 1-3 parts of 1 mol / L La(NO3)3, 1-2 parts of 1 mol / L Sr(NO3)2, 0.5-1 part of 1 mol / L Co(NO3)2, 2-6 parts of 1 mol / L citric acid and 100-200 parts of deionized water. A honeycomb ceramic carrier is processed to form a sheet, so installation and replacement are convenient, the cost is saved, and full utilization of resources is promoted.

Description

technical field [0001] The invention relates to a ceramic material, in particular to a sheet-shaped honeycomb ceramic containing glass fiber and a preparation method thereof. technical background [0002] Motor vehicle pollution has become an important source of air pollution in my country and an important cause of haze and photochemical smog pollution. Vehicle exhaust is mainly nitrogen oxides (NO x ), hydrocarbons (HC), carbon monoxide (C0), particulate matter, etc., have become the main air pollutants. Therefore, the most important thing to solve the air pollution problem is to solve the problem of automobile exhaust pollution. [0003] The automobile exhaust purifier is mainly composed of three parts: the shell, the carrier and the catalyst, among which the selection of the catalyst is very important. Three-way catalyst refers to the ability to remove NO at the same time x , HC, CO these three main pollutants catalysts, a large number of experimental studies have show...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/195C04B35/622C04B35/80C04B38/00C04B41/87
CPCC04B35/195C04B35/622C04B35/803C04B38/0006C04B41/5045C04B41/87C04B2235/3201C04B2235/3206C04B2235/3241C04B2235/3244C04B2235/349C04B2235/5216C04B2235/5228C04B41/5031C04B41/5027C04B41/4535C04B41/0072
Inventor 闫秦峻
Owner BENGBU NANZI INSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products