High-breathable synthetic fiber composition and preparation method thereof

A technology of synthetic fiber and air permeability, which is applied in the field of preparation of synthetic fiber with high air permeability and its preparation, which can solve the problems of poor air permeability and achieve the effect of improving air permeability and heat insulation performance

Inactive Publication Date: 2016-12-07
南京理工宇龙新材料科技股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its polyimide fiber has poor air permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A highly air-permeable synthetic fiber composition comprising the following components in parts by weight:

[0019] 100 parts of polyimide fiber, 20 parts of high alumina bauxite clinker, 5 parts of calcium aluminate cement, 2 parts of polyvinyl acetate emulsion, 6 parts of cresyl diphenyl phosphate, 1 part of stearic acid, polyethylene 2 parts, 2 parts of polybutylene terephthalate.

[0020] The preparation method of the above-mentioned highly air-permeable synthetic fiber composition, its preparation steps are:

[0021] 1), take the corresponding raw material components by weight, mix and stir to form a slurry, so that the slurry is fluid;

[0022] 2) Pour the slurry into the ring mould, use the vibrating table to vibrate or hold the stirring rod to pound the slurry in the mold, so that the air bubbles in the slurry are fully removed, the slurry is dense, and then statically solidified;

[0023] 3), solidified and released from the mold, dried at room temperature fo...

Embodiment 2

[0026] A highly air-permeable synthetic fiber composition comprising the following components in parts by weight:

[0027] 100 parts of polyimide fiber, 18 parts of high alumina bauxite clinker, 7 parts of calcium aluminate cement, 3 parts of polyvinyl acetate emulsion, 8 parts of cresyl diphenyl phosphate, 2 parts of stearic acid, polyethylene 32 to 4 parts, 6 parts of polybutylene terephthalate.

[0028] The preparation method of the above-mentioned highly air-permeable synthetic fiber composition, its preparation steps are:

[0029] 1), take the corresponding raw material components by weight, mix and stir to form a slurry, so that the slurry is fluid;

[0030] 2) Pour the slurry into the ring mould, use the vibrating table to vibrate or hold the stirring rod to pound the slurry in the mold, so that the air bubbles in the slurry are fully removed, the slurry is dense, and then statically solidified;

[0031] 3), solidified and released from the mold, dried at room tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-breathable synthetic fiber composition including, by weight, 100 parts of polyimide fibers, 15-20 parts of a high alumina bauxite clinker, 5-8 parts of calcium aluminate cement, 2-5 parts of a polyvinyl acetate emulsion, 6-10 parts of tolyldiphenyl phosphate, 1-3 parts of stearic acid, 2-4 parts of polyethylene, and 2-7 parts of polybutylene terephthalate. The heat-insulation material is significantly improved in heat insulation and has excellent breathability.

Description

technical field [0001] The invention belongs to the field of fire-resistant and heat-insulating materials, and in particular relates to a synthetic fiber with high air permeability and a preparation method thereof. Background technique [0002] Polyimide fiber has good spinnability and can be made into various textiles for special occasions. Due to its high and low temperature resistance, flame retardancy, non-melting, self-extinguishing when away from fire and excellent temperature insulation, polyimide fiber thermal insulation protective clothing is comfortable to wear, good skin adaptability, permanent flame retardancy, and the size It is stable, safe, and has a long service life. Compared with other fibers, due to the low thermal conductivity of the material itself, it is also an excellent thermal insulation material. But its polyimide fiber has poor air permeability. Contents of the invention [0003] Purpose of the invention: In order to solve the deficiencies of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K21/02D01F9/08
CPCC09K21/02D01F9/08
Inventor 王天驰戴生伢张引李金金
Owner 南京理工宇龙新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap