Straw plant fiber synthetic resin and preparation technology thereof

A plant fiber and synthetic resin technology, applied in the field of straw plant fiber synthetic resin and its preparation technology, can solve the problems of unfavorable degradation, damage to soil water permeability, and high cost, so as to alleviate resource shortage, increase farmers' income, and reduce production costs. Effect

Inactive Publication Date: 2016-12-14
安徽科邦树脂科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing tableware, furniture, kitchen utensils and other daily necessities on the market are all made of wood, bamboo, ordinary plastics and other products. Pollution" destroys the water permeability of the soil, while wood and bamboo products require deforestation and waste water pollution during the manufacturing process, so they are not very good environmental protection materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A straw plant fiber synthetic resin, comprising the following raw materials in parts by weight: 30 parts of rice straw powder, 5 parts of rice bran wax, 15 parts of cellulose, 3 parts of aliphatic polycarbonate, 15 parts of cornstarch, 3 parts of sorbitol, Arabica 3 parts of rubber powder, 5 parts of superfine aluminum silicate, 10 parts of polylactic acid fiber;

[0021] Its preparation process comprises the following steps:

[0022] (1), the rice straw is subjected to ultra-fine grinding processing to obtain fine rice straw powder;

[0023] (2), put sorbitol and aliphatic polycarbonate into the high-speed mixer, add rice bran wax and stir evenly at the same time to obtain the primary mixed material;

[0024] (3), the rice straw powder of step (1) is put into the high-speed mixer and mixed with the initial mixing material of step (2), and cornstarch is added at the same time and stirred evenly, then cooled to room temperature, pulverized after being solidified into lu...

Embodiment 2

[0031] A straw plant fiber synthetic resin, comprising the following raw materials in parts by weight: 60 parts of rice straw powder, 10 parts of rice bran wax, 40 parts of cellulose, 8 parts of aliphatic polycarbonate, 40 parts of corn starch, 8 parts of sorbitol, Arabica 8 parts of rubber powder, 10 parts of superfine aluminum silicate, 20 parts of polylactic acid fiber;

[0032] Its preparation process comprises the following steps:

[0033] (1), the rice straw is subjected to ultra-fine grinding processing to obtain fine rice straw powder;

[0034] (2), put sorbitol and aliphatic polycarbonate into the high-speed mixer, add rice bran wax and stir evenly at the same time to obtain the primary mixed material;

[0035] (3), the rice straw powder of step (1) is put into the high-speed mixer and mixed with the initial mixing material of step (2), and cornstarch is added at the same time and stirred evenly, then cooled to room temperature, pulverized after being solidified into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of chemical materials, in particular to a straw plant fiber synthetic resin and a preparation technology thereof. The straw plant fiber synthetic resin is prepared from straw powder, rice bran wax, cellulose, aliphatic polycarbonate, corn starch, sorbitol, gum Arabic powder, superfine aluminum silicate and polylactic acid fiber. The preparation technology comprises the following steps that 1, fine particle straw powder is prepared; 2, a preliminary mixing material is prepared; 3, straw fiber powder is prepared; 4, a mixed addition material is prepared; 5, after the mixed addition material and polylactic acid fiber are stirred to be uniform, and blending extrusion and injection molding are performed to obtain straw plant fiber synthetic resin. In order to avoid waste of resources such as crop waste, the resources are sufficiently utilized, and environmental pollution is lowered; the production cost is low, the application range is quite wide, the advantage of rural resources can be brought into play, and effective methods and ways are provided for reasonably utilizing waste crops.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to a straw plant fiber synthetic resin and a preparation process thereof. Background technique [0002] As a large agricultural country, with the continuous harvest of agriculture, the output of crop straws and other wastes has also increased significantly, of which the output of bare straws is about 650 million t / year. Except for the development and utilization of feed and fertilizer, most of them are burned, which not only wastes resources, but also seriously endangers the natural ecological environment. Therefore, the comprehensive utilization of abandoned crops is of great significance. While human beings create modern civilization, it also brings negative impacts - white pollution. Disposable tableware, disposable plastic products, and agricultural mulch are difficult to recycle, and their treatment methods are mainly incineration and landfill. Incineration will produce a la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L1/02C08L69/00C08L5/00C08L67/04C08L3/02C08K3/34C08K5/053
CPCC08L97/02C08L2201/06C08L2205/035C08L2205/16C08L1/02C08L69/00C08L5/00C08L67/04C08L3/02C08K3/34C08K5/053
Inventor 袁振洲
Owner 安徽科邦树脂科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap