Anti-oxidation nylon breather valve material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-oxidation and breathable valve technology, applied in the field of breathable valve materials, can solve the problems of poor dispersion, achieve good hardness and impact strength, improve oxidation resistance, and improve storage stability
Inactive Publication Date: 2017-01-04
NINGBO TONGGUAN ELECTRIC AUTOMATION EQUIP
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Traditional breathable valve materials are mostly composed of nylon and glass fiber blends, and glass fiber is prone to problems such as poor dispersion as a reinforcing agent for nylon. Therefore, how to improve the compatibility of glass fiber in nylon or find new The raw material to replace the glass fiber reinforced nylon material is the direction of our research
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0016] An anti-oxidation nylon breathable valve material, which is composed of the following raw materials in parts by weight:
[0018] A preparation method of the anti-oxidation nylon breathable valve material, comprising the following steps:
[0019] (1) Add the above-mentioned sodium fluorosilicate to deionized water 60 times its weight, stir evenly, add 10 mol / l sulfuric acid dropwise, adjust the pH to 2, raise the temperature to 70°C, keep stirring for 10 minutes, add the above Calcium zeolite, stirred to room temperature, added saturated octadecylamide, ultrasonicate...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an anti-oxidation nylon breather valve material. The material is prepared from, by weight, 1-2 parts of 4-tert-amylphenol, 3-4 parts of lauryl mercaptan, 1-2 parts of 2,6-di-tert-butyl-p-cresol, 0.7-1 part of saturated stearamide, 4-6 parts of acetyl triethyl citrate, 0.7-1 part of naphthenic soap, 100-140 parts of nylon 6, 1-2 parts of nickel sulfamate, 27-40 parts of scolecite, 3-4 parts of aluminum stearate, 4-6 parts of polyethylene wax, 0.1-0.2 part of hexamethyl cyclotrisiloxane, 0.1-0.2 part of tribasic lead sulfate, 6-8 parts of sodium fluosilicate, 0.4-1 part of dibenzothiazyl disulfide, 0.1-0.2 part of dicumyl peroxide and 5-7 parts of acrylamide. Antioxidant performance of the finished material is effectively improved by adding 4-tert-amylphenol, 2,6-di-tert-butyl-p-cresol and the like. The breather valve material has good hardness and impact strength, and storage stability of the finished product is effectively improved by adding naphthenic soap, nickel sulfamate, tribasic lead sulfate and the like.
Description
technical field [0001] The invention relates to the technical field of breathable valve materials, in particular to an oxidation-resistant nylon breathable valve material and a preparation method thereof. Background technique [0002] Waterproof and breathable valve, commonly known as respirator, breathable screw, etc., the outer shell is PA66+20% glass fiber raw material injection molding or brass is used as the hard support, and the outer shell is high temperature resistant silicone O-ring. The membrane material and the shell are combined through a variety of tight packaging processes, which have the characteristics of stable performance, simple installation, long service life, and high waterproof and breathable performance; [0003] Traditional breathable valve materials are mostly composed of nylon and glass fiber blends, and glass fiber is prone to problems such as poor dispersion as a reinforcing agent for nylon. Therefore, how to improve the compatibility of glass fib...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.