High-hardness and high-wear-resistance acrylate water-based paint

An acrylate and water-based acrylate technology, applied in the field of coatings, can solve problems such as weather resistance, poor adhesion, low coating film hardness, and hinder development, achieve excellent elongation at break, reduce pollution, and prevent brittleness cracking effect

Active Publication Date: 2017-02-08
ANHUI JINDUN PAINT
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional solvent-based acrylic paints will release a large amount of volatile organic compounds during the film formation process, causing pollution to the environment
However, t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention proposes a high-hardness and high-wear-resistant acrylic water-based paint, which is composed of A component and B component in a weight ratio of 1:4;

[0022] Wherein, the raw materials of the A component include by weight: 30 parts of water-based acrylate emulsion, 45 parts of alkyd resin, 3 parts of polyhydroxyl unsaturated polyester resin, 10 parts of phenolic resin, 5 parts of nitrocellulose, silane Joint agent KH-560 modified nano-silica 10 parts, calcium carbonate whiskers 2 parts, talc powder 1.5 parts, dipropylene glycol methyl ether 1 part, dipropylene glycol butyl ether 2 parts, anti-sedimentation agent 1 part, wetting agent 1.5 parts part, 0.05 part of defoamer;

[0023] The raw materials of the B component include by weight: 10 parts of permethyletherified melamine resin, 8 parts of 3,5-dimethyl-2-aminobenzoic acid, 0.5 parts of leveling agent, and 35 parts of deionized water.

Embodiment 2

[0025] The present invention proposes a high-hardness and high-wear-resistant acrylic water-based paint, which is composed of A component and B component in a weight ratio of 1:3;

[0026] Wherein, the raw materials of the A component include by weight: 50 parts of water-based acrylate emulsion, 15 parts of alkyd resin, 20 parts of polyhydroxyl unsaturated polyester resin, 2 parts of phenolic resin, 15 parts of nitrocellulose, silane Joint agent KH-560 modified nano-silica 2 parts, calcium carbonate whiskers 5 parts, talc powder 0.3 parts, dipropylene glycol methyl ether 3 parts, dipropylene glycol butyl ether 0.5 parts, anti-sedimentation agent 2 parts, wetting agent 1 part, 0.3 part of defoamer;

[0027] The raw materials of the B component include by weight: 15 parts of permethyletherified melamine resin, 3 parts of 3,5-dimethyl-2-aminobenzoic acid, 1 part of leveling agent, and 20 parts of deionized water.

Embodiment 3

[0029] The present invention proposes a high-hardness and high-wear-resistant acrylic water-based paint, which is composed of A component and B component in a weight ratio of 1:3.8;

[0030]Wherein, the raw materials of the A component include by weight: 35 parts of water-based acrylate emulsion, 40 parts of alkyd resin, 11 parts of polyhydroxyl unsaturated polyester resin, 8 parts of phenolic resin, 9 parts of nitrocellulose, silane Joint agent KH-560 modified nano-silica 8 parts, calcium carbonate whiskers 2.7 parts, talc powder 1.3 parts, dipropylene glycol methyl ether 1.7 parts, dipropylene glycol butyl ether 1.5 parts, anti-sedimentation agent BYK410 0.7 parts, organic bentonite 0.6 parts 1.3 parts, 1.3 parts of wetting agent, 0.2 parts of defoamer;

[0031] The raw materials of the B component include by weight: 13 parts of permethyl etherified melamine resin, 7 parts of 3,5-dimethyl-2-aminobenzoic acid, 0.6 parts of leveling agent, and 31 parts of deionized water;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a high-hardness and high-wear-resistance acrylate water-based paint, which comprises a component A and a component B. The component A comprises the following raw materials: aqueous acrylate emulsion, alkyd resin, polyhydroxy unsaturated polyester resin, phenolic resin, nitrocellulose, silane coupling agent KH-560 modified nano-silicon dioxide, calcium carbonate whisker, talc, dipropylene glycol methyl ether, dipropylene glycol butyl ether, anti-settling agent, wetting agent and anti-foaming agent. The component B comprises the following raw materials: fully-methoxylated melamine resin, 3, 5-dimethyl-2-aminobenzoic acid, flatting agent and de-ionized water. The high-hardness and high-wear-resistance acrylate water-based paint is high in hardness, good in wear resistance, excellent in water resistance and heat resistance, and long in service life.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-hardness and high-wear-resistant acrylate water-based paint. Background technique [0002] Acrylic coatings have high hardness, excellent gloss and chemical resistance after film formation, and are low in cost, and are widely used in the automotive, construction and furniture industries. Traditional solvent-based acrylic paints release a large amount of volatile organic compounds during the film-forming process, causing pollution to the environment. However, there are still many deficiencies in water-based acrylic coatings, such as low coating film hardness, poor weather resistance and poor adhesion, which hinder its development. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a high-hardness and high-wear-resistant acrylate water-based paint, which has high hardness, good wear resistance, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/08C09D151/08C09D167/06C09D161/06C09D7/12
CPCC08K2201/011C08L2201/08C08L2205/02C08L2205/035C09D151/08C09D167/08C08L51/08C08L67/06C08L61/06C08K13/06C08K9/06C08K3/36C08K7/08C08K3/34C08K5/06C08L67/08
Inventor 朱恒衡梅长林张国胜
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap