Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of high-viscosity acrylate adhesive and its preparation process

An acrylate and preparation technology, which is applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of increasing the difficulty of use, reducing the relative adhesion of adhesives, increasing the amount of use, etc., to achieve Good durability and timeliness, reduction of VOC amount, and anti-static accumulation effect

Active Publication Date: 2018-07-24
YASUSA CHEM CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, in the adhesives prepared for the purpose of environmental protection, the advantages brought by these raw materials are lost, the relative adhesion of the prepared adhesives decreases, the amount of use is increased, and the relative viscosity increases, which increases the difficulty of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation process of a high-viscosity acrylic adhesive, specifically comprising the following steps:

[0030] 1) Take the following raw materials by weight ratio: 700 parts of methyl methacrylate, 120 parts of isooctyl acrylate, 80 parts of acrylic acid, 1500 parts of ethyl acetate, 7 parts of 2-hydroxyethyl acrylate, 150 parts of rosin resin, hydroxyl 50 parts of blocked polymethicone oil, 5 parts of ferric hydroxide;

[0031] 2) Add 500 parts of methyl methacrylate, 120 parts of isooctyl acrylate, and 600 parts of ethyl acetate into the reaction kettle, and stir at 65-70°C for 1 hour;

[0032] 3) Take 30 parts of acrylic acid and 3 parts of 2-hydroxyethyl acrylate into the reaction kettle in step 2), and stir at 65-70°C for 0.5 hours;

[0033] 4) Add 200 parts of methyl methacrylate, 100 parts of ethyl acetate, 50 parts of acrylic acid, and 4 parts of 2-hydroxyethyl acrylate into the reaction kettle in step 3), and stir at 71-75°C for 1 hour ;

[0034] 5) Disso...

Embodiment 2

[0044] A preparation process of a high-viscosity acrylic adhesive, specifically comprising the following steps:

[0045] 1) Take the following raw materials by weight ratio: 700 parts of methyl methacrylate, 120 parts of isooctyl acrylate, 80 parts of acrylic acid, 1500 parts of ethyl acetate, 7 parts of 2-hydroxyethyl acrylate, 150 parts of rosin resin, hydroxyl 50 parts of blocked polymethicone oil, 5 parts of ferric hydroxide;

[0046] 2) Add 500 parts of methyl methacrylate, 120 parts of isooctyl acrylate, and 600 parts of ethyl acetate into the reaction kettle, and stir for 1 hour at 65-70°C; add additives after completion, and the additives are calculated in parts by weight Including the following components: 0.5 parts of dicumyl peroxide, 4 parts of epichlorohydrin rubber, 3 parts of azo compounds, 5 parts of dimethyldiethoxysilane, 0.3 parts of magnesium oxide, 1.5 parts of succinimide, 3 parts of polyisobutenylamine, 0.5 parts of 2-tert-butyl-4-methylphenol, the addi...

Embodiment 3

[0059] A preparation process of a high-viscosity acrylic adhesive, specifically comprising the following steps:

[0060] 1) Take the following raw materials by weight ratio: 700 parts of methyl methacrylate, 120 parts of isooctyl acrylate, 80 parts of acrylic acid, 1500 parts of ethyl acetate, 7 parts of 2-hydroxyethyl acrylate, 150 parts of rosin resin, hydroxyl 50 parts of blocked polymethicone oil, 5 parts of ferric hydroxide;

[0061] 2) Add 500 parts of methyl methacrylate, 120 parts of isooctyl acrylate, and 600 parts of ethyl acetate into the reaction kettle, and stir at 65-70°C for 1 hour;

[0062] 3) Take 30 parts of acrylic acid and 3 parts of 2-hydroxyethyl acrylate into the reaction kettle in step 2), and stir at 65-70°C for 0.5 hours;

[0063] 4) Add 200 parts of methyl methacrylate, 100 parts of ethyl acetate, 50 parts of acrylic acid, and 4 parts of 2-hydroxyethyl acrylate into the reaction kettle in step 3), and stir at 71-75°C for 1 hour After completion, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of adhesives, in particular to a high-adhesiveness acrylate adhesive and a process for preparing the same. Raw materials for preparing the high-adhesiveness acrylate adhesive comprise the following components in parts by weight: 700 parts of methyl methacrylate, 120 parts of 2-ethylhexyl acrylate, 80 parts of acrylic acid, 1500 parts of ethyl acetate, 7 parts of 2-hydroxyethyl acrylate, 150 parts of rosin resin, 50 parts of hydroxyl end-capping polymethyl silicone oil and 5 parts of ferric hydroxide. No methylbenzene is volatilized from a downstream product of the product and the environmental friendliness is good; meanwhile, since the preparation process provided by the invention adopts a step-by-step charging method, the implosion is effectively prevented from occurring, the dispersity of the product is high, the VOC (volatile organic compounds) content of the downstream product is obviously reduced and most importantly, the adhesiveness is improved.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a high-viscosity acrylate adhesive and a preparation process thereof. Background technique [0002] Adhesive, also known as adhesive, referred to as glue (bonding agent, adhesive), is a non-metallic medium material that makes an object closely connected with another object. The adhesive only occupies a very thin layer of volume between the two adherend surfaces, but after the adhesive is used to complete the bonding construction, the obtained adhesive joints can meet various requirements of actual needs in terms of mechanical properties and physical and chemical properties. It can effectively bond materials together. [0003] Acrylic adhesives have a wide range of raw materials, simple preparation process, rapid drying and molding, good transparency, good bonding performance to various materials, and good weather resistance, water resistance, and chemical resistance. In parti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/12C09J193/04C09J183/06C09J11/08C09J11/06C09J11/04
CPCC08L2201/04C08L2205/03C08L2205/035C09J11/04C09J11/06C09J11/08C09J133/12C08L93/04C08L83/06C08K2003/2265C08L71/03C08L23/22C08K13/02C08K2003/222C08K5/5419
Inventor 张中杰
Owner YASUSA CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com