Non-combustible damping coating

A technology of damping coatings and raw materials, applied in the field of damping coatings, can solve the problems of low flame retardant performance, fire hazard, low temperature composite damping factor, etc., and achieve the effect of good salt spray resistance.

Active Publication Date: 2018-06-29
BEIJING MUCHEN FIREPROOF INSULATION SPECIAL MATERIALS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a non-combustible damping coating, which solves the problems of low flame retardancy and fire hazards in the existing damping coatings, and has a wider temperature range and a lower composite damping factor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-combustible damping coating
  • Non-combustible damping coating
  • Non-combustible damping coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A non-combustible grade damping coating, calculated by parts by weight, including the following raw materials:

[0036] 300 parts of acrylic waterproof emulsion, 100 parts of antirust emulsion, 50 parts of plasticized acrylic emulsion, 50 parts of pure acrylic emulsion, 15 parts of film-forming aid, 50 parts of floating beads, 50 parts of talcum powder, 200 parts of silica powder, aluminum hydroxide 200 parts, 50 parts of nano-montmorillonite / polypyrrole composite powder, 25 parts of preservative and 5 parts of black paste.

[0037] Among them, the anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd., its solid content is 41±1%, pH is 7-7.5, glass transition temperature is 20°C, minimum film-forming temperature is 30°C, viscosity Less than 20cps, with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good weather resistance and good corrosion resistance.

[0038] Th...

Embodiment 2

[0049] A non-combustible grade damping coating, calculated by parts by weight, including the following raw materials:

[0050] 290 parts of acrylic waterproof emulsion, 95 parts of antirust emulsion, 55 parts of plasticized acrylic emulsion, 55 parts of pure acrylic emulsion, 13 parts of film-forming aid, 45 parts of floating beads, 45 parts of talcum powder, 195 parts of silica powder, magnesium hydroxide 195 parts, 45 parts of nano-montmorillonite / polypyrrole composite powder, 23 parts of preservative and 4 parts of black paste.

[0051] Among them, the anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd., its solid content is 41±1%, pH is 7-7.5, glass transition temperature is 20°C, minimum film-forming temperature is 30°C, viscosity Less than 20cps, with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good weather resistance and good corrosion resistance.

[0052] Th...

Embodiment 3

[0062] A non-combustible grade damping coating, calculated by parts by weight, including the following raw materials:

[0063] 310 parts of acrylic waterproof emulsion, 105 parts of antirust emulsion, 45 parts of plasticized acrylic emulsion, 45 parts of pure acrylic emulsion, 17 parts of film-forming aid, 55 parts of floating beads, 55 parts of talcum powder, 205 parts of silica powder, magnesium hydroxide 100 parts, 105 parts of ammonium octamolybdate, 55 parts of nano-montmorillonite / polyaniline composite powder, 27 parts of preservative and 6 parts of black paste.

[0064] Among them, the anti-rust emulsion is DL-1065 anti-rust emulsion produced by Beijing Donglian Chemical Co., Ltd., which has a solid content of 41±1%, a pH of 7-7.5, a glass transition temperature of 20°C, a minimum film-forming temperature of 30°C, and a viscosity of Less than 20cps, with high gloss, high hardness, good leveling and solvent resistance, excellent adhesion to substrates, high gloss, good w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
particle diameteraaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides non-combustible grade damping paint. The paint comprises, by weight, 290-310 parts of acrylic acid waterproof emulsion, 95-105 parts of anti-rust emulsion, 45-55 parts of plasticization acrylic acid emulsion, 45-55 parts of pure acrylic emulsion, 13-17 parts of a coalescing agent, 285-315 parts of functional filler, 195-205 parts of fire retardant and 45-55 parts of anti-corrosive filler. The damping paint solves the problems that existing damping paint is low in flame retardancy, and potential fire hazards exist, has a wide temperature range and is low in compound damping factor.

Description

technical field [0001] The invention belongs to the technical field of damping coatings, in particular to a non-combustible damping coating. Background technique [0002] Water-based damping coatings mainly use water as a dispersant, have low VOC, and are environmentally friendly, and are gradually replacing traditional organic solvent-based damping coatings and asphalt-type damping sheets. At the same time, due to the characteristics of its coating, it can be easily coated on more complex interfaces without cutting. Therefore, it has more advantages in construction than the traditional butyl rubber type damping film. Due to some disadvantages of water-based damping coatings, their wider application is also limited. [0003] Traditional water-based damping coatings dry slowly, affecting construction progress. In terms of quick-drying water-based damping coatings, the published Chinese patent CN102850888A adopts the method of A and B two-component emulsion to improve the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D133/04C09D133/08C09D5/08C09D5/18C09D7/61C08F220/18C08F212/08C08F220/14C08F220/46C08F220/06C08F4/40
CPCC08F4/40C08F220/18C08F220/1804C08K2201/014C08L2201/02C08L2205/025C08L2205/035C09D5/08C09D5/18C09D7/61C09D133/00C08L33/00C08L33/04C08L33/08C08L79/04C08K13/04C08K3/34C08K3/346C08L79/02C08F220/1818C08F212/08C08F220/14C08F220/46C08F220/06
Inventor 孙天宝谢金彪
Owner BEIJING MUCHEN FIREPROOF INSULATION SPECIAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com