Hydrophobic association polymer with various loop-structure side chains and preparation method and application thereof
A hydrophobic association and polymer technology, which is applied in the preparation of hydrophobic association polymers. Hydrophobic association polymers can solve the problems of pipeline corrosion damage, poor polymer performance, and poor temperature resistance in the field of oil displacement agents, and achieve Effects of improving spatial structure and rigidity, increasing hydrodynamic volume, and strengthening hydrophobic association
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example
[0110] Preparation Example 1: Preparation of the hydrophobically associating polymer of the present invention
[0111] The implementation steps of this embodiment are as follows:
[0112] A. Preparation of monomer mixture solution
[0113] Acrylamide, N-acryloylmorpholine, 2-acrylamide-2-methylpropanesulfonic acid, isobornyl methacrylate pinane acrylate and N-(2-hydroxy-3-acrylamide methyl-4, 5-Dimethylbenzyl) acrylamide contains capsaicin functional structure acrylamide, which is dissolved in a 15% ethanol aqueous solution with a concentration of 15% by volume according to the weight ratio of 74:5:12:1.5:1.5, and then the concentration is 0.1mol / L NaOH aqueous solution to adjust the pH value of the obtained solution to 8 to obtain a monomer mixture solution with a total monomer content of 10% by weight;
[0114] B. Synthesis of hydrophobically associating polymers
[0115] Accurately measure one-fifth by volume of the monomer mixture solution obtained in step A above, add 10% steari...
Example
[0118] Preparation Example 2: Preparation of the hydrophobically associating polymer of the present invention
[0119] The implementation steps of this embodiment are as follows:
[0120] A. Preparation of monomer mixture solution
[0121] Acrylamide, N-acryloylmorpholine, 2-acrylamide-2-methylpropanesulfonic acid, isobornyl methacrylate pinane acrylate and N-(2-hydroxy-3-acrylamide methyl-4, 6-Dimethylbenzyl) acrylamide contains capsaicin functional structure acrylamide, which is dissolved in 1% ethanol aqueous solution by volume in a weight ratio of 60:3:14:5.0:0.3, and then used with a concentration of 5.0mol / L NaOH aqueous solution to adjust the pH value of the obtained solution to 6 to obtain a monomer mixture solution with a total monomer content of 5% by weight;
[0122] B. Synthesis of hydrophobically associating polymers
[0123] Accurately measure one-fifth by volume of the monomer mixture solution obtained in step A above, and add 1% sodium lauryl sulfate surfactant based ...
Example
[0126] Preparation Example 3: Preparation of the hydrophobically associating polymer of the present invention
[0127] The implementation steps of this embodiment are as follows:
[0128] A. Preparation of monomer mixture solution
[0129] Acrylamide, N-acryloylmorpholine, 2-acrylamide-2-methylpropanesulfonic acid, isobornyl acrylate, pinane acrylate and N-(3,4-dihydroxy-6-acrylamide methylbenzyl) ) Acrylamide contains capsaicin functional structure acrylamide, which is dissolved in 20% ethanol aqueous solution by volume according to the weight ratio of 85:6:8:2.8:2.0, and then the sodium hydroxide solution with a concentration of 1.8mol / L The pH value of the obtained solution is adjusted to 9 to obtain a monomer mixture solution with a total monomer content of 16% by weight;
[0130] B. Synthesis of hydrophobically associating polymers
[0131] Accurately measure one-fifth by volume of the monomer mixture solution obtained in step A above, add 4% sodium dodecylbenzene sulfonate surfa...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap