Composite modified environment-friendly metal corrugated pipe adhesive and preparation method thereof

A metal bellows, composite modification technology, applied in the field of material chemistry, can solve the problems of low glue strength, poor effect, short glue opening time, etc., and achieve the effect of high glue strength, good waterproof performance, and short glue opening time

Inactive Publication Date: 2017-04-19
WUXI YONGXING METAL HOSE
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the polyvinyl alcohol / starch composite adhesive prepared by the above-mentioned prior art is mainly aimed at the preparation of plywood, and the effect in the bellows of the metal hose is relatively poor, the glue opening time is short, and the bonding strength is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite modified environment-friendly metal corrugated pipe adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A composite modified environment-friendly adhesive for metal bellows, which is prepared by proportioning the following components in parts by weight: 16 parts of polyvinyl alcohol, 13 parts of corn starch, 13 parts of konjac powder, 12 parts of chitosan, grape Mannan 11 parts, borax 11 parts, aluminum oxide 3 parts, sodium hydroxide 8 parts, magnesium sulfate 6 parts, iron sulfate 6 parts.

[0025] A method for preparing a composite modified environment-friendly metal bellows adhesive, comprising the following steps:

[0026] (1) Adhesive matrix preparation: mix cornstarch and konjac flour, add deionized water to it, the total mass of the mixture: the volume of deionized water is 1:3, after stirring and mixing, heat to 60 ° C, while heating Stir to obtain the adhesive matrix;

[0027] (2) Preparation of the first modifier: mix alumina, magnesium sulfate and ferric sulfate and grind them into powder, add sulfuric acid with a mass fraction of 50% therein, and stir until ...

Embodiment 2

[0033] A composite modified environment-friendly adhesive for metal bellows, which is prepared by proportioning the following components in parts by weight: 28 parts of polyvinyl alcohol, 21 parts of corn starch, 20 parts of konjac powder, 22 parts of chitosan, grape Mannan 15 parts, borax 17 parts, aluminum oxide 8 parts, sodium hydroxide 14 parts, magnesium sulfate 14 parts, iron sulfate 13 parts.

[0034] A method for preparing a composite modified environment-friendly metal bellows adhesive, comprising the following steps:

[0035] (1) Adhesive matrix preparation: mix cornstarch and konjac flour, add deionized water to it, the total mass of the mixture: the volume of deionized water is 1:5, after stirring and mixing, heat to 70 ° C, while heating Stir to obtain the adhesive matrix;

[0036] (2) Preparation of the first modifier: mix alumina, magnesium sulfate and ferric sulfate and grind them into powder, add sulfuric acid with a mass fraction of 63% therein, and stir unt...

Embodiment 3

[0042] A composite modified environment-friendly adhesive for metal bellows, which is prepared by proportioning the following components in parts by weight: 35 parts of polyvinyl alcohol, 28 parts of corn starch, 26 parts of konjac powder, 27 parts of chitosan, grape Mannan 19 parts, borax 22 parts, aluminum oxide 11 parts, sodium hydroxide 19 parts, magnesium sulfate 17 parts, iron sulfate 18 parts.

[0043] A method for preparing a composite modified environment-friendly metal bellows adhesive, comprising the following steps:

[0044] (1) Adhesive matrix preparation: mix cornstarch and konjac flour, add deionized water to it, the total mass of the mixture: the volume of deionized water is 1:6, after stirring and mixing, heat to 75 ° C, while heating Stir to obtain the adhesive matrix;

[0045] (2) Preparation of the first modifier: mix alumina, magnesium sulfate and ferric sulfate and grind them into powder, add sulfuric acid with a mass fraction of 75% therein, and stir un...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite modified environment-friendly metal corrugated pipe adhesive and a preparation method of the composite modified environment-friendly metal corrugated pipe adhesive. The composite modified environment-friendly metal corrugated pipe adhesive is prepared from, by weight, 16-35 parts of polyvinyl alcohol, 13-28 parts of corn starch, 13-26 parts of konjaku flour, 12-27 parts of chitosan, 11-19 parts of konjac gulcomannan, 11-22 parts of sodium borate, 3-11 parts of aluminum oxide, 8-19 parts of sodium hydroxide, 6-17 parts of magnesium sulfate and 6-18 parts of ferric sulfate. The composite modified environment-friendly metal corrugated pipe adhesive is long in adhesion time and high in adhesion strength, and has good waterproof performance and good corrosion resistance.

Description

technical field [0001] The invention belongs to the field of material chemistry and relates to an adhesive, in particular to a composite modified environment-friendly metal bellows adhesive and a preparation method thereof. Background technique [0002] Polyvinyl alcohol is a water-soluble polymer with a wide range of uses and unique properties. It is widely used in the production of coatings, adhesives, emulsifiers, paper processing agents, textiles, and plastic films. As a rapidly developing hot-melt adhesive, polyvinyl alcohol has good strong adhesion, high film strength, toughness and transparency, oil resistance, solvent resistance, corrosion resistance, wear resistance, and good gas barrier properties. Thermal stability, suitable for bonding wood-based panels, blockboards, plywood, particleboard, high-density fiberboard, etc., with the characteristics of simple manufacturing process and fast curing speed. However, the characteristics of polyhydric water-soluble polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J129/04C09J103/02C09J105/00C09J105/08C09J105/02C09J11/04
CPCC09J129/04C08L2203/18C08L2205/02C08L2205/035C09J11/04C08L3/02C08L5/00C08L5/08C08L5/02C08K3/00C08K2003/387C08K2003/2227C08K3/22C08K2003/3063C08K2003/3072
Inventor 王铮
Owner WUXI YONGXING METAL HOSE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap