CLSY non heavy metal emission metal surface treatment fluid and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A heavy metal and treatment liquid technology, applied in the coating process of metal materials, etc., can solve the problems of destroying the natural ecological balance, high pollution, high energy consumption, etc., and achieve the effect of enhancing the anti-corrosion ability
Active Publication Date: 2017-04-26
山东创利思源环境科技有限责任公司
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
After a certain amount of steel components are processed, a large amount of phosphating waste liquid and cleaning liquid are discharged, which seriously pollutes the living and working environment of people and destroys the natural ecological balance.
The whole phosphating process is a process of high energy consumption and high pollution. Moreover, the anti-corrosion ability of the steel surface after phosphating treatment is very weak
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] In the present embodiment, the raw materials for preparing CLSY non-heavy metal discharge steel surface treatment liquid are constituted by mass parts as follows:
[0036] Film-forming agent I 5, film-forming agent II 15, passivating agent benzoyl peroxide 1, rust converting agent tetrameric acid magnesium zinc phosphate 16, rust inhibitor acid zinc phosphate 5, plasticizing and curing agent hexamethylene Base tetramine 1, stabilizer benzoic acid 0.5, butanol 5, solvent I ethanol 32, solvent II water 20.
[0037] In this embodiment, the CLSY steel surface treatment liquid is prepared according to the following method.
[0038] 1. Add 1 / 2 of solvent I ethanol and solvent II water to 1 / 2 # Reactor, heat up, keep warm at 60±2°C, then add stabilizer I benzoic acid and stabilizer II butanol sequentially, stir until the material forms a single-phase system, then add plasticizing and curing agent, keep warm after fully melting, and obtain A , save the kettle for later use. ...
Embodiment 2
[0044] The raw material of CLSY iron and steel surface treatment liquid constitutes by quality in the present embodiment:
[0045] Film-forming agent I 6, film-forming agent II 16, passivator 1, rust converting agent 18, rust inhibitor 6, plasticizing curing agent 1, stabilizer I0.5, stabilizer II 6, solvent I 30, solvent II 18
[0046] In this embodiment, the preparation method of the CLSY iron and steel surface treatment liquid is the same as that in Embodiment 1.
Embodiment 3
[0048] The raw material mass fraction of CLSY iron and steel surface treatment liquid constitutes in the present embodiment:
[0049] Film-forming agent I 7, film-forming agent II 17, passivator 1.5, rust converting agent 19, rust inhibitor 8, plasticizing curing agent 1.5, stabilizer I 0.5, stabilizer II 8, solvent I 28, solvent II 20
[0050]In this example, the preparation method of the CLSY iron and steel surface treatment liquid is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses raw material components of a CLSY non heavy metal emission metal surface treatment fluid and a preparation method of a product and belongs to the field of new materials or fine chemical industry. The CLSY non heavy metal emission metal surface treatment fluid has the innovative points that alcohol and water are used as solvents to replace an organic solvent which has influence on environment and belongs to water soluble coatings; compounds of Al3+, Mg2+ and Zn2+ with very strong rust prevention capability are used to replace heavy metal compounds as a rust inhibitor (the Al3+, the Mg2+ and the Zn2+ cannot be oxidized and rusted under any condition); and benzoyl peroxide with stronger passivation ability is used to replace Cr7+, strong resin is used as a film forming agent, and a rough high-temperature-resistant protective paint film can be formed on the metal surface. When the CLSY non heavy metal emission metal surface treatment fluid is prepared and applied, three wastes are not discharged, and various disadvantages of the traditional phosphating solution are completely overcome; an application method is simple and can use all of coating methods including a spraying method, a brushing method, a rolling method and a soaking method; after the product is tested, a good conclusion is obtained; and the CLSY non heavy metal emission metal surface treatment fluid creates an innovation road with good effect, resource saving, energy saving and environmental protection on metal surface treatment.
Description
[0001] 1. Technical field [0002] The invention of this patent relates to the protection technology of iron and steel against rust and corrosion, and belongs to the field of new materials or fine chemicals. [0003] 2. Background technology [0004] For degreasing and rust-free steel components, the first step in the whole anti-corrosion process is to phosphate (passivate) the steel surface. The traditional phosphating process is to immerse the fat-free and rust-free steel components in a phosphating solution containing various heavy metals (Cr, Pb, Cd, etc.), and perform phosphating treatment at a certain temperature. Hexavalent chromium (Cr 6+ ) and tetravalent lead (Pb 4+ ) etc. to passivate the steel surface. After a certain amount of steel components are processed, a large amount of phosphating waste liquid and cleaning liquid are discharged, which seriously pollutes the living and working environment of people and destroys the natural ecological balance. The whole ph...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more