Self-adhesive polymer waterproof membrane for weather-resistant high-extension roof and preparation method thereof

A waterproof membrane and polymer technology, applied in chemical instruments and methods, building components, building structures, etc., can solve the problems of poor weather resistance and inability to be exposed to use, and achieve good heat resistance, high weather resistance, The effect of high crystallinity

Active Publication Date: 2019-04-05
天津市禹红建筑防水材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, the self-adhesive polymer waterproof membrane used in building waterproofing projects can only reach 70 degrees due to its high temperature performance, and the weather resistance of the product is poor, so it cannot be used exposed
The original materials are also limited in application and promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-adhesive polymer waterproof membrane for weather-resistant high-extension roof and preparation method thereof
  • Self-adhesive polymer waterproof membrane for weather-resistant high-extension roof and preparation method thereof
  • Self-adhesive polymer waterproof membrane for weather-resistant high-extension roof and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A heat-resistant and weather-resistant high-adhesion modified asphalt, which is made of raw materials containing the following parts by weight: petroleum asphalt 90#: 100 parts, softening oil (naphthenic oil): 10 parts, styrene-butadiene rubber (SBR): 10 parts, synthetic rubber (SIS): 8 parts, aldehyde resin KT100 particles: 2 parts, silane coupling agent: 2 parts and terpene resin T120: 8 parts, of which, silane coupling agent and terpene resin as a tackifier.

[0030] A self-adhesive polymer waterproof membrane for weather-resistant high-extension roofs. The waterproof membrane includes a five-layer structure: from top to bottom: anti-aging POE protective film, modified asphalt layer, metallocene modified polyethylene, A modified asphalt layer and a silicon-coated isolation aluminum foil film; the modified asphalt layer adopts the above-mentioned heat-resistant and weather-resistant high-adhesion modified asphalt; wherein, the aging-resistant POE protective film is fo...

Embodiment 2

[0042] A heat-resistant and weather-resistant high-adhesion modified asphalt, which is made of raw materials containing the following parts by weight: petroleum asphalt 90#: 100 parts, softening oil (naphthenic oil): 11 parts, styrene-butadiene rubber (SBR): 11 parts, synthetic rubber (SIS): 9 parts, aldehyde resin KT100 particles: 3 parts, silane coupling agent: 3 parts and terpene resin T120: 9 parts, of which, silane coupling agent and terpene resin as a tackifier.

[0043] A self-adhesive polymer waterproof membrane for weather-resistant high-extension roofs. The waterproof membrane includes a five-layer structure: from top to bottom: anti-aging POE protective film, modified asphalt layer, metallocene modified polyethylene, A modified asphalt layer and a silicon-coated isolation aluminum foil film; the modified asphalt layer adopts the above-mentioned heat-resistant and weather-resistant high-adhesion modified asphalt; wherein, the aging-resistant POE protective film is fo...

Embodiment 3

[0054] A heat-resistant and weather-resistant high-adhesion modified asphalt, which is made of raw materials containing the following parts by weight: petroleum asphalt 90#: 100 parts, softening oil (naphthenic oil): 12 parts, styrene-butadiene rubber (SBR): 12 parts, synthetic rubber (SIS): 10 parts, aldehyde resin KT100 particles: 5 parts, silane coupling agent: 5 parts and terpene resin T120: 10 parts, of which, silane coupling agent and terpene resin as a tackifier.

[0055] A self-adhesive polymer waterproof membrane for weather-resistant high-extension roofs. The waterproof membrane includes a five-layer structure: from top to bottom: anti-aging POE protective film, modified asphalt layer, metallocene modified polyethylene, A modified asphalt layer and a silicon-coated isolation aluminum foil film; the modified asphalt layer adopts the above-mentioned heat-resistant and weather-resistant high-adhesion modified asphalt; wherein, the aging-resistant POE protective film is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a high weather -resistant extended roof for waterproof coils and preparation methods for self -adhesive polymers., Maoman modifiers, polyethylene, modified asphalt layer and silicon coating aluminum foil film; the modified asphalt used in the modified asphalt layer is made of raw materials containing the following weightOil: 10‑12 copies, butyl -benzene rubber (SBR): 10‑12 copies, synthetic rubber (SIS): 8‑10 copies, aldehydes, KT particles: 2‑5 copies, Silicane puppet couplet: 2‑5 parts and 2‑5 copies and 2‑5 parts and 2‑5 copies and 2‑5 copies and siberT120: 8‑10 copies.The invention uses a variety of raw materials compounding to improve the weather resistance and physical mechanical properties of materials, and solves the limitations of existing self -adhesive asphalt waterproofing materials that should not be exposed.

Description

technical field [0001] The invention relates to the technical field of designing waterproof building materials, in particular to a self-adhesive polymer waterproof membrane for weather-resistant high-extension roofs and a preparation method thereof. Background technique [0002] Self-adhesive polymer waterproof membrane is widely used in waterproof engineering in construction engineering. The membrane is a membrane formed by coating or scraping SBS modified bitumen waterproof membrane production process. [0003] In the prior art, the self-adhesive polymer waterproof membrane used in building waterproofing projects can only reach 70 degrees due to its high temperature performance, and the weather resistance of the product is poor, so it cannot be used exposed. The original materials are also limited in application and promotion. Contents of the invention [0004] In view of this, in order to solve the above technical problems, the present invention proposes a self-adhesiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L91/00C08L9/06C08L53/02C08L61/00C08L45/00C08K5/54B32B11/04B32B13/06B32B15/20B32B17/06B32B27/06B32B27/32B32B37/00
CPCB32B11/046B32B13/06B32B15/20B32B17/06B32B27/06B32B27/32B32B37/00B32B2255/06B32B2255/20B32B2255/26B32B2307/306B32B2307/71B32B2307/712B32B2419/06C08L95/00C08L2205/035C08L91/00C08L9/06C08L53/02C08L61/00C08L45/00C08K5/54
Inventor 周玉梅周荣凯
Owner 天津市禹红建筑防水材料有限公司