Antibacterial, deodorant and efficient deodorizing cellulose fibers and preparation method thereof
A technology of cellulose fiber and type A cellulose, which is applied in chemical post-treatment of cellulose/protein rayon, preparation of spinning solution, wet spinning, etc., can solve the problems of loss of effective substances and reduction of fiber deodorization function. , to achieve the effect of increasing the content, lasting and stable antibacterial and deodorizing function
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example 1:
[0032] Prepare 1.11dtex×38mm antibacterial, deodorant, and efficient deodorizing cellulose fiber:
[0033] 1) Preparation of composite antibacterial deodorant
[0034] (1) Preparation of high-absorption opal powder: mix the opal powder and low-quality water into the reactor at a ratio of 1:5, at a temperature of 200 ℃, stirring speed 400r / min, stirring for 2h, the opal powder After being fully dissociated, sulfuric acid with a concentration of 1mol / L is added for activation. The activation time is 2h, and the activated product is separated and dried to obtain opal powder. The powder is prepared by wet grinding method with a particle size of less than 3μm. High-absorption opal powder for viscose fiber production.
[0035] (2) Preparation of microencapsulated slurry of Pteris vulgaris extract: mix melamine and formaldehyde solution in a ratio of 1:3, adjust the pH of the mixture to 7.5, temperature to 65°C, and rotate at 300r / min Stir the reaction in the reactor to...
Example Embodiment
[0042] Example 2:
[0043] Prepare 1.33dtex×38mm antibacterial, deodorant, and efficient deodorizing cellulose fiber:
[0044] 1) Preparation of composite antibacterial deodorant
[0045] (1) Preparation of high-absorption opal powder: mix the opal powder and low-quality water into the reactor at a ratio of 1:7, at a temperature of 150 ℃, stirring speed 200r / min, stirring for 1.5h, opal powder After full dissociation, add hydrochloric acid for activation, the concentration is 2mol / L, and the activation time is 2h. After activation, the product is separated and dried to improve the adsorption capacity of the opal powder, so as to prepare the opal powder. The powder uses the wet method. Grinding method prepares high-absorption opal powder with a particle size of 3μm or less, which is suitable for viscose fiber production.
[0046] (2) Preparation of microencapsulated slurry of Pteris sylvestris extract: Mix melamine and formaldehyde solution in a ratio of 1:4, adjust the pH of the mixt...
Example Embodiment
[0053] Example 3:
[0054] Prepare 1.67dtex×38mm antibacterial, deodorant, and efficient deodorizing cellulose fiber:
[0055] 1) Preparation of composite antibacterial deodorant
[0056] (1) Preparation of high-absorption opal powder: mix the opal powder and low-quality water into the reactor at a ratio of 1:10, stir for 1.5h at a temperature of 120°C and a stirring speed of 300r / min, the opal powder After being fully dissociated, nitric acid is added for activation, the concentration is 5mol / L, the activation time is 1.5h, and the product is separated and dried after activation to obtain opal powder. The powder is prepared by wet grinding method with a particle size of 3μm or less high-absorption opal powder suitable for viscose fiber production.
[0057] (2) Preparation of microencapsulated slurry of Pteris sylvestris extract: Mix melamine and formaldehyde solution in a ratio of 1:5, adjust the pH of the mixture to 8.0, temperature to 50°C, and rotate at 250r / min. Stir and react ...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap