sio 2 medium charge and sio 2 Separation test method for /si interface state

A test method and interface state technology, applied in semiconductor/solid-state device testing/measurement, circuits, electrical components, etc., can solve the problems of unfavorable popularization and use of separation test methods, and achieve the advantages of popularization and use, low equipment requirements, and simple preparation process. quick effect

Inactive Publication Date: 2021-05-25
INST OF ELECTRONICS ENG CHINA ACAD OF ENG PHYSICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, often only large-scale integrated circuit manufacturing companies have ion implanters, and it is difficult for ordinary laboratories to meet such testing requirements.
Therefore, this separation test method developed by the Sandia National Laboratory in the United States is not conducive to widespread promotion and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • sio <sub>2</sub> medium charge and sio <sub>2</sub> Separation test method for /si interface state
  • sio <sub>2</sub> medium charge and sio <sub>2</sub> Separation test method for /si interface state
  • sio <sub>2</sub> medium charge and sio <sub>2</sub> Separation test method for /si interface state

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Using the method of dry oxygen oxidation, grow 150 nm thick SiO on the surface of a p-type silicon wafer with a resistivity of 50 Ω.cm 2 thin film; subsequently, using the method of thermal evaporation on SiO 2 An aluminum thin film is grown on the surface, and then a MIS device is manufactured. The structure diagram of the corresponding MIS device and where N o t and N it distribution, such as figure 1 shown.

[0029] (2) At normal temperature, carry out C / V test to the MIS device described in step (1), the corresponding C / V curve is as follows figure 1 shown. Obtain the flat band voltage V from the C / V curve fb , and then calculate the total charge density N tot (N tot =N ot + N it ). The corresponding C / V curve is as figure 2 Shown:

[0030] N tot = (W ms -V fb ).C ox (1)

[0031] Among them, N tot is the total charge concentration, N tot =N ot + N it ;W ms is the difference between the metal and semiconductor work functions, and the ...

Embodiment 2

[0038] (1) Using the plasma-enhanced chemical vapor deposition method, a 30 nm thick SiO was grown on the surface of an n-type silicon wafer with a resistivity of 0.1 Ω.cm 2 thin film; subsequently, using the method of magnetron sputtering on SiO 2 A gold film is grown on the surface, and then the MIS device is made;

[0039] (2) At normal temperature, carry out C / V test to the MIS device described in step (1), obtain flat-band voltage V fb , and then calculate the total charge density N tot (N tot =N ot + N it );

[0040] (3) Further, the deep-level transient spectroscopy (DLTS) test is carried out on the MIS device described in step (1), and the test temperature range is 20-300K. According to the measured deep-level transient spectrum curve, combined with formula (2), the distribution of the energy level density of the interface state with the energy level is calculated, and the energy level density of the interface state is integrated with the energy level to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a kind of SiO 2 Medium charge and SiO 2 Separation test method of / Si interface state, including: (1) growing SiO on the surface of silicon wafer 2 After thin film, further on SiO 2 A metal film is grown on the surface to obtain a MIS device; (2) C / V test is performed on the MIS device to obtain the flat-band voltage V fb , and then calculate the total charge density N tot ; (3) Perform a deep level transient spectrum test on the above MIS device, obtain the distribution of the energy level state density of the interface state with the energy level, and obtain the total interface state N after integration it ;(4)N tot with N it Subtract to get N ot , so as to achieve N ot with N it separation test. The test structure (MIS) used in the present invention has a simple and fast preparation process, has low requirements on equipment, and is beneficial to popularization and use in the scientific and industrial circles.

Description

technical field [0001] The invention belongs to the technical field of semiconductors, in particular to a SiO 2 Medium charge and SiO 2 / Si interface state separation test method. Background technique [0002] From the birth of the world's first transistor in 1947 to the advent of the world's first integrated circuit in 1958, microelectronics technology has only developed for more than 50 years. Microelectronics technology has changed the entire society and brought about a revolution in information technology. Until now, the characteristic line width of devices in integrated circuits has been decreasing year by year, and continues to develop in accordance with "Moore's Law". In 2014, Intel and Samsung have achieved mass production of 14nm FinFET chips. If Intel can continue to develop according to its established route in the next few years, it will realize 7nm and 5nm process technology in 2017 and 2019 respectively. However, to further reduce the characteristic line wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L21/66
CPCH01L22/14
Inventor 董鹏宋宇李沫侯世尧代刚张健
Owner INST OF ELECTRONICS ENG CHINA ACAD OF ENG PHYSICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com