Ceramization agent for electrophoretic coating pretreatment, preparation method and usage method for ceramization agent

An electrophoretic coating and pre-treatment technology, applied in the direction of metal material coating process, etc., can solve the problems of limited types and limited scope of use, and achieve the effect of improving bonding, excellent effect and good conductivity

Active Publication Date: 2017-05-24
芜湖市瑞杰环保材料科技有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the application of a single silane treatment agent in the pretreatment of metal surfaces is still in the research and development stage.
[0004] Although the vitrification agent is generally recognized in the home appliance industry, it has not been widely used in other industries. The main reason

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramization agent for electrophoretic coating pretreatment, preparation method and usage method for ceramization agent
  • Ceramization agent for electrophoretic coating pretreatment, preparation method and usage method for ceramization agent
  • Ceramization agent for electrophoretic coating pretreatment, preparation method and usage method for ceramization agent

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0043] Example 1

[0044] A pottery agent for pretreatment of electrophoretic coating, containing the following raw materials in weight percentage:

[0045]

[0046]

[0047] The rest is deionized water.

[0048] 45% fluorozirconic acid provides both fluoride ion and zirconium ion; 45% fluorotitanic acid provides both fluoride ion and titanium ion.

[0049] A preparation method of a pottery agent for pretreatment of electrophoretic coating, including the following steps:

[0050] 1) Add two-thirds of the formula amount of deionized water to the reactor, and then add the formula amount of 45% fluorozirconic acid and 45% fluorotitanic acid in sequence, stir thoroughly until completely dissolved into a clear solution; then add the formula amount Rare earth accelerator cerium nitrate, complexing agent citric acid and oxidant hydrogen peroxide, stir until clear and transparent;

[0051] 2) Add one-tenth of the formula amount of deionized water to another container, heat it to 30-40°C, add th...

Example Embodiment

[0062] Example 2

[0063] A pottery agent for pretreatment of electrophoretic coating, containing the following raw materials in weight percentage:

[0064]

[0065] The rest is deionized water.

[0066] The ammonium fluorozirconate provides both fluoride ion and zirconium ion; sodium fluorotitanate provides both fluoride ion and titanium ion.

[0067] A preparation method of a pottery agent for pretreatment of electrophoretic coating, including the following steps:

[0068] 1) Add two-thirds of the formula amount of deionized water to the reaction kettle, and then add the formula amount of ammonium fluorozirconate and sodium fluorotitanate in sequence, stir thoroughly until completely dissolved into a clear solution; then add the formula amount of rare earth Promoter lanthanum nitrate, complexing agent potassium sodium tartrate and oxidant potassium chlorate, stir until clear and transparent;

[0069] 2) Add one-tenth of the formula amount of deionized water to another container, heat ...

Example Embodiment

[0080] Example 3

[0081] A pottery agent for pretreatment of electrophoretic coating, containing the following raw materials in weight percentage:

[0082] Potassium fluorozirconate 0.5%

[0083] Sodium fluorotitanate 1%

[0084] γ-Aminopropyltriethoxysilane 0.8%

[0085] 0.2% chelate solution of bis(dioctyloxypyrophosphate) ethylene titanate and triethanolamine

[0086]

[0087] The balance is deionized water.

[0088] Potassium fluorozirconate provides both fluoride ion and zirconium ion; sodium fluorotitanate provides both fluoride ion and titanium ion.

[0089] A preparation method of a pottery agent for pretreatment of electrophoretic coating, including the following steps:

[0090] 1) Add two-thirds of the formula amount of deionized water to the reactor, and then add the formula amount of potassium fluorozirconate and sodium fluorotitanate in turn, stir thoroughly until completely dissolved into a clear solution; then add the formula amount of rare earth Promoter cerium chloride, c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention method provides a ceramization agent for electrophoretic coating pretreatment, a preparation method and a usage method for the ceramization agent. Compared with the prior art, fluorine ions slightly dissolve the surfaces of steel and a zinc substrate first, and meanwhile, the fluorine ions and zirconium/titanium ions form a compact conversion film layer on the dissolved metal surface; and a silane coupling agent and a cross-linking agent in colloid achieve the synergistic effect, and meanwhile, a rare earth promoter in a solution also plays a role. An organic-inorganic hybrid film is formed on the metal surface, and the corrosion resistance of the conversion film as well as the adhesive force of the conversion film and electrophoretic paint are far superior to that of ternary phosphating films and common ceramization films.

Description

technical field [0001] The invention belongs to metal surface treatment technology, and in particular relates to a ceramic agent for electrophoretic coating pretreatment, a preparation method and a use method thereof, which are suitable for the electrophoretic coating pretreatment process of automobiles and auto parts products, so that electrophoretic paint and metal The matrix is ​​tightly bound. Background technique [0002] At present, the application of metal surface treatment agent technology to replace phosphating solution is becoming more and more mature in the home appliance industry, and it is showing a trend of diversification. Among them, zirconium salt or ceramic agent compounded with zirconium salt and silane is dominant. A single zirconium film not only It has poor corrosion resistance, is also brittle, and has poor binding force with electrophoretic organic coatings. [0003] Silane is called industrial monosodium glutamate and is widely used. Silane contain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/34C23C22/73
CPCC23C22/34C23C22/73C23C2222/20
Inventor 褚云婷
Owner 芜湖市瑞杰环保材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap