A kind of mineral feed mold remover and preparation method thereof

A mildew remover and mineral technology, applied in the field of mineral feed mildew remover and its preparation, can solve the problems of high nutrient absorption, animal anorexia, poor taste, etc., achieve high mold inhibition rate, eliminate pollution, The effect of simple preparation method

Active Publication Date: 2021-02-19
HEBEI UNIV OF TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the mold remover has a strong adsorption capacity for mycotoxins, it also has a high degree of adsorption for nutrients and has a poor taste. Adding it to the feed will cause animals to anorexia and refuse to eat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mineral feed mold remover and preparation method thereof
  • A kind of mineral feed mold remover and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The steps of the preparation method of above-mentioned mineral feed mildew remover are:

[0020] (a) Carry out particle size downgrading treatment on attapulgite, tourmaline and iron tailings as mineral raw materials, and the particle size after downgrading treatment is 60 mesh (250 microns) to 200 mesh (74 microns);

[0021] (b) uniformly mixing the downgraded attapulgite, tourmaline and iron tailings, and calcining at 600°C for 3 hours to obtain a mineral mixture;

[0022] (c) sorbic acid is dissolved in ethanol, and the quality of ethanol is 8~15 times of sorbic acid quality, obtains sorbic acid solution;

[0023] (d) mixing the mineral mixture calcined in step (b) and the sorbic acid solution obtained in step (c), magnetically stirring, drying, and sieving to obtain a mineral feed mold remover.

[0024] The present invention also protects a feed added with the above-mentioned mineral feed mildew remover. The mineral feed mildew remover is added to the complete fee...

Embodiment 1

[0030] The weight components of the raw materials of the mineral feed mildew remover in this embodiment include: attapulgite 60%, tourmaline 25%, iron tailings 5%, sorbic acid 10%.

[0031] Preparation:

[0032] (a) Carry out particle size downgrading treatment on attapulgite, tourmaline and iron tailings as mineral raw materials, and the particle size after downgrading treatment is 60 mesh (250 microns) to 200 mesh (74 microns);

[0033] (b) uniformly mixing the downgraded attapulgite, tourmaline and iron tailings, and calcining at 600°C for 3 hours to obtain a mineral mixture;

[0034] (c) sorbic acid is dissolved in ethanol, and the quality of ethanol is 10 times of sorbic acid quality, obtains sorbic acid solution;

[0035] (d) mixing the mineral mixture calcined in step (b) and the sorbic acid solution obtained in step (c), magnetically stirring, drying, and sieving to obtain a mineral feed mold remover.

[0036] Method of use: add the above-mentioned feed mold remover ...

Embodiment 2

[0038] The weight components of the raw materials of the mildew remover in this embodiment include: attapulgite 65%, tourmaline 20%, iron tailings 5%, sorbic acid 10%. The preparation and use methods are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a mineral feed mildew remover and a preparation method thereof, which is characterized in that the weight components of the raw materials of the mildew remover include: attapulgite 60%~75%, tourmaline 15%~25%, iron tail Ore 2%~10%, sorbic acid 8%~12%. The preparation method of the mildew remover is: (a) carry out particle size reduction treatment on attapulgite, tourmaline and iron tailings of mineral raw materials, and the particle size after the reduction treatment is 60 mesh to 200 mesh; The attapulgite, tourmaline and iron tailings are uniformly mixed, and calcined at 600°C for 3 hours to obtain a mineral mixture; (c) dissolving sorbic acid in ethanol, whose mass is 8 to 15 times the mass of sorbic acid, to obtain sorbic acid solution; (d) mixing the mineral mixture calcined in step (b) and the sorbic acid solution obtained in step (c), magnetically stirring, drying, and sieving to obtain a mineral feed mold remover.

Description

technical field [0001] The invention relates to the technical field of feed in the breeding industry, in particular to a mineral feed mildew remover and a preparation method thereof. Background technique [0002] Mycotoxins are highly toxic secondary metabolites produced by molds during growth and reproduction, and can be produced during the growth of grains, feed manufacturing, storage and transportation. Generally speaking, mycotoxins are mainly produced by 4 kinds of molds: Aspergillus (aflatoxin, ochratoxin, etc.), Penicillium (citrinin, etc.), Ergot (ergot toxin), shuttle Bacteria (vomitoxin, zearalenone, T-2 toxin, etc.). After feed contaminated by mycotoxins is ingested by animals, mycotoxins and their metabolites may remain in liver, kidney, muscle, blood, milk and eggs, causing potential harm to animal health and production performance. Proper detoxification treatment of toxin-contaminated feed is necessary and has certain practical value in improving the availabi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A23K20/00A23K20/28
Inventor 梁金生韩筱玉孟军平顾小杨张红
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com