Axial fan blade with reinforced sweepforward blade and preparation method thereof

An axial flow fan blade and blade technology, which is applied in the field of fan blades and their preparation, can solve the problems of increased vibration and noise, insufficient rigidity and high temperature resistance, and easy deformation, so as to reduce material deformation, improve aging performance, increase The effect of material toughness

Inactive Publication Date: 2017-05-31
NINGBO LANGDI IMPELLER MACHINERY
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing axial-flow fan blades reinforced with forward-swept blades are made of ordinary glass fiber-reinforced AS, ABS or PP materials. Due to their insufficient rigidity and high temperature resistance, they are prone to deformation during transportation and after long-term use. There will be a problem of increased vibration and noise in the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Axial fan blade with reinforced sweepforward blade and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A forward-swept blade-reinforced axial-flow fan blade is injection molded from the following materials in terms of mass percentage:

[0048] Fiberglass 20%

[0049] Carbon Fiber 3.5%

[0050] Mica 6.0%

[0051] Silane coupling agent DB792 1.0%

[0052] Silane coupling agent KBM-403 1.5%

[0053] Cyclic anhydride type compatibilizer 0.5%

[0054] Ethoxylated Lauramide 0.5%

[0055] Silver-loaded inorganic antibacterial agent 0.8%

[0056] Ethylene bis stearamide 1.5%

[0057] Methyl Methacrylate-Butadiene-Styrene Terpolymer 1.0%

[0058] Halogen-free flame retardant 0.5%

[0059] Antioxidant 1.0%

[0060] Light stabilizer 0.2%

[0061] Heat stabilizer 0.2%

[0062] PP margin.

[0063] The preparation method of the above-mentioned forward-swept blade reinforced axial flow fan blade, the method includes the following steps: mixing PP resin, mica, silane coupling agent DB792, and silane coupling agent KBM-403 in a high-mixer for 10-15min ; Placed in the main fe...

Embodiment 2

[0065] A forward-swept blade-reinforced axial-flow fan blade is injection molded from the following materials in terms of mass percentage:

[0066] Glass fiber 15.0%

[0067] Carbon Fiber 4.5%

[0068] Mica 10.0%

[0069] Silane coupling agent DB792 0.8%

[0070] Silane coupling agent KBM-403 1.5%

[0071] Cyclic anhydride type compatibilizer 1.0%

[0072] Ethoxylated Lauramide 0.8%

[0073] Silver-loaded inorganic antibacterial agent 0.5%

[0074] Ethylene bis stearamide 0.5%

[0075] Methyl methacrylate-butadiene-styrene terpolymer 2.0%

[0076] Halogen-free flame retardant 1.5%

[0077] Antioxidant 1.0%

[0078] Light stabilizer 0.2%

[0079] Heat stabilizer 0.2%

[0080] PP margin.

[0081] The preparation method of the above-mentioned forward-swept blade reinforced axial flow fan blade, the method includes the following steps: mixing PP resin, mica, silane coupling agent DB792, and silane coupling agent KBM-403 in a high-mixer for 10-15min ; Placed in the main ...

Embodiment 3

[0083] A forward-swept blade-reinforced axial-flow fan blade is injection molded from the following materials in terms of mass percentage:

[0084] Glass fiber 20.0%

[0085] Carbon fiber 1.0%

[0086] Mica 5.0%

[0087] Silane coupling agent DB792 1.5%

[0088] Silane coupling agent KBM-403 1.5%

[0089] Cyclic anhydride type compatibilizer 1.0%

[0090] Ethoxylated Lauramide 0.8%

[0091] Silver-loaded inorganic antibacterial agent 0.5%

[0092] Ethylene bis stearamide 0.5%

[0093] Methyl Methacrylate-Butadiene-Styrene Terpolymer 1.0%

[0094] Halogen-free flame retardant 1.5%

[0095] Antioxidant 1.0%

[0096] Light stabilizer 0.2%

[0097] Heat stabilizer 0.2%

[0098] PP margin.

[0099] The preparation method of the above-mentioned forward-swept blade reinforced axial flow fan blade, the method includes the following steps: mixing PP resin, mica, silane coupling agent DB792, and silane coupling agent KBM-403 in a high-mixer for 10-15min ; Placed in the main...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a fan blade and a preparation method thereof. The axial fan blade with a reinforced sweepforward blade is prepared from, by mass, 76-89% of PP, 15-25% of glass fiber, 1.0-5.0% of carbon fiber, 3.0-10% of mica, 0.1-1.5% of silane coupling agent DB792, 0.1-1.5% of silane coupling agent KBM-403, 0.2-2.0% of cyclic anhydride compatibilizer, 0.5-1.0% of ethoxylated lauryl amide, 0.2-1.0% of silver-loaded inorganic antibacterial agent, 0.5-2.0% of ethylene bis-stearamide, 0.5-3.0% of methyl methacrylate-butadiene-styrene copolymer, 0.5-2.0% of halogen free flame retardant, 0.5-2.0% of anti-oxidant, 0.1-1.0 part of light stabilizer and 0.1-1.0% of heat stabilizer. The axial fan blade with the reinforced sweepforward blade has a high heat resistance, chemical corrosion resistance, anti-aging, anti-moulding, anti-ultraviolet properties and the like, the density and hardness are high, the size change is small, and the tensile strength of the plastic material is increased. At the same time, the axial fan blade with the reinforced sweepforward blade has the anti-static, antimicrobial, fire-retardant properties, and increased anti-aging property and a thermal decomposition performance.

Description

technical field [0001] The invention relates to wind blades and a preparation method thereof. Background technique [0002] With the improvement of living standards, people pay more and more attention to the requirements of the living environment. As an air conditioner used in an indoor airtight environment, its impact on fan noise is also increasingly concerned. The air conditioner indoor unit fan is the key component of the air supply of the air conditioner, so it has an important impact on the size of the indoor fan noise. [0003] Most of the existing axial-flow fan blades reinforced with forward-swept blades are made of ordinary glass fiber-reinforced AS, ABS or PP materials. Due to their insufficient rigidity and high temperature resistance, they are prone to deformation during transportation and after long-term use. There will be a problem of increased vibration and noise. Contents of the invention [0004] In order to solve the above-mentioned technical problems,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/04C08K13/06C08K9/12C08K3/08C08K7/14C08K7/06C08K3/34C08K5/20
CPCC08L23/12C08K2201/014C08L2201/02C08L2201/04C08L2201/08C08L51/04C08K13/06C08K9/12C08K2003/0806C08K7/14C08K7/06C08K3/34C08K5/20
Inventor 韩小红柴水华周会中洪银川冯燕立施建立王银祥张焕法曹香妮
Owner NINGBO LANGDI IMPELLER MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap