Bookbinding machine motor installation base PBT engineering plastic and motor installation base

A technology of engineering plastics and mounting bases, applied in the field of engineering plastics, can solve the problems of adverse effects on the environment and people's health, difficulty in handling pollutants, and high production costs, and achieve excellent physical and mechanical properties, excellent mechanical properties, and electrical properties. Good results

Active Publication Date: 2017-05-31
东莞市票友机电科技有限公司 +1
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing binding machine motor mounts are all made of aluminum alloy. The aluminum alloy motor mount has good mechanical properties, but its processing requirements are high, the production cost is high, the efficiency is low, the production cycle is long, and the product yield is low. , and in the long-term operation process, the wear rate is high, the corrosion resistance is poor, and the insulation treatment needs to be improved; on the other hand, the production of aluminum alloy belongs to the field of severe pollution, which has adverse effects on the environment and people's health, and subsequent pollutant treatment Difficult and costly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of PBT engineering plastics for binding machine motor mounting seat, is made up of the raw material of following parts by weight:

[0033] 50 parts of PBT resin

[0034] 5 parts glass fiber

[0035] Composite toughening agent 6 parts

[0036] Lubricant 0.5 parts

[0037] Composite flame retardant 20 parts

[0038] Weathering agent 1 part

[0039] Antioxidant 2 parts

[0040] 4 parts of inorganic filler.

[0041] The melt index of the PBT resin is 24g / 10min (measurement temperature is 250°C, mass is 2.16kg), and the melting point is 220-230°C. The glass fiber is an alkali-free glass fiber, the diameter of the glass fiber is 8-12 μm, and the dielectric constant is 3.9.

[0042] The composite toughening agent is composed of the following raw materials: hyperbranched epoxy resin 35 wt%, ethylene-methyl acrylate-glycidyl methacrylate terpolymer 40 wt% and ethylene-vinyl acetate copolyester 25 wt% , the number of epoxy groups of the hyperbranched epoxy resin is...

Embodiment 2

[0049] A kind of PBT engineering plastics for binding machine motor mounting seat, is made up of the raw material of following parts by weight:

[0050] 60 parts of PBT resin

[0051] 25 parts glass fiber

[0052] Composite toughening agent 8 parts

[0053] Lubricant 0.7 parts

[0054] Composite flame retardant 25 parts

[0055] 1.5 parts of weathering agent

[0056] Antioxidant 1.5 parts

[0057] 6 parts of inorganic filler.

[0058] The melt index of the PBT resin is 29g / 10min, and the melting point is 220-230°C. The glass fiber is an alkali-free glass fiber, the diameter of the glass fiber is 8-12 μm, and the dielectric constant of the glass fiber is 4.1.

[0059] The composite toughening agent is composed of the following raw materials: hyperbranched epoxy resin 25%, ethylene-methyl acrylate-glycidyl methacrylate terpolymer 50 wt%, ethylene-vinyl acetate copolyester 25 wt%, The number of epoxy groups of the hyperbranched epoxy resin is 12, and the number average mo...

Embodiment 3

[0065] A kind of PBT engineering plastics for binding machine motor mounting seat, is made up of the raw material of following parts by weight:

[0066] 60 parts of PBT resin

[0067] 35 parts glass fiber

[0068] Composite toughening agent 10 parts

[0069] Lubricant 0.6 parts

[0070] Composite flame retardant 30 parts

[0071] Weathering agent 2 parts

[0072] Antioxidant 1 part

[0073] 5 parts of inorganic filler.

[0074] The melt index of the PBT resin is 27g / 10min, and the melting point is 220-230°C. The glass fiber is an alkali-free glass fiber, the diameter of the glass fiber is 8-12 μm, and the dielectric constant of the glass fiber is 4.2.

[0075] The composite toughening agent is composed of the following raw materials: hyperbranched epoxy resin 30 wt%, ethylene-methyl acrylate-glycidyl methacrylate terpolymer 45 wt% and ethylene-vinyl acetate copolyester 15 wt% , the number of epoxy groups of the hyperbranched epoxy resin is 21, and the number average mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of engineering plastic, in particular to bookbinding machine motor installation base PBT engineering plastic and a motor installation base. The motor installation base PBT engineering plastic is prepared from the following raw materials in parts by weight: 50 to 70 parts of PBT, 5 to 60 parts of glass fiber, 6 to 12 parts of composite toughening agent, 0.5 to 1 part of lubricant, 20 to 30 parts of composite flame retardant, 1 to 2 parts of weather-proof agent, 1 to 2 parts of antioxidant and 4 to 8 parts of inorganic filler. The bookbinding machine motor installation base PBT engineering plastic prepared in the invention has excellent comprehensive mechanical property and processing property, further has lower dielectric constant and good fire resistance and insulation, can reduce the weight of the motor base when being applied to manufacturing the bookbinding machine motor installation base, improves safety performance, shortens a production and manufacturing period, improves product yield, reduces abrasion and has long service life and excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a PBT engineering plastic for a binding machine motor mounting seat and a drilling motor mounting seat. Background technique [0002] Binding machines are widely used in the binding of paper documents such as bills and archives in various industries, and play an important role in people's daily life and work. When the binding machine is in use, the motor shaft used for drilling is in a state of high-speed rotation, and the motor mount needs to withstand relatively large impacts, so the motor mount has high requirements. However, the existing binding machine motor mounts are all made of aluminum alloy. The aluminum alloy motor mount has good mechanical properties, but its processing requirements are high, the production cost is high, the efficiency is low, the production cycle is long, and the product yield is low. , and in the long-term operation process, the wear r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L63/00C08L23/08C08L83/04C08L63/04C08K13/06C08K7/14C08K9/04C08K7/08C08K3/22B29C47/92B29C48/92
CPCB29C48/92B29C2948/9259B29C2948/92704C08K2201/003C08K2201/011C08L67/02C08L2201/02C08L2201/22C08L2203/20C08L2205/02C08L2205/035C08L63/00C08L23/0884C08L23/0853C08L83/04C08L63/04C08K13/06C08K7/14C08K9/04C08K7/08C08K3/2279
Inventor 胡晋
Owner 东莞市票友机电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More