High-temperature-resistant flame-retardant conveying rail and preparation method thereof

A conveying track, high temperature resistant technology, applied in coatings, fire retardant coatings, epoxy resin coatings, etc., can solve the problems of easily damaged transportation tracks, casualties, etc., and achieve the effects of convenient operation, enhanced absorption rate, and reduced production costs

Inactive Publication Date: 2017-05-31
SUZHOU KESHENG STORAGE & LOGISTICS EQUIP
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The transportation track is an extremely important part of the storage industry. Most of the transportation tracks in the prior art are easily damaged, and they are flammable due to long-term use and cause casualties. In order to improve work efficiency and safety, the present invention proposes a high-temperature resistant flame-retardant Conveyor track and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides a high-temperature-resistant and flame-retardant conveying track. The outer surface of the conveying track is coated with a layer of high-temperature-resistant and flame-retardant layer. The high-temperature-resistant and flame-retardant layer is formed by mixing components A and B according to the mass ratio A:B=7:2 , A and B comprise the following components in parts by mass:

[0028] Component A includes the following components in parts by mass: 33 parts of ATO powder, 12 parts of E-20 epoxy resin, 24 parts of alcohol-soluble acrylic resin, 8 parts of benzyl alcohol, and 17 parts of graphite fluoride , ethanol: 9 parts, flame retardant: 13 parts, thickener: 5 parts, film-forming aid: 11 parts;

[0029] Component B includes the following components in parts by mass: UV absorber: 9 parts, dispersant: 5 parts, thickener: 8 parts, film-forming aid: 15 parts, sodium tetraborate: 2 parts, mixed Phosphate: 3 parts, potassium hydrogen phthalate: 1 ...

Embodiment 2

[0038] This embodiment provides a high-temperature-resistant and flame-retardant conveying track. The outer surface of the conveying track is coated with a layer of high-temperature-resistant and flame-retardant layer. The high-temperature-resistant and flame-retardant layer is formed by mixing components A and B according to the mass ratio A:B=7:2 , A and B comprise the following components in parts by mass:

[0039] Component A includes the following components in parts by mass: ATO powder 33-37 parts, E-20 epoxy resin: 16 parts, alcohol-soluble acrylate resin: 26 parts, benzyl alcohol: 13 parts, fluorinated graphite: 22 parts, ethanol: 12 parts, flame retardant: 16 parts, thickener: 7 parts, film-forming aid: 13 parts;

[0040] Component B includes the following components in parts by mass: UV absorber: 11 parts, dispersant: 9 parts, thickener: 12 parts, film-forming aid: 18 parts, sodium tetraborate: 5 parts, mixed Phosphate: 7 parts, potassium hydrogen phthalate: 3 parts...

Embodiment 3

[0049] This embodiment provides a high-temperature-resistant and flame-retardant conveying track. The outer surface of the conveying track is coated with a layer of high-temperature-resistant and flame-retardant layer. The high-temperature-resistant and flame-retardant layer is formed by mixing components A and B according to the mass ratio A:B=7:2 , A and B comprise the following components in parts by mass:

[0050] Component A includes the following components in parts by mass: 35 parts of ATO powder, 14 parts of E-20 epoxy resin, 25 parts of alcohol-soluble acrylic resin, 11 parts of benzyl alcohol, and 20 parts of graphite fluoride , ethanol: 11 parts, flame retardant: 14 parts, thickener 6 parts, film-forming aid: 12 parts;

[0051] Component B includes the following components in parts by mass: UV absorber: 10 parts, dispersant: 7 parts, thickener: 10 parts, film-forming aid: 16 parts, sodium tetraborate: 3 parts, mixed Phosphate: 5 parts, potassium hydrogen phthalate:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant flame-retardant conveying rail which comprises a conveying rail body, wherein the outer surface of the conveying rail body is coated by a layer of high-temperature-resistant flame-retardant layer. The high-temperature-resistant flame-retardant layer is prepared from a first component and a second component which are mixed according to a mass ratio of the first component to the second component being 7 to 2. The first component is prepared from the following ingredients in parts by mass: 33 to 37 parts of ATO powder, 12 to 16 parts of E-20 epoxy resin, 24 to 26 parts of alcohol-soluble acrylate resin, 8 to 13 parts of benzyl alcohol, 17 to 22 parts of carbon monofluoride, 9 to 12 parts of alcohol, 13 to 16 parts of flame retardant, 5 to 7 parts of thickening agent and 11 to 13 parts of coalescing agent. The second component is prepared from the following ingredients in mass fraction: 9 to 11 parts of ultraviolet light absorber, 5 to 9 parts of dispersing agent, 8 to 12 parts of thickening agent, 15 to 18 parts of coalescing agent, 2 to 5 parts of sodium tetraborate, 3 to 7 parts of mixed phosphate, 1 to 3 parts of potassium biphthalate, 4 to 6 parts of allyl alcohol, 13 to 15 parts of auxiliary materials and 20 to 35 parts of solvent. The high-temperature-resistant flame-retardant conveying rail disclosed by the invention not only improves work efficiency, but also reduces environmental pollution; in addition, practicability of the conveying rail is enhanced.

Description

technical field [0001] The invention relates to the technical field of storage equipment, in particular to a high-temperature-resistant and flame-retardant conveying track and a preparation method thereof. Background technique [0002] The transportation track is an extremely important part of the storage industry. Most of the transportation tracks in the prior art are easily damaged, and they are flammable due to long-term use and cause casualties. In order to improve work efficiency and safety, the present invention proposes a high-temperature resistant flame-retardant Conveyor track and its preparation method. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a high-temperature-resistant and flame-retardant conveying track for the above shortcomings of the prior art, including a conveying track whose outer surface is coated with a high-temperature-resistant and flame-retardant layer, and a high-temperature-resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/10C09D133/08C09D163/00C09D7/12C09D5/18
CPCC09D133/10C08L2201/02C08L2201/08C09D5/18C09D7/61C09D7/63C09D133/08C08L63/00C08K13/02C08K3/22C08K5/05C08K3/04C08K5/521C08K5/12C08K5/06C08K5/053C08K3/08
Inventor 王忠义王正勇
Owner SUZHOU KESHENG STORAGE & LOGISTICS EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com