Graphene tencel composite fiber and preparation method thereof

A technology of composite fiber and tencel, which is applied in fiber processing, plant fiber, rayon manufacturing, etc., to achieve the effect of increasing the flexibility of graphene

Active Publication Date: 2017-06-23
常州市卓盛纺织有限公司
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] So far, there are no reports on the research and preparation of environmentally friendly functional composite fibers with super strength, excellent electrical conductivity, thermal conductivity, UV protection, far infrared, excellent antibacterial and direct contact with the skin. It is necessary to develop an environmentally friendly clothing fiber that combines the advantages of graphene and Tencel fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0023] A kind of graphene tencel composite fiber graphene tencel composite fiber, described graphene tencel composite fiber is to utilize graphene oxide solution and cellulose pulp to add NMMO (N-methylmorpholine-N oxide) and water It is prepared by mixing, dissolving, filtering, spinning through dry-spraying-wet process, and finishing with silk thread and graphene oxide finishing solution.

[0024] A kind of preparation method according to described graphene tencel composite fiber, comprises the following steps:

[0025] Step 1: Preparation of graphene oxide NMMO·H 2 O solution: add 10% graphene oxide solution with a mass fraction of 70% NMMO aqueous solution, mix and stir for 3 hours, treat in ultrasonic for 1 hour, and obtain graphene oxide NMMO·H by vacuum distillation 2 O solution.

[0026] Step 2: Dissolving and filtering the spinning mixed solution: in graphene oxide NMMO·H 2 Add pulverized wood pulp with a degree of polymerization of 600, antibacterial agent, and an...

specific Embodiment 2

[0034] A kind of graphene tencel composite fiber graphene tencel composite fiber, described graphene tencel composite fiber is to utilize graphene oxide solution and cellulose pulp to add NMMO (N-methylmorpholine-N oxide) and water It is prepared by mixing, dissolving, filtering, spinning through dry-spraying-wet process, and finishing with silk thread and graphene oxide finishing solution.

[0035] A kind of preparation method according to described graphene tencel composite fiber, comprises the following steps:

[0036] Step 1: Preparation of graphene oxide NMMO·H 2 O solution: add 30% graphene oxide solution with mass fraction to 80% NMMO aqueous solution, mix and stir for 5 hours, treat in ultrasonic wave for 2 hours, and obtain graphene oxide NMMO·H by vacuum distillation 2 O solution.

[0037] Step 2: Dissolving and filtering the spinning mixed solution: in graphene oxide NMMO·H 2 Add crushed wood pulp with a degree of polymerization of 600-1000, antibacterial agent, ...

specific Embodiment 3

[0045] A kind of graphene tencel composite fiber graphene tencel composite fiber, described graphene tencel composite fiber is to utilize graphene oxide solution and cellulose pulp to add NMMO (N-methylmorpholine-N oxide) and water It is prepared by mixing, dissolving, filtering, spinning through dry-spraying-wet process, and finishing with silk thread and graphene oxide finishing solution.

[0046] A kind of preparation method according to described graphene tencel composite fiber, comprises the following steps:

[0047] Step 1: Preparation of graphene oxide NMMO·H 2 O solution: add 20% graphene oxide solution with a mass fraction of 70-80% NMMO aqueous solution, mix and stir for 4 hours, treat in ultrasonic for 1.4 hours, and obtain graphene oxide NMMO·H by vacuum distillation 2 O solution.

[0048] Step 2: Dissolving and filtering the spinning mixed solution: in graphene oxide NMMO·H 2 Add pulverized wood pulp with a degree of polymerization of 800, antibacterial agents,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a graphene tencel composite fiber and a preparation method thereof. The graphene tencel composite fiber is prepared by mixing a graphene oxide solution and cellulose pulp into NMMO (N-methylmorpholine-N oxide) and water, dissolving, filtering, spinning by virtue of a dry-wet spinning process and then finishing by virtue of silk yarns and a graphene oxide finishing solution. The tencel composite fiber contains graphene and is prepared by the following steps: preparing a spinning solution, spinning, and finishing the yarns by virtue of graphene. The obtained yarns can sufficient integrate the excellent characteristics of tencel and graphene, has excellent physical properties of the tencel, such as moisture absorption performance, dyeing performance, comfort, high strength and the like, also improves the flexibility, conductivity, and bacteria resistance of the grpahene, and are ideal fibers for clothes. The preparation process and a production process are pollution-free to the environment, the fiber product waste can be naturally degraded, damage to the environment can be avoided, and a recyclable resource is easy to form.

Description

technical field [0001] The invention belongs to the field of new textile materials, and relates to a graphene tencel composite fiber and a preparation method thereof. Background technique [0002] Graphene is a new type of carbon nano light material with a unique two-dimensional crystal structure of single atomic layer. Due to its ultra-high strength, excellent electrical conductivity, thermal conductivity, and light transmittance, as well as excellent antibacterial, anti-ultraviolet, and far-infrared functions. [0003] Tencel fiber uses wood pulp as raw material to produce a new fiber through solvent spinning method. It has the comfort of cotton, the strength of polyester, the luxurious beauty of wool and the unique feel and soft drape of silk, all of which are extremely resilient when dry. In the wet state, the wet strength is far better than the cellulose fibers of cotton. Pure natural materials, environmentally friendly manufacturing process, green and environmentall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F2/00D01F1/09D01F1/10D06M11/74D06M15/263D06M15/55D06M15/564D06M101/06
CPCD01F1/09D01F1/10D01F1/103D01F2/00D06M11/74D06M15/263D06M15/55D06M15/564D06M2101/06
Inventor 张炜栋黄旭
Owner 常州市卓盛纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com