Carbon Nanotube Composite High Performance Tire Tread Compound and Its Application

A carbon nanotube composite and carbon nanotube technology, which is applied to special tires, tire parts, rolling resistance optimization, etc., can solve the problems of high price and no industrialized tires on the market, so as to achieve low production cost and improve various Performance, effect of preventing agglomeration and entanglement

Active Publication Date: 2018-03-23
山东宝力科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application of these new materials has indeed improved the performance of the tire, but due to the high price, it is basically still in the stage of laboratory promotion, and there is no industrialized or commercialized tire on the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Carbon nanotube composite high-performance tire tread rubber is made from the following raw materials in parts by weight: 100 parts of environmentally friendly reclaimed rubber, 60 parts of carbon nanotube masterbatch, 40 parts of cracked carbon black, 100 parts of natural rubber, zinc oxide 15 parts, 8 parts of dibutyl tin dichloride, 5 parts of coupling agent, 12 parts of vulcanizing agent;

[0031] The carbon nanotube masterbatch is prepared by mixing carbon nanotubes, natural rubber and an accelerator according to a weight ratio of 1:1:0.6.

[0032] As mentioned, the accelerator is composed of sulfonated polyacrylamide, hydroxypropyl distarch phosphate, polyoxypropylene oxide ethylene glyceryl ether and 2-ethyl-4-methylimidazole according to the weight of 1: 1.5: 2: 0.9 Than made.

[0033] As mentioned, the carbon nanotubes are single-walled carbon nanotubes.

[0034] As mentioned, the molecular weight of sulfonated polyacrylamide is between 2 million and 3 millio...

Embodiment 2

[0042] Carbon nanotube composite high-performance tire tread rubber is made from the following raw materials in parts by weight: 100 parts of environmentally friendly reclaimed rubber, 55 parts of carbon nanotube masterbatch, 50 parts of cracked carbon black, 90 parts of natural rubber, zinc oxide 20 parts, 10 parts of dibutyl tin dichloride, 7 parts of coupling agent, 10 parts of vulcanizing agent.

[0043] As mentioned above, the carbon nanotube masterbatch is prepared by mixing carbon nanotubes, natural rubber and accelerator according to the weight ratio of 1:1.3:0.5.

[0044] As mentioned, the accelerator is composed of sulfonated polyacrylamide, hydroxypropyl distarch phosphate, polyoxypropylene oxide ethylene glyceryl ether and 2-ethyl-4-methylimidazole according to the weight of 1:1.2:2.5:0.7 Than made.

[0045] As mentioned, the carbon nanotubes are multi-walled carbon nanotubes.

[0046] As mentioned, the coupling agent is a titanate coupling agent.

[0047] All t...

Embodiment 3

[0049] Carbon nanotube composite high-performance tire tread rubber is made from the following raw materials in parts by weight: 100 parts of environmentally friendly reclaimed rubber, 50 parts of carbon nanotube masterbatch, 60 parts of cracked carbon black, 80 parts of natural rubber, zinc oxide 25 parts, 12 parts of dibutyl tin dichloride, 9 parts of coupling agent, 8 parts of vulcanizing agent;

[0050] The carbon nanotube masterbatch is prepared by mixing carbon nanotubes, natural rubber and an accelerator according to a weight ratio of 1:1.5:0.4.

[0051] As mentioned, the accelerator is composed of sulfonated polyacrylamide, hydroxypropyl distarch phosphate, polyoxypropylene oxide ethylene glyceryl ether and 2-ethyl-4-methylimidazole according to the weight of 1:1:3:0.5 Than made.

[0052] As mentioned, the carbon nanotubes are modified carbon nanotube powders.

[0053] As described, the coupling agent is a silane coupling agent.

[0054] All the other are with embod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Degree of sulfonationaaaaaaaaaa
Login to view more

Abstract

The invention discloses tread rubber for a carbon nano tube composite high-performance tire. The tread rubber is prepared from, by weight, 100 parts of environment-friendly regeneration rubber, 50-60 parts of carbon nano tube rubber master batch, 40-60 parts of pyrolysis carbon black, 80-100 parts of natural rubber, 15-25 parts of zinc oxide, 8-12 parts of dibutyltin dichloride, 5-9 parts of coupling agent and 8-12 parts of a vulcanizing agent. The invention further discloses application thereof for a high-performance tire tread. The excellent nano tube excellent performance advantage is brought into play, the production cost of the tire is effectively lowered, the tread rubber has the advantages of being high in abrasion resistance and heat conductivity coefficient, low in rolling resistance and endurance thermogenesis, and low in production cost. The tread rubber for the carbon nano tube composite high-performance tire is free from extraneous odor, does no harm to the human body, remarkably improves the various performances, can be used for producing the high-performance rubber, is safe and environmentally friendly, and has the wide market prospect.

Description

technical field [0001] The invention belongs to the technical field of tire manufacturing, and in particular relates to a carbon nanotube composite tread rubber for high-performance tires and an application thereof. Background technique [0002] my country's annual tire output ranks first in the world, but it is not yet a tire powerhouse. Foreign tire companies have implemented technical and trade barriers in the manufacture of high-performance tires, resulting in domestic tires that can only reach the low-end quality, and corporate profits are meager. At the same time, a large number of waste rubber products are treated as waste products and garbage in our country every year, which not only causes a lot of waste of resources, but also causes "black pollution" which has become an increasingly serious environmental problem. At present, the recycling and application of waste tires are mostly concentrated on low-grade products such as tire retreading, environmentally friendly r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L17/00C08L7/00C08K13/04C08K7/24C08K3/04C08K3/22C08K5/57B60C1/00
CPCB60C1/0016C08K2201/011C08L17/00C08L2205/025C08L2205/035C08L7/00C08K13/04C08K7/24C08K3/04C08K2003/2296C08K5/57Y02T10/86
Inventor 尹作鹏卢德政
Owner 山东宝力科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap