Uvioresistant and antioxidant ground mat and preparation method thereof

An anti-ultraviolet and anti-oxidation technology, applied in the field of floor mats, can solve the problems of easy aging, achieve the effects of improving high temperature resistance and low temperature resistance, excellent synergistic effect, and reducing processing difficulty

Inactive Publication Date: 2017-07-07
广东雅丽斯佳新材料有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the PVC floor mats currently on the market generally have the defect of easy aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] An anti-ultraviolet and anti-oxidation floor mat, comprising a PVC base material layer and a silk braided layer attached to the upper surface of the PVC base material layer, the PVC base material layer comprising the following raw materials in parts by weight:

[0052] PVC resin 85 parts

[0053] 30 parts plasticizer

[0054] Filler 20 parts

[0055] Stabilizer 3 parts

[0056] Impact modifier 4 parts

[0057] Anti-ultraviolet agent 0.5 parts

[0058] Antioxidant 0.5 part

[0059] Lubricant 1.0 parts.

[0060] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin at a weight ratio of 1:1.

[0061] The plasticizer is a mixture of diisononyl cyclohexane 1,2-dicarboxylate and dioctyl adipate in a weight ratio of 1.5:0.8.

[0062] The filler is heavy calcium carbonate with a particle size of 50 nm and modified by a titanate coupling agent.

[0063] The stabilizer is a mixture of calcium stearate, zinc stearate, β-diketone and zeoli...

Embodiment 2

[0081] An anti-ultraviolet and anti-oxidation floor mat, comprising a PVC base material layer and a silk braided layer attached to the upper surface of the PVC base material layer, the PVC base material layer comprising the following raw materials in parts by weight:

[0082] PVC resin 90 parts

[0083] 32 parts plasticizer

[0084] Filler 22 parts

[0085] Stabilizer 4 parts

[0086] Impact modifier 5 parts

[0087] Anti-ultraviolet agent 0.8 part

[0088] Antioxidant 0.8 parts

[0089] Lubricant 1.1 parts.

[0090] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin at a weight ratio of 1:1.2.

[0091] The plasticizer is a mixture composed of diisononyl cyclohexane 1,2-dicarboxylate and dioctyl adipate at a weight ratio of 1.8:0.9.

[0092] The filler is heavy calcium carbonate with a particle size of 60nm and modified by a titanate coupling agent.

[0093] The stabilizer is a mixture of calcium stearate, zinc stearate, β-diketo...

Embodiment 3

[0111] An anti-ultraviolet and anti-oxidation floor mat, comprising a PVC base material layer and a silk braided layer attached to the upper surface of the PVC base material layer, the PVC base material layer comprising the following raw materials in parts by weight:

[0112] PVC resin 95 parts

[0113] 35 parts plasticizer

[0114] Filler 25 parts

[0115] Stabilizer 5 parts

[0116] Impact modifier 6 parts

[0117] 1 part anti-ultraviolet agent

[0118] Antioxidant 1 part

[0119] Lubricant 1.2 parts.

[0120] The PVC resin is a mixture of calcium carbide-based PVC resin and ethylene-based PVC resin in a weight ratio of 1:1.5.

[0121] The plasticizer is a mixture composed of diisononyl cyclohexane 1,2-dicarboxylate and dioctyl adipate in a weight ratio of 2:1.

[0122] The filler is heavy calcium carbonate with a particle size of 75nm and modified by a titanate coupling agent.

[0123] The stabilizer is a mixture of calcium stearate, zinc stearate, β-diketone and ze...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of floor mats, in particular to an anti-ultraviolet and anti-oxidation floor mat and a preparation method thereof. The anti-ultraviolet and anti-oxidation floor mat includes a PVC base material layer and a silk braided layer attached to the upper surface of the PVC base material layer. The PVC substrate layer includes the following raw materials in parts by weight: 85-105 parts of PVC resin, 30-40 parts of plasticizer, 20-30 parts of filler, 3-7 parts of stabilizer, 4-8 parts of impact modifier 0.5-1.5 parts of anti-ultraviolet agent, 0.5-1.5 parts of antioxidant, 1.0-1.4 parts of lubricant. The anti-ultraviolet and anti-oxidation floor mat of the present invention has good anti-ultraviolet and anti-oxidation effects, is environmentally friendly and non-toxic, has good strength, toughness and flame retardancy, and has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of floor mats, in particular to an anti-ultraviolet and anti-oxidation floor mat and a preparation method thereof. Background technique [0002] With the development of economic construction, people's living standards are also constantly improving. There will be some floor mats in people's rooms and cars, and the floor mats are used to isolate the coldness of the ground. Traditional carpet mats are generally difficult to clean, not easy to dry after cleaning, and have the defects of mold and smell, which bring many changes to the use. At present, a new kind of PVC floor mat has appeared on the market. This kind of floor mat is almost completely made of PVC material, which is easy to clean and easy to dry. However, PVC floor mats currently on the market generally have the defect of being prone to aging. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L33/08C08L23/30C08L51/06C08K13/06C08K5/11C08K5/12C08K9/04C08K3/26C08K5/3475C08K5/134C08K5/526C08K5/103C08K5/20C08K9/12C08K3/08C08K3/22C08K3/38C08K5/098B32B27/32B32B27/20B32B27/22B32B27/12B32B5/08B32B37/02
CPCC08L27/06B32B5/08B32B27/12B32B27/20B32B27/22B32B27/322B32B37/02B32B2307/558B32B2307/71C08L2201/08C08L2205/02C08L2205/025C08L2205/035
Inventor 徐祥林罗恺青
Owner 广东雅丽斯佳新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com