Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Sun-proof and antibacterial fiber protofilament

An antibacterial fiber and raw silk technology, applied in the field of textile fiber manufacturing, can solve the problems of poor sunscreen and UV protection, easy to breed bacteria and other microorganisms, etc., and achieve the effects of excellent moisture absorption, high strength and good toughness.

Inactive Publication Date: 2017-07-07
ZHEJIANG FENGHE TEXTILE CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the excellent hygroscopic properties of vinylon fiber, it is often used to make summer clothes. However, the summer weather is hot and the intensity of ultraviolet rays is high, so sun protection has become an important thing. Due to the characteristics of vinylon fiber, its sunscreen and anti-ultraviolet properties The ability is poor, so it needs to be modified for sun protection and UV protection. At the same time, the temperature in summer is suitable, and bacteria and other microorganisms are easy to breed on the surface of clothing. For the physical and mental health of consumers, the antibacterial performance of clothing has become extremely important.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A sunscreen and antibacterial fiber precursor, prepared from the following raw materials in parts by weight: 100 parts of polyvinyl alcohol, 4 parts of sunscreen additives, 6 parts of antibacterial additives, and 625 parts of water; the sunscreen additive is composed of the following raw materials: fibrous titanium dioxide 90wt%, Glucose 2wt%, sodium ascorbate 8wt%; antibacterial additive is made up of following raw materials: aluminum phosphate 20wt%, calcium phosphate 10wt%, aluminum tripolyphosphate 70wt%;

[0026] Fibrous titanium dioxide is prepared by the following steps: first mix metatitanic acid powder and molten salt, then ball mill in ethanol at a speed of 2000rpm for 6 hours at a high speed, dry after ball milling, and then calcinate the dried raw material at 730°C for 4 hours Hours, after calcination is completed and cooled, it is ball milled in water at a medium speed at 1000rpm for 1 hour, and then washed 5 times to obtain fibrous titanium dioxide; the wei...

Embodiment 2

[0033] A sunscreen and antibacterial fiber precursor, prepared from the following raw materials in parts by weight: 100 parts of polyvinyl alcohol, 5 parts of sunscreen additives, 7 parts of antibacterial additives, and 655 parts of water; the sunscreen additive consists of the following raw materials: fibrous titanium dioxide 91wt%, Glucose 2.5wt%, sodium ascorbate 6.5wt%; antibacterial additive is made up of following raw materials: aluminum phosphate 24wt%, calcium phosphate 14wt%, aluminum tripolyphosphate 62wt%;

[0034] Fibrous titanium dioxide is prepared by the following steps: first mix metatitanic acid powder and molten salt, then ball mill in ethanol at a speed of 2500rpm for 8 hours at a high speed, dry after ball milling, and then calcinate the dried raw material at 760°C for 6 Hours, after calcination is completed and cooled, it is ball milled in water at a medium speed of 1450rpm for 1.5 hours, and then washed 6 times to obtain fibrous titanium dioxide; the weigh...

Embodiment 3

[0041] A sunscreen and antibacterial fiber precursor, prepared from the following raw materials in parts by weight: 100 parts of polyvinyl alcohol, 7 parts of sunscreen additives, 7 parts of antibacterial additives, and 685 parts of water; the sunscreen additive is composed of the following raw materials: fibrous titanium dioxide 94wt%, Glucose 2.5wt%, sodium ascorbate 3.5wt%; antibacterial additive is made up of following raw materials: aluminum phosphate 27wt%, calcium phosphate 17wt%, aluminum tripolyphosphate 56wt%;

[0042] Fibrous titanium dioxide is prepared by the following steps: first mix metatitanic acid powder and molten salt, then ball mill in ethanol at a speed of 3500rpm for 10 hours at a high speed, dry after ball milling, and then calcinate the dried raw material at 770°C for 8 Hours, calcination is completed and cooled, then ball milled in water at a medium speed at 1650rpm for 2 hours, and then washed 6 times to obtain fibrous titanium dioxide; the weight rat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
modulusaaaaaaaaaa
spfaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of production of textile fibers and discloses a sun-proof and antibacterial fiber protofilament. The sun-proof and antibacterial fiber protofilament is produced from the raw materials such as polyvinyl alcohol, a sun-proof additive, an antibacterial additive and water and the like, wherein the sun-proof additive comprises fibrous titanium dioxide, glucose and sodium ascorbate; the antibacterial additive comprises aluminum phosphate, calcium phosphate and aluminum tripolyphosphate. The sun-proof antibacterial fiber protofilament based on polyvinyl acetal fiber is high in strength, high in tenacity and excellent in moisture absorption property and has sun-proof, ultraviolet-proof and antibacterial functions; the sun-proof property of the fiber protofilament meets the national standard; the antibacterial property of the fiber protofilament is excellent.

Description

technical field [0001] The invention relates to the technical field of textile fiber manufacturing, in particular to a sunscreen and antibacterial fiber precursor. Background technique [0002] Polyvinyl acetal fiber, also known as vinylon fiber, has a relative density of 1.26-1.30g / cc, a softening point of 220-230°C, and a softening point of 110°C in water; the fineness of cotton-type short fibers is 1.4 denier; the dry and wet strengths are 5.4 gram force / denier, 4.3 gram force / denier, dry and wet elongation are 16.5%, 17.5% respectively, Young's modulus 550 kg force / mm, elastic recovery rate (3%) 70%; it is characterized by high strength, toughness Good moisture absorption, wear resistance, acid and alkali resistance, high wet strength, not afraid of mould, etc. Vinylon fiber is mainly used to make clothes, and can also be used to make various cables, canvas, agricultural windproof, cold-proof gauze, etc. [0003] Due to the excellent hygroscopic properties of vinylon fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/50D01F1/10D01F11/06D01D5/06D01D1/02
CPCD01F6/50D01D1/02D01D5/06D01F1/103D01F1/106D01F11/06
Inventor 许云峰
Owner ZHEJIANG FENGHE TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com