High-strength environmental-protection colored brick tile and preparing method thereof

A high-strength and environmentally friendly technology, applied in roofs, roof coverings, buildings, etc. using tile/slate tiles, it can solve the problems of the impact of the waterproof performance of colored tiles, the effect is not obvious, and achieve good physical isolation and waterproof effect, excellent mechanics. performance, cost reduction effect

Inactive Publication Date: 2017-07-11
HEFEI OAKS NEW BUILDING MATERIAL CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the preparation process of the color tile machine improves the water permeability of the color tile by controlling the color tile density and increases the adhesion of the pigment, the waterproof performance of the pure acrylic paint n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1:

[0029] A high-strength environmentally-friendly color brick tile and preparation method according to a preferred embodiment of the present invention;

[0030] The high-strength environment-friendly colored bricks and tiles are prepared from the following raw materials in parts by weight:

[0031] 28 parts of raw gypsum, 20 parts of diatomaceous earth, 9 parts of shale diatom mud, 23 parts of attapulgite, 26 parts of limestone, 12 parts of sodium silicate, 8 parts of glass fiber, 15 parts of river bottom fine sand, 30 parts of cement, additives 5 servings.

[0032] The attapulgite clay is a paste-like attapulgite clay, that is, the paste-like attapulgite clay before the wet beneficiation of the attapulgite clay without solid-liquid separation. The mass ratio of the attapulgite clay to water is 1:10, which has a relatively high Good viscosity and plasticity are conducive to the emulsification and bonding between raw materials. When applied to the preparation of colo...

Example Embodiment

[0044] Example 2:

[0045] A high-strength environmentally-friendly color brick tile and preparation method according to a preferred embodiment of the present invention;

[0046] The high-strength environmentally friendly color bricks and tiles are prepared from the following parts by weight of various raw materials: 20 parts by weight of raw gypsum, 10 parts of diatomaceous earth, 5 parts of shale diatom mud, 13 parts of attapulgite, 25 parts of limestone, and silicon 8 parts of sodium, 3 parts of glass fiber, 10 parts of river bottom fine sand, 21 parts of cement, 3 parts of additives.

[0047] The attapulgite clay is paste-like attapulgite clay, that is, the paste-like attapulgite clay before the wet beneficiation of the attapulgite clay without solid-liquid separation, wherein the mass ratio of the attapulgite clay to water is 1:5, which has relatively high Good viscosity and plasticity are conducive to the emulsification and bonding between raw materials. When applied to the pr...

Example Embodiment

[0059] Example 3:

[0060] A high-strength environmentally-friendly color brick tile and preparation method according to a preferred embodiment of the present invention;

[0061] The high-strength environment-friendly colored bricks and tiles are prepared from the following raw materials in parts by weight:

[0062] 35 parts of raw gypsum, 25 parts of diatomaceous earth, 12 parts of shale diatom mud, 26 parts of attapulgite, 30 parts of limestone, 15 parts of sodium silicate, 11 parts of glass fiber, 18 parts of river bottom fine sand, 35 parts of cement, additives 8 servings.

[0063] The attapulgite clay is a paste-like attapulgite clay, that is, the paste-like attapulgite clay before the wet beneficiation of the attapulgite clay without solid-liquid separation, wherein the mass ratio of the attapulgite clay to water is 1:5-10, It has good viscosity and plasticity, which is conducive to the emulsification and bonding between raw materials. When applied to the preparation of color t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Initial setting timeaaaaaaaaaa
Final setting timeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength environmental-protection colored brick tile and a preparing method thereof, and belongs to the technical field of building materials. The colored brick tile comprises the following components: raw gypsum, diatomite, shale diatom mud, attapulgite, limestone, sodium silicate, glass fibers, fine river bottom sand, cement and an additive. The preparation method comprises the steps: respectively weighing the raw gypsum, diatomite, shale diatom mud, limestone, sodium silicate, fine river bottom sand and cement, and crushing and mixing to obtain a mixture a1; mixing evenly the mixture a1 with the attapulgite, adding water during stirring, then adding the glass fibers to the mixture, and fully stirring evenly to obtain a mixture a2; and carrying out extrusion molding of the mixture a2, curing, then spraying with a coating, and drying to obtain the colored brick tile. The colored brick tile has good mechanical strength and water permeable resistance, can effectively avoid the phenomenon of cracking in the process of using the colored brick tile, can greatly improve the service life of the colored brick tile, also has good anti-mildew effect, and effectively prevent the growth of algae around the colored brick tile.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-strength environmental-friendly colored tile and a preparation method. Background technique [0002] Colored tile, that is, colored concrete roof tile, is a building material that is extruded or molded with cement and sand as the main raw materials. It has the advantages of high strength, smooth coverage and long life. It does not use clay or sintering, saves arable land and energy, and conforms to the national industrial policy. Therefore, it is a building material that conforms to the national conditions, conforms to the times, is deeply loved by the masses, and has broad development prospects. At present, domestic roll-pressed colored tiles are prone to cracking during use, which affects the popularization and use of rolled-pressed colored tiles. [0003] The Chinese invention patent with the publication number CN104016634A discloses a roll-pressed colored...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B41/63E04D1/04E04D1/16C04B111/27
CPCC04B28/04C04B41/4884C04B41/63C04B2111/00594C04B2111/27E04D1/04E04D1/16C04B22/143C04B14/08C04B14/102C04B14/28C04B22/00C04B14/42C04B14/06C04B24/282C04B2103/54C04B41/4543
Inventor 曹智远
Owner HEFEI OAKS NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap