A technology of composite materials and composite nucleating agents, applied in the field of polymer material preparation, can solve the problems of inability to guarantee the crystallinity of low mold temperature injection molding products, the effect of cold crystallization temperature is not obvious, and adapt to water cooling system technology, etc., to achieve Good comprehensive mechanical properties, shortened production process, good gloss effect

Active Publication Date: 2019-02-05
本松新材料技术(芜湖)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Over the years, a large number of researches and inventions have focused on adding various nucleating agents (including inorganic, organic and polymers, etc.) to increase the thermal crystallization peak temperature of PET to around 220°C, shortening the crystallization cycle, but such methods have no The effect of reducing the cold crystallization temperature is not obvious, and it is impossible to ensure that low mold temperature injection molding products have a high degree of crystallinity, and PET cannot be adapted to the existing water cooling system technology of injection molding machines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A pet composite material
  • A pet composite material
  • A pet composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～8

[0057] Weigh the corresponding formula components according to the formula table in Table 1, dry the weighed PET resin to a moisture content of ≤0.07%, mix it with other components except reinforcing fillers and plasticizers, Feed port feeding, glass fiber is fed from the side feeding port, plasticizer is pumped in from the middle of the extruder with a metering pump, plasticized, melted, then extruded, drawn, cooled, dried, cut pellets to obtain modified PET composite materials.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PET composite material, which comprises the following components in parts by weight: 34 to 55 parts of PET, 25 to 45 parts of enhanced filling material, 3 to 8 parts of composite nucleating agent, and 0 to 3 parts of flexibilizer; wherein the composite nucleating agent comprises a chemical nucleating agent and a plasticizer, the weight ratio of the plasticizer to PET resin is 3.5-7:100, the plasticizer is prepared by compounding a benzsulfamide plasticizer with other plasticizers, other plasticizers can be one or more of polyethylene glycol-diethyl hexyl alcohol, neopentyl glycol diphenyl ester, tribenzyl propylidene ether diethyl hexyl alcohol, and triethylene glycol diphenyl ester, the structural formula of the benzsulfamide plasticizer is represented in the description, and in the structural formula, R represents a branched alkyl group or a straight chain alkyl group. The composite material is injection-moulded at a mould temperature of 85 DEG C, the crystallization is complete, the moulding period is short, and the PET composite material can be used to produce large moulded goods or precision thin-wall moulded goods.

Description

technical field [0001] The invention relates to the field of polymer material preparation, in particular to a glass fiber-reinforced PET composite material with excellent high-temperature dimensional stability and rapid injection molding at low mold temperature. Background technique [0002] As one of the five general-purpose engineering plastics, polyethylene terephthalate (PET) has outstanding toughness, aging resistance, creep resistance, friction and wear resistance, and its glass fiber reinforced products (PET / GF) have Excellent physical and chemical properties, heat resistance and electrical properties. Compared with similar polybutylene terephthalate (PBT) and nylon (PA) materials, the overall performance of glass fiber reinforced PET is better than PBT, close to PA, The price is even more advantageous, attracting a large number of researchers to devote themselves to the research of PET plastic engineering. [0003] However, the PET molecular chain is relatively rigi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L71/02C08L23/08C08L53/02C08K13/04C08K7/14C08K5/435C08K5/098C08K3/28C08K3/34C08K5/103
CPCC08K2201/011C08K2201/014C08L67/02C08L2201/02C08L2201/08C08L2205/035C08L2205/24C08L71/02C08L23/0876C08L53/025C08K13/04C08K7/14C08K5/435C08K5/098C08K3/28C08K3/34C08K5/103
Inventor 曾昭礼陈光辉周永松徐淑芬
Owner 本松新材料技术(芜湖)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com