Processing technology of aluminum alloy for cooling device

A processing technology and technology of heat dissipation device, applied in the field of aluminum alloy, can solve problems such as condensation water corrosion, bacterial reproduction, etc., and achieve the effects of improving support strength, improving mechanical properties, and improving service life

Active Publication Date: 2017-07-14
山东创新精密科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In addition, the surface of the heat sink that has been used for a long time will be corroded by the condensed water accumulated on the surface and the bacteria will multiply. Therefore, while improving the mechanical strength and thermal conductivity of the aluminum alloy, it is also necessary to treat the surface with corrosion resistance and antibacterial treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0025] A kind of aluminum alloy processing technology for heat dissipation device of the present invention, comprises the following steps in sequence:

[0026] (1) Composition optimization; the content of each component is: Si 0.5%, Fe 0.3%, Cu 0.04%, Mn 1%, Zn 1.2%, Mg 0.3%, Zr0.2%, Sr 0.03%, and the balance is Al and unavoidable impurities.

[0027] (2) Billet making;

[0028] (3) Extrude at a speed of 1-1.2m / min, and the temperature of the mold during extrusion is 520±10°C;

[0029] (4) Quenching, the quenching method is air cooling + water cooling;

[0030] (5) Stretching and straightening, the stretching rate is 1.2%;

[0031] (6) Aging treatment, aging treatment at 180°C for 6 hours;

[0032] (7) Cleaning, the surface of the aluminum alloy workpiece is cleaned with water, acetone, and water in sequence;

[0033] (8) Coating, after alkali washing and pickling, immerse in 75°C film treatment agent for 2 minutes, take it out and dry at 120°C for 40 minutes to form a fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing technology of an aluminum alloy for a cooling device. The technologies of composition optimization, blank making, extrusion, quenching, stretcher straightening, aging treatment, cleaning and coating are sequentially carried out; and according to a prepared aluminum alloy cooling fin, the room-temperature tensile strength is not smaller than 320 MPa, the yield strength is not smaller than 230 MPa, the postwelding yield strength is not smaller than 120 MPa, corrosion resistance is high, and the antimicrobial property is good.

Description

technical field [0001] The invention relates to the technical field of aluminum alloys, in particular to an aluminum alloy processing technology for heat dissipation devices. Background technique [0002] At present, heat sinks of heat sinks made of aluminum alloys have been widely used. They are light in weight, high in strength, good in wear resistance, not easily deformed after processing, and have excellent thermal conductivity. The structure of the heat exchanger is increasingly pursued to be lighter and thinner, and the change of the structure puts forward higher requirements for the balance of the mechanical strength and thermal conductivity of the aluminum alloy. [0003] In addition, the surface of the heat sink that has been used for a long time will be corroded by the condensed water accumulated on the surface and the bacteria will multiply. Therefore, while improving the mechanical strength and thermal conductivity of the aluminum alloy, it is also necessary to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/10C22F1/053C23G1/22C23G1/12C23C22/78C23C22/05
CPCC22C21/10C22F1/002C22F1/053C23C22/05C23C22/78C23G1/125C23G1/22
Inventor 崔立新赵晓光成凯马维红
Owner 山东创新精密科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com