Noble-metal-loaded grade-hole macropore-mesoporous gamma-Al2O3 catalyst and preparation method of catalyst

A technology of hierarchical pores and noble metals, applied in the field of hierarchical pore macroporous-mesoporous γ-Al2O3 catalysts and its preparation, can solve the problems of complex preparation process, uneven loading of active components, poor pore structure, etc. The effect of surface area, excellent pore structure and pore properties, and excellent adsorption

Inactive Publication Date: 2017-07-28
WUHAN UNIV OF TECH
View PDF13 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing noble metal-supported catalysts have a series of problems such as complex preparation process, poor pore structure, and uneven loading of active components.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Noble-metal-loaded grade-hole macropore-mesoporous gamma-Al2O3 catalyst and preparation method of catalyst
  • Noble-metal-loaded grade-hole macropore-mesoporous gamma-Al2O3 catalyst and preparation method of catalyst
  • Noble-metal-loaded grade-hole macropore-mesoporous gamma-Al2O3 catalyst and preparation method of catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A hierarchical macroporous-mesoporous γ-Al loaded with noble metals 2 o 3 Catalyst, its preparation method comprises the steps:

[0047] 1) Add 3mL of deionized water to the acetonitrile solution (20ml, 99.5wt%, relative density ρ=0.79), stir evenly to obtain an aqueous solution of acetonitrile, and then uniformly drop 2g of aluminum sec-butoxide solution (97wt%, relative density ρ=0.967), found to generate white precipitate immediately, under the condition of 25 ℃, after standing for 10min, use magnetic stirrer to stir 10min under the rotating speed of 100r / min, then stand for 10min, get white precipitate I;

[0048] 2) The white precipitate I obtained in step 1) is subjected to suction filtration, and the product obtained by suction filtration is placed in an oven at 60° C., left to stand for 12 hours and fully dried to obtain a white powder, which is used as a loaded precursor (macroporous-mesoporous AlOOH Precursor);

[0049] 3) Under the condition of 25℃, 1g H ...

Embodiment 2

[0053] A hierarchical macroporous-mesoporous γ-Al loaded with noble metals 2 o 3 Catalyst, its preparation method comprises the steps:

[0054] 1) Add 3mL of deionized water to the acetonitrile solution (20ml, 99.5wt%, relative density ρ=0.79), stir evenly to obtain an aqueous solution of acetonitrile, and then uniformly drop 2g of aluminum sec-butoxide solution (97wt%, relative density ρ=0.967), found to generate white precipitate immediately, under the condition of 25 ℃, after standing for 10min, use magnetic stirrer to stir 10min under the rotating speed of 100r / min, then stand for 10min, get white precipitate I;

[0055] 2) The obtained white precipitate I obtained in step 1) is subjected to suction filtration, and the product obtained by suction filtration is placed in a 60° C. oven, left to stand for 12 hours and fully dried to obtain a white powder, which is used as a loaded precursor (macropore-mediated Porous AlOOH precursor);

[0056] 3) Add 1g H 2 PtCl 6 ·6H 2...

Embodiment 3

[0060] A hierarchical macroporous-mesoporous γ-Al loaded with noble metals 2 o 3 Catalyst, its preparation method comprises the steps:

[0061] 1) Add 4mL of deionized water to the acetonitrile solution (20ml, 99.5wt%, relative density ρ=0.79), stir evenly to obtain an aqueous acetonitrile solution, and then uniformly drop 2g of aluminum sec-butoxide solution (97wt%, relative density ρ=0.967), found to generate white precipitate immediately, under the condition of 25 ℃, after standing for 10min, use magnetic stirrer to stir 10min under the rotating speed of 100r / min, then stand for 10min, get white precipitate I;

[0062] 2) The white precipitate I product obtained in step 1) is subjected to suction filtration, and the product obtained by suction filtration is placed in a 60° C. oven, left to stand for 12 hours and fully dried to obtain a white powder, which is used as a loading precursor (macropore-mesoporous AlOOH precursor);

[0063] 3) Add 1g H 2 PtCl 6 ·6H 2 O powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Large hole sizeaaaaaaaaaa
Mesopore sizeaaaaaaaaaa
Large hole diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a noble-metal-loaded grade-hole macropore-mesoporous gamma-Al2O3 catalyst. A preparation method of the catalyst comprises the steps of with an acetonitrile water solution as a reaction medium, constructing a catalyst carrier with a hole-hole crosslinking and cut-through duct system by regulating the content of water in an acetonitrile water system in a reaction process, and carrying out noble metal loading, so as to synthesize noble-metal-loaded macropore-mesoporous aluminum oxide catalyst with the grade holes. The preparation method is simple, feasible and applicable to batch production, synthesis conditions are mild, the reaction is easily controllable, and the cycle is short; the prepared catalyst has a grade-hole macropore-mesoporous structure, mesopores are formed by aluminum oxide nanorods through assembling, and loaded noble metal active components are uniformly distributed on carriers, so that the catalyst integrally has good duct connectivity, a high specific surface area and a large pore volume and has good application prospects in the fields of petrochemical engineering and catalysts and particularly the fields of deoxidation and hydrogenation of biomass diesel, utilization of biomass diesel byproducts and the like.

Description

technical field [0001] The invention belongs to the technical field of inorganic synthesis, and in particular relates to a hierarchically porous macroporous-mesoporous γ-Al loaded with precious metals 2 o 3 Catalyst and method for its preparation. Background technique [0002] In modern petrochemical industry, new energy development, and comprehensive utilization of resources, supported catalysts occupy an irreplaceable important position. γ-Al, known as "activated alumina", 2 o 3 Because of its advantages such as adjustable pore structure, large specific surface area, good adsorption performance, low price, acidic surface and good thermal stability, it has become a catalyst or catalyst carrier widely used in the chemical and petrochemical industries. It is widely used in ammonia cracking, ammonia refining, hydroreforming and other fields. Due to their stable chemical properties, difficult to be oxidized, and their excellent physical properties and unique catalytic activ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/42B01J35/10
CPCB01J23/42B01J35/615B01J35/651B01J35/635B01J35/647
Inventor 苏宝连汪建南彭钊孙明慧陈丽华
Owner WUHAN UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com