Adsorption material for gas masks

A technology of adsorption material and gas mask, which is applied in the field of protective equipment, can solve the problems of easy failure of disinfection drugs and single function of activated carbon of gas mask, and achieve the effect of inhibiting microbial growth, low cost and convenient use

Inactive Publication Date: 2017-08-08
林志雄
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing gas respirator is to place active carbon or disinfectant medicine in the air intake of mouth mask, and the poisonous air on the job site is sucked into human body after being filtered by disinfectant medicine or activated carbon, and the activated carbon function of this kind of gas mask mask is single and the disinfectant medicine is also easy to fail

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Adsorbent materials for gas masks, including the following components in parts by mass:

[0025] 20 parts of montmorillonite,

[0026] 15 parts of modified activated carbon,

[0027] 7 parts of biomass adsorbent;

[0028] Described biomass adsorbent is prepared according to the following steps:

[0029] a. Dry the corncobs and crush them into powders of 100-150 mesh;

[0030] b. Disperse the powder in step a at 6 g / mL in a mixture of deionized water and ethanol to form a suspension, and stir the suspension under ultrasonic conditions to disperse the powder evenly; wherein the deionized water and ethanol The concentration of ethanol in the mixture is 70v / v%;

[0031] c. Add 3wt% citric acid to the suspension in step b, stir well and place it at 4°C for 36 hours at a constant temperature, then at 16°C for 36 hours, then add baking soda until the pH value= 7~8;

[0032] d. Filter with nylon mesh, wash with deionized water, and then dry at 60° C. to obtain the biomass...

Embodiment 2

[0041] Adsorbent materials for gas masks, including the following components in parts by mass:

[0042] 15 parts of montmorillonite,

[0043] 10 parts of modified activated carbon,

[0044] 5 parts of biomass adsorbent;

[0045] Described biomass adsorbent is prepared according to the following steps:

[0046] a, bagasse is dried and crushed to 100 mesh powder;

[0047] b. Disperse the powder of step a in a mixture of deionized water and ethanol at 1 g / mL to form a suspension, and stir the suspension under ultrasonic conditions to disperse the powder evenly; wherein the deionized water and ethanol The concentration of ethanol in the mixture is 60v / v%;

[0048] c. Add 1wt% citric acid to the suspension in step b, stir well and place it at 0°C for 24 hours, then at 10°C for 30 hours, then add baking soda until the pH value= 7~8;

[0049] d. Filter with nylon mesh, wash with deionized water, and then dry at 60° C. to obtain the biomass adsorbent.

[0050] Described modifie...

Embodiment 3

[0058] Adsorbent materials for gas masks, including the following components in parts by mass:

[0059] 25 parts of montmorillonite,

[0060] 20 parts of modified activated carbon,

[0061] 8 parts of biomass adsorbent;

[0062] Described biomass adsorbent is prepared according to the following steps:

[0063] a, corncob is dried, pulverized to 150 mesh powder;

[0064] b. Disperse the powder in step a at 8 g / mL in a mixture of deionized water and ethanol to form a suspension, and stir the suspension under ultrasonic conditions to disperse the powder evenly; wherein the deionized water and ethanol The concentration of ethanol in the mixed solution is 80v / v%;

[0065] c. Add 6wt% citric acid to the suspension in step b, stir well and place it at 8°C for 48 hours, then at 18°C ​​for 45 hours, then add baking soda until the pH value= 7~8;

[0066] d. Filter with nylon mesh, wash with deionized water, and then dry at 60° C. to obtain the biomass adsorbent.

[0067] Describe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an adsorption material for gas masks. The adsorption material comprises the following components by mass: 15-25 parts of montmorillonite, 10-20 parts of modified activated carbon, and 5-8 parts of a biomass adsorbent. The biomass adsorbent is prepared by: drying and crushing corncob or bagasse, dispersing the obtained crushed material into a mixed solution of deionized water and ethanol to form a suspension solution, then adding citric acid, carrying out staged constant temperature standing, then adding baking soda, and performing washing and drying. The adsorption material for gas masks obtained by the invention has good adsorption function, can effectively absorb various suspended matters in the air, also has weak electrical conductivity, and can play an antistatic role. The adsorption material for gas masks obtained by the invention also can effectively inhibit microorganism growth and avoid mildewing. The obtained adsorption material for gas masks is low in cost and convenient for use, and is also applicable to interior decoration, air purification and other fields.

Description

technical field [0001] The invention belongs to the technical field of protective equipment and relates to an adsorption material for a gas mask. Background technique [0002] A gas mask is a kind of anti-virus product that protects the respiratory system of personnel. It is generally composed of a filter box or a canister and a mask body. The main body of the mask isolates the air and acts as a seal; the canister of the poison box plays the role of filtering poisonous gas and dust, and is mainly used in the working environment with low concentration of harmful gas and dust. Respirators are widely used in the fields of petroleum, chemical industry, mining, metallurgy, military, fire protection, emergency rescue and disaster relief, health and epidemic prevention, technology and environmental protection. [0003] Existing gas respirator is to place activated carbon or disinfectant medicine at the air intake of mouth mask, and the poisonous air on the job site is sucked into ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/30B01J20/22A61L9/014
CPCB01J20/16A61L9/014B01D53/04B01D53/81B01D2257/30B01D2257/70B01D2257/7027B01D2257/93B01D2258/06B01J20/20B01J20/22
Inventor 林志雄
Owner 林志雄
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap