Functional self-assembling nano-polypeptide hydrogel material and application thereof in preparation of hemostatic materials

A hydrogel and short peptide technology, applied in medical science, drug delivery, bandages, etc., can solve the problems of long hemostasis time, difficult dressing change, wound adhesion, etc., and achieves easy operation, good biocompatibility, and simple operation. Effect

Inactive Publication Date: 2017-08-15
JINAN UNIVERSITY
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Commonly used clinical hemostatic materials such as hemostatic gauze, hemostatic fiber, and hemostatic bandage have limitations in use: the hemostatic time is longer, it is easy to adhere to the wound and it is difficult to ch...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional self-assembling nano-polypeptide hydrogel material and application thereof in preparation of hemostatic materials
  • Functional self-assembling nano-polypeptide hydrogel material and application thereof in preparation of hemostatic materials
  • Functional self-assembling nano-polypeptide hydrogel material and application thereof in preparation of hemostatic materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: the preparation of the polypeptide material of hydrogel

[0030] The short peptide (its sequence is: (arginine-alanine-aspartic acid-alanine) 4 -Arginine-Isoleucine-Lysine-Valine-Alanine-Valine) is dissolved in ultrapure water, and then configured into a solution with a concentration of 5~15ml / mL, and Tris-base solution Mix, the concentration of Trsi-base solution is 0.1~1 mol / mL, adjust its pH value to 7, and then mix with PBS / DMEM solution at a volume ratio of 2:1, and quickly form a gel after standing still, and after the properties are stable, Ready to use.

[0031] Such as figure 1 As shown, the rheometer was used to detect the shear thinning performance of the neutral aqueous solution of the above-mentioned short peptide. It has the characteristics of shear thinning and is very suitable for injection. It can be injected to the bleeding point to form a hydrogel instantly to control bleeding.

Embodiment 2

[0032] Embodiment 2: the preparation of the polypeptide material of hydrogel

[0033] The short peptide (its sequence is: (arginine-alanine-aspartic acid-alanine) 4 -Lysine-Isoleucine-Lysine-Valine-Alanine-Valine is dissolved in ultrapure water, and then configured into a solution with a concentration of 5~15ml / mL, and mixed with Tris-base solution , the concentration of Trsi-base solution is 0.1~1 mol / mL, adjust its pH value to 7, and then mix it with PBS / DMEM solution at a volume ratio of 2:1. ready for use.

Embodiment 3

[0034] Embodiment 3: the polypeptide material preparation of hydrogel

[0035] The short peptide (its sequence is: (arginine-alanine-aspartic acid-alanine) 4 -Histidine-Isoleucine-Lysine-Valine-Alanine-Valine is dissolved in ultrapure water, and then prepared into a solution with a concentration of 5~15ml / mL, and mixed with Tris-base solution , the concentration of Trsi-base solution is 0.1~1 mol / mL, adjust its pH value to 7, and then mix it with PBS / DMEM solution at a volume ratio of 2:1. ready for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a short peptide. The sequence of the short peptide is (arginine-alanine-aspartic acid-alanine)4-arginine-isoleucine-lysine-valine-alanine-valine, (arginine-alanine-aspartic acid-alanine)4-lysine-isoleucine-lysine-valine-alanine-valine or (arginine-alanine-aspartic acid-alanine)4-histidine-isoleucine-lysine-valine-alanine-valine. The invention simultaneously discloses a functional self-assembling nano-polypeptide hydrogel material prepared from the short peptide. The hydrogel material has a shear thinning characteristic, can immediately form hydrogel after being injected to a bleeding point through an injector, can be applied to rapid hemostasis and is particularly applied to the situation that the bleeding point environment is complicated; and the short peptide can form nano-fiber hydrogel at the room temperature when the pH value is neutral and can simulate a natural extracellular matrix structure and has good physical and chemical properties and biocompatibility.

Description

technical field [0001] The invention belongs to the technical field of hemostatic materials, and more specifically relates to a functional self-assembled nanometer polypeptide hydrogel material and its application in the preparation of hemostatic materials. Background technique [0002] First aid treatment of sudden accidents in daily life, trauma hemostasis in the operation process of patients in the hospital, especially the rescue of wounded soldiers in war, it is very important to effectively and quickly stop bleeding locally in patients, because uncontrolled bleeding is Leading cause of sudden accidents, hemorrhage during medical operations, or death on the battlefield. Early control of bleeding becomes the best strategy to reduce the death of patients. In the Iraq campaign, 50% of the casualties on the battlefield were due to excessive bleeding. Even when the casualty is able to support medical equipment for treatment, uncontrolled hemorrhage is still the leading fact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L26/00
CPCA61L26/008A61L26/0047A61L2400/04C08L89/00
Inventor 何留民邵晗许小婷
Owner JINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap