Caries-prevention toothpaste and preparing method thereof

A technology for toothpaste and dental caries, applied in the field of anti-caries toothpaste and its preparation, can solve the problems of insignificant other effects and unfavorable human health, achieve good antibacterial and anti-inflammatory effects, reduce the exogenous stain index of teeth, and inhibit the formation of dental caries. Effect

Inactive Publication Date: 2017-08-18
缪来耿
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, the anti-caries toothpaste on the market is mainly fluoride-containing toothpaste, and long-term use of fluoride-containing toothpaste is not good for human health. In addition, anti-caries toothpaste has the defect that other effects are not obvious except for the effect of preventing dental caries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Caries-prevention toothpaste and preparing method thereof
  • Caries-prevention toothpaste and preparing method thereof
  • Caries-prevention toothpaste and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1, a kind of anti-caries toothpaste

[0050] The anti-caries toothpaste consists of the following components and parts by weight thereof:

[0051] 0.1 part of functional powder, 22 parts of calcium carbonate, 23 parts of sorbitol, 1 part of cocamidopropyl betaine, 0.4 part of sodium carboxymethylcellulose, 0.03 part of sodium saccharin, 0.03 part of methyl paraben, 0.2 parts of sodium alginate and 24 parts of deionized water.

[0052] The functional powder is composed of hydroxyapatite modified material, tourmaline nano powder and zinc oxide nano powder in a weight ratio of 13:6:3.

[0053] The tourmaline nano powder is composed of lithium tourmaline nano powder and magnesium tourmaline nano powder in a weight ratio of 2:13.

[0054] The particle diameter of the tourmaline nano powder is 80nm, and the particle diameter of the zinc oxide nano powder is 30nm.

[0055] The preparation method of the hydroxyapatite modified material is:

[0056] (1) Take 50mL ...

Embodiment 2

[0066] Embodiment 2, a kind of anti-caries toothpaste

[0067] The anti-caries toothpaste consists of the following components and parts by weight thereof:

[0068] 0.3 parts of functional powder, 28 parts of calcium carbonate, 28 parts of sorbitol, 2 parts of cocamidopropyl betaine, 1.2 parts of sodium carboxymethylcellulose, 0.05 parts of sodium saccharin, 0.06 parts of methyl paraben, 0.5 parts of sodium alginate and 30 parts of deionized water.

[0069] The functional powder is composed of hydroxyapatite modified material, tourmaline nano powder and zinc oxide nano powder in a weight ratio of 15:4:1.

[0070] The tourmaline nano powder is composed of lithium tourmaline nano powder and magnesium tourmaline nano powder in a weight ratio of 4:9.

[0071] The particle diameter of the tourmaline nano powder is 110nm, and the particle diameter of the zinc oxide nano powder is 90nm.

[0072] The preparation method of the hydroxyapatite modified material is:

[0073] (1) Take ...

Embodiment 3

[0083] Embodiment 3, a kind of anti-caries toothpaste

[0084] The anti-caries toothpaste consists of the following components and parts by weight thereof:

[0085] 0.2 parts of functional powder, 25 parts of calcium carbonate, 25 parts of sorbitol, 1.2 parts of cocamidopropyl betaine, 0.7 parts of sodium carboxymethylcellulose, 0.04 parts of sodium saccharin, 0.04 parts of methyl paraben, 0.4 parts of sodium alginate and 28 parts of deionized water.

[0086] The functional powder is composed of hydroxyapatite modified material, tourmaline nano powder and zinc oxide nano powder in a weight ratio of 14:5:2.

[0087] The tourmaline nano powder is composed of lithium tourmaline nano powder and magnesium tourmaline nano powder in a weight ratio of 3:10.

[0088] The particle diameter of the tourmaline nano powder is 100nm, and the particle diameter of the zinc oxide nano powder is 50nm.

[0089] The preparation method of the hydroxyapatite modified material is:

[0090] (1) Ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of articles of daily use, and particularly relates to caries-prevention toothpaste and a preparing method thereof. The caries-prevention toothpaste comprises, by weight, 0.1-0.3 part of functional powder body, 22-28 parts of calcium carbonate, 23-28 parts of sorbitol, 1-2 parts of cocamidopropyl betaine, 0.4-1.2 parts of sodium carboxymethylcellulose, 0.03-0.05 part of saccharin sodium salt, 0.03-0.06 part of methyl 4-hydroxybenzoate, 0.2-0.5 part of sodium alginate, and 24-30 parts of deionized water. The caries-prevention toothpaste does not contain fluorine, and conducts daily maintenance of teeth, at the same time, the caries-prevention toothpaste has a good anti-microbial and anti-inflammation effect, can more effectively reduce oral cavity germs, alleviate the oral cavity problem generated by the germs, the germs are prevented from invading the human body from the oval cavity, an oval cavity environment in which cariogenic bacteria do not easily propagate is created for the human body, and the formation of decayed teeth can be effectively inhibited.

Description

technical field [0001] The invention belongs to the technical field of daily chemical products, and in particular relates to an anti-caries toothpaste and a preparation method thereof. Background technique [0002] "Dental caries", commonly known as "tooth decay" and "tooth decay", is a disease with a very high incidence rate in humans. The third oral health survey in my country shows that more than 66 out of every one hundred 5-year-old children have dental caries in their mouths. Among middle-aged people aged 35-44, this proportion rises to 88.1%, while those aged 65-74 The caries rate of the elderly is as high as 98.4%. The World Health Organization has listed dental caries, tumors, and cardiovascular diseases as three key human diseases. Like the latter two diseases, dental caries also has the characteristics of good preventive effect, less pain, less damage and less cost in early treatment. [0003] Dental caries is a progressive lesion of tooth hard tissue caused by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/73A61K8/49A61K8/19A61K8/24A61K8/27A61K8/34A61K8/37A61K8/44A61Q11/00A61Q17/00
CPCA61K8/733A61K8/19A61K8/24A61K8/27A61K8/345A61K8/37A61K8/442A61K8/49A61K8/731A61K2800/413A61Q11/00A61Q17/005
Inventor 缪来耿
Owner 缪来耿
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com