A process for preparing polyurethane powder adhesive by using polyurethane prepolymer reverse phase suspension polymerization method
A technology of polyurethane prepolymer and polyurethane powder, which is applied in the field of polymer chemistry, can solve the problems of endangering the health of workers, time-consuming process, and high production cost, and achieves the effects of convenient implementation, controllable softness and hardness, and easy construction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0035] (1) Add chain extender ethylenediamine into liquid paraffin (mass ratio 1:6), heat in a water bath to 50°C, and stir for 5 minutes at a rotational speed of 600r / min to obtain a water-in-oil dispersion mixed liquid;
[0036] (2) Keep the water-in-oil dispersion system at a constant temperature to 50°C, slowly add polyurethane prepolymer (the mass ratio of polyurethane prepolymer to liquid paraffin is 1:25), and carry out chain extension reaction for 50 minutes to obtain suspension in water;
[0037] (3) Add water-based polyurethane hardener (the mass ratio of water-based polyurethane hardener to polyurethane prepolymer is 1:5), solid particles appear in about 6-8 minutes, and the whole process continues to stir and react for 40 minutes, and the temperature is cooled to obtain a solid containing polyurethane glue The suspension of the particles; after filtering and drying at 30°C, the polyurethane powder glue of the present invention can be obtained.
[0038] Wherein, wh...
Embodiment 2
[0040] (1) Add the chain extender ethylenediamine to the recovered liquid paraffin obtained in Example 1 (mass ratio: 1:8), heat it in a water bath to 40°C, and stir for 10 minutes at a speed of 800r / min to obtain water-in-oil Dispersion system mixture;
[0041] (2) Keep the water-in-oil dispersion system at a constant temperature to 40°C, slowly add polyurethane prepolymer (the mass ratio of polyurethane prepolymer to recovered liquid paraffin is 1:40), and carry out chain extension reaction for 60 minutes to obtain oil Water-encapsulated suspensions;
[0042] (3) Add water-based polyurethane hardener (the mass ratio of water-based polyurethane hardener to polyurethane prepolymer is 1:8), and solid particles appear in about 4-6 minutes. The whole process continues to stir and react for 30 minutes, and the temperature is cooled to obtain a solid containing polyurethane glue. Suspension of particles. After filtering and drying at 30°C, the polyurethane powder glue of the pres...
Embodiment 3
[0044] (1) Add the chain extender ethylenediamine to the recovered liquid paraffin obtained in Example 1 (mass ratio: 1:7), heat it in a water bath to 55°C, and stir for 15 minutes at a speed of 800r / min to obtain water-in-oil Dispersion system mixture;
[0045] (2) Keep the temperature of the water-in-oil dispersion system mixture at 55°C, slowly add the polyurethane prepolymer (the mass ratio of the polyurethane prepolymer to the recovered liquid paraffin is 1:50), and carry out the chain extension reaction for 50 minutes to obtain the oil Water-encapsulated suspensions;
[0046] (3) Add water-based polyurethane hardener (the mass ratio of water-based polyurethane hardener to polyurethane prepolymer is 1:10), solid particles appear in about 2-5 minutes, and the whole process continues to stir and react for 30 minutes, and the temperature is cooled to obtain a solid containing polyurethane glue Suspension of particles. After filtering and drying at 30°C, the polyurethane po...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com