Slipproofing agent for surface of ceramic tile and preparation method of slipproofing agent

A technology of anti-slip agent and surfactant, applied in the field of anti-slip agent for ceramic tile surface and its preparation, can solve the problems of inconvenience, hidden danger, good anti-slip effect, etc., achieve good effect, eliminate cleaning, and increase the effect of anti-slip effect

Active Publication Date: 2017-09-01
GUANGDONG QINGZHU TECH CO LTD
View PDF1 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As we all know, the aqueous solution of hydrogen fluoride can chemically react with the silicate on the surface of porcelain / stone bricks, so the anti-slip agents on the market are almost all strongly acidic solutions that use hydrogen fluoride acidic solution as the main agent. The strong acidity of the product leads to certain safety, environmental protection and labor protection hidden dangers and inconvenience in the production, transportation, storage and use of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Slipproofing agent for surface of ceramic tile and preparation method of slipproofing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] This embodiment relates to an anti-slip agent for ceramic tile surfaces, the anti-slip agent includes the following raw materials in parts by weight:

[0103] Fluoride salt 30wt%

[0104] Corrosion inhibitor 5wt%

[0105] Surfactant 0.5wt%

[0106] Humectant 1wt%

[0107] Fragrance 0.25wt%

[0108] The balance is water.

[0109] The fluoride salt is ammonium fluoride; the corrosion inhibitor is compounded by sodium oxalate and ammonium sulfate at a molar ratio of 1:1; the surfactant is sodium dodecylbenzene sulfonate; the humectant is glycerol.

[0110] The preparation method of the anti-slip agent for the tile surface comprises the following steps:

[0111] (1) Weigh an appropriate amount of fluoride salt, dissolve it in water and stir to obtain an aqueous solution of fluoride salt;

[0112] (2) Weigh an appropriate amount of corrosion inhibitor and add it to the fluoride salt solution, and stir evenly to obtain a corrosion inhibition salt solution;

[0113] (3)...

Embodiment 2

[0119] This embodiment relates to an anti-slip agent for ceramic tile surfaces, the anti-slip agent includes the following raw materials in parts by weight:

[0120] Fluoride salt 20wt%

[0121] Corrosion inhibitor 3wt%

[0122] Surfactant 0.5wt%

[0123] Humectant 1wt%

[0124] Fragrance 0.2wt%

[0125] The balance is water.

[0126] The fluoride salt is ammonium fluoride; the corrosion inhibitor is compounded by sodium oxalate and ammonium sulfate at a molar ratio of 1:0.8; the surfactant is sodium dodecylbenzene sulfonate; the humectant is glycerol.

[0127] The preparation method of the anti-slip agent for the tile surface comprises the following steps:

[0128] (1) Weigh an appropriate amount of fluoride salt, dissolve it in water and stir to obtain an aqueous solution of fluoride salt;

[0129] (2) Weigh an appropriate amount of corrosion inhibitor and add it to the fluoride salt solution, and stir evenly to obtain a corrosion inhibition salt solution;

[0130] (3...

Embodiment 3

[0136] This embodiment relates to an anti-slip agent for ceramic tile surfaces, the anti-slip agent includes the following raw materials in parts by weight:

[0137] Fluoride salt 25wt%

[0138] Corrosion inhibitor 4wt%

[0139] Surfactant 0.5wt%

[0140] Humectant 1wt%

[0141] Fragrance 0.2wt%

[0142] The balance is water.

[0143] The fluoride salt is ammonium fluoride; the corrosion inhibitor is compounded by sodium oxalate and ammonium sulfate at a molar ratio of 1:1.1; the surfactant is sodium dodecylbenzene sulfonate; the humectant is glycerol.

[0144] The preparation method of the anti-slip agent for the tile surface comprises the following steps:

[0145] (1) Weigh an appropriate amount of fluoride salt, dissolve it in water and stir to obtain an aqueous solution of fluoride salt;

[0146] (2) Weigh an appropriate amount of corrosion inhibitor and add it to the fluoride salt solution, and stir evenly to obtain a corrosion inhibition salt solution;

[0147] (3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a slipproofing agent for the surface of a ceramic tile and a preparation method of the slipproofing agent. The slipproofing agent is prepared from villiaumite, a corrosion inhibitor, a surfactant, a humectant, essence and the balance of water, wherein the villiaumite is ammonium fluoride and / or ammonium hydrogen fluoride. The preparation method of the slipproofing agent comprises the following steps:, at 25 to 30 DEG C, weighing and taking proper raw materials in sequence, and uniformly agitating the proper raw materials, so as to subsequently obtain the slipproofing agent for the surface of the ceramic tile. According to the slipproofing agent, the villiaumite is used as a main raw material; a product is a neutral aqueous solution; a fluorine ion generates a chemical reaction with a silicate component in the ceramic tile under the action of an ammonium ion in a formula, so as to produce silicon fluoride gas for escaping; the direct effect of the chemical reaction is that numerous nano-sized microporous structures are formed in the surface of the ceramic tile; thus, a slipproofing effect is achieved; nontoxic and harmless raw materials are used by the formula of the slipproofing agent; a neutral solution is convenient to transport and use; further, the slipproofing agent provided by the invention has ultrahigh seepage force.

Description

technical field [0001] The invention relates to the technical field of ceramic tile anti-skid, in particular to an anti-skid agent for ceramic tile surfaces and a preparation method thereof. Background technique [0002] Anti-slip agent is a liquid that prevents slipping and can be used on natural stone or hard tile surfaces such as ceramic tiles, floor tiles, terrazzo, flagstone, granite, marble, ceramic and ceramic bathtubs, shower floor and other stone or inorganic materials surface. [0003] With the needs of urbanized buildings, more and more buildings use bright hard materials such as marble, tiles, and mosaics. These materials are suitable for large buildings such as exhibition halls, hotels, supermarkets, shopping centers, restaurants, gymnasiums, swimming pools, Bathrooms and residential buildings are indispensable. But the ensuing problem is that some slipping accidents continue to occur due to the smoothness of the ground, and even cause human disability. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85
CPCC04B41/009C04B41/5018C04B41/85C04B2111/00362C04B35/00C04B41/5014C04B41/46C04B41/4535C04B41/4905C04B41/4803
Inventor 曹志勇邵友元刘柳
Owner GUANGDONG QINGZHU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com