High-strength and wear-resisting liteglow glass product and preparation method thereof

A glass product, high-strength technology, applied in the field of glass products, can solve the problems of broken glass bubbles, inconvenient daily use, waste of cost, etc., and achieve the effects of reducing power consumption, good application value, and convenient operation.

Inactive Publication Date: 2017-10-03
HEFEI LIYUTAI GLASS PROD CO LTD
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, some developed countries have certain safety specifications for various electrical products. Glass bulbs are highly fragile products, and the fragments are extremely sharp, which can easily hurt people. Glass bulbs sold to developed countries must meet the requirements. The outside of the glass bulb is covered with a protective layer to prevent the glass bulb from accidentally breaking and hurting people during actual use or when replacing and installing the bulb
In addition, some electronic products such as mobile phones, media players and other devices are also susceptible to fragile behavior, which not only causes inconvenience to people's daily use, but also causes waste of cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-strength wear-resistant luminous glass product and a preparation method of a preferred embodiment of the present invention;

[0026] The high-strength wear-resistant luminous glass product is prepared from the following parts by weight of each raw material:

[0027] 69 parts of silicon dioxide;

[0028] 5 parts of aluminum oxide;

[0029] 8 parts of calcium oxide;

[0030] 6 parts of magnesium oxide;

[0031] 1.5 parts of graphene;

[0032] 7 parts of titanium dioxide;

[0033] 12 parts of boron trioxide;

[0034] 6 parts of sodium silicate;

[0035] 2.5 parts of potassium oxide;

[0036] 3 parts of antimony oxide;

[0037] 2.5 parts of arsenic oxide;

[0038] 4 parts of luminous powder.

[0039] The luminous powder is a light-induced energy storage type luminous powder. Because of its short excitation time, long luminescence and afterglow time, high brightness, it does not contain any radioactive substances, is non-toxic, harmless, non-burning, does not contain phosphorus, lead a...

Embodiment 2

[0048] A high-strength wear-resistant luminous glass product and a preparation method of a preferred embodiment of the present invention;

[0049] The high-strength wear-resistant luminous glass product is prepared from the following raw materials in parts by weight:

[0050] 60 parts of silica;

[0051] 3 parts of aluminum oxide;

[0052] 5 parts of calcium oxide;

[0053] 2 parts of magnesium oxide;

[0054] 0.5 part of graphene;

[0055] 5 parts of titanium dioxide;

[0056] 6 parts of boron trioxide;

[0057] 4 parts of sodium silicate;

[0058] 1 part of potassium oxide;

[0059] 0.5 parts of antimony oxide;

[0060] 1.5 parts of arsenic oxide;

[0061] 2 parts of luminous powder.

[0062] The luminous powder is a light-induced energy storage type luminous powder.

[0063] The method for preparing high-strength wear-resistant luminous glass products of the present invention includes the following steps:

[0064] (1) Weigh the raw materials according to the proportions, and place them in the b...

Embodiment 3

[0071] A high-strength wear-resistant luminous glass product and a preparation method of a preferred embodiment of the present invention;

[0072] The high-strength wear-resistant luminous glass product is prepared from the following raw materials in parts by weight:

[0073] 75 parts of silicon dioxide;

[0074] 8 parts of aluminum oxide;

[0075] 10 parts of calcium oxide;

[0076] 7 parts of magnesium oxide;

[0077] Graphene 2.5 parts;

[0078] 10 parts of titanium dioxide;

[0079] 15 parts of boron trioxide;

[0080] 9 parts of sodium silicate;

[0081] 3 parts of potassium oxide;

[0082] Antimony oxide 3.5 parts;

[0083] 4 parts of arsenic oxide;

[0084] 5 parts of luminous powder.

[0085] The luminous powder is a light-induced energy storage type luminous powder.

[0086] The method for preparing high-strength wear-resistant luminous glass products of the present invention includes the following steps:

[0087] (1) Weigh each raw material according to the proportion, and place it in a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength and wear-resisting liteglow glass product and a preparation method thereof. The glass product is prepared from the following components: silicon dioxide, aluminum oxide, calcium oxide, magnesium oxide, graphene, titanium dioxide, diboron trioxide, sodium silicate, potassium oxide, antimony oxide, arsenic oxide and noctilucent powder. The preparation method comprises the following steps: firstly, carrying out mixed melting on all the components to obtain a molten mass; secondly, raising the temperature of the molten mass to 1400 to 1500DEG C and performing thermal insulation for 12 to 14 hours; thirdly, feeding a glass molten mass into a forming machine to obtain glass products with different shapes and sizes; fourthly, carrying out annealing treatment on the glass products to obtain a finished product. The glass product prepared by the preparation method disclosed by the invention has better strength and wear resistance; the fragile degree of the product can be greatly reduced, the service life of the product is prolonged, and the use cost of the product is reduced.

Description

Technical field [0001] The invention relates to the technical field of glass products, in particular to a high-strength wear-resistant luminous glass product and a preparation method. Background technique [0002] Glass products are widely used in all corners of life. For example, a common ordinary light bulb includes two parts: a glass bulb and a metal shell. Inside the glass bulb, there is a filament wound in a spiral shape, and the filament is connected to a bracket made of metal wire; Both ends of the filament are respectively connected to two connection points of the metal shell. At present, some developed countries have certain safety specification requirements for various electrical products. Glass bulbs are highly fragile products, and the fragments are extremely sharp and easily hurt. The glass bulbs sold in developed countries must meet the requirements The outside of the glass bulb is covered with a protective layer to prevent the glass bulb from accidentally breaking...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C4/12C03C6/04C03C6/02C03C1/00
CPCC03C1/00C03C4/12
Inventor 武娟
Owner HEFEI LIYUTAI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com