Mesh-shaped polyurethane foam anti-explosive barrier material mixed with activated superfine waste rubber powder and its preparation method

An explosion-proof barrier material and polyurethane foam technology, which is applied in the field of reticulated polyurethane foam explosion-proof barrier material and its preparation, can solve the problems of short life, poor waterproofness, and increased cost of use, and achieve high opening rate, strong explosion-proof barrier ability, The effect of improving the service life

Inactive Publication Date: 2017-10-17
安徽圣源橡塑科技有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of reticulated polyurethane foam is restricted by the season, its life is short, it needs to be replaced regularly, and its waterproofness is poor, which increases the cost of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A reticular polyurethane foam explosion-proof barrier material compounded with activated ultrafine waste rubber powder is prepared from the following raw materials in parts by weight: 80 parts of polyether polyol with a molecular weight of 3000, 60 parts of toluene diisocyanate, activated ultrafine waste 5 parts of rubber powder, 8 parts of foaming agent, 0.5 part of foam stabilizer, 0.1 part of stannous octoate, 0.1 part of triethylenediamine, 1 part of nano-expanded graphite, and 1 part of ultrafine rare earth tailings powder.

[0016] Among them, the activated superfine waste rubber powder is obtained by putting 150 mesh superfine waste rubber powder into the activation solution at 40°C for 2.5 hours, then filtering, washing and drying; the activation solution is made of 30% hydrogen peroxide and high iron Potassium acid and water are compounded according to the weight part of 0.1:0.1:1.

[0017] The preparation method of the reticulated polyurethane foam explosion-p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mesh-shaped polyurethane foam anti-explosive barrier material mixed with activated superfine waste rubber powder and its preparation method. In the invention, a traditional mesh-shaped polyurethane foam material is added with superfine waste rubber powder after activation treatment of hydrogen peroxide / potassium ferrate composite system so as to perform filling and modification treatment. The surface of the activated waste rubber powder contains multiple functional groups, the reaction activity is high, and the compatibility with the system is good; the material has the advantages of reducing the production cost of the mesh-shaped polyurethane foam, effectively improving the physical performance and wave absorbing oil resistance of the mesh-shaped polyurethane foam, prolonging the service life and further improving the anti-explosive barrier ability; besides, the added nano expanded graphite and superfine rare-earth tailing powder and other materials have coordinately enhanced the meshing performance of the composite polyurethane material; the aperture ratio is higher, and the anti-explosive barrier ability is stronger.

Description

technical field [0001] The invention relates to the technical field of explosion-proof barrier materials, in particular to a reticular polyurethane foam explosion-proof barrier material compounded with activated superfine waste rubber powder and a preparation method thereof. Background technique [0002] my country is a big country in tire production and automobiles. With the rapid increase of family car ownership, a large number of waste tires are produced every year. How to effectively recycle these waste tires and prevent environmental pollution has very important practical significance and huge economic value. . At present, the more common waste tire recycling methods mainly include direct utilization of prototypes, heat generation by incineration, retreading of old tires, production of recycled rubber, and production of vulcanized rubber powder. Among them, the production of rubber powder is the most common processing method. At present, it is mainly used in the fields ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L19/00C08K7/24C08K3/00C08J9/04C08G18/76C08G18/48
CPCC08L75/08C08G18/48C08G18/7614C08J9/04C08J2375/08C08J2419/00C08K2201/011C08L2203/14C08L19/003C08K7/24C08K3/00
Inventor 王新志张凯郑海迪
Owner 安徽圣源橡塑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap