Light-emitting type building coating material

A kind of architectural coating and luminous technology, which is applied in the field of building materials, can solve the problems of short luminous time at night, failure to display luminous effect, and toxic raw materials, so as to improve the anti-contamination performance and self-cleaning performance, and meet the diverse needs of the market. Long lasting effect of high brightness

Inactive Publication Date: 2017-11-03
RUGAO CHANGJIANG SCI & TECHCAL IND CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The night-time luminous products in the domestic paint market generally use synthetic resin emulsion colorful spray paints. Although this paint is rich in color and strong in texture, it also has some shortcomings, such as the dull surface after decoration. Unable to display the luminous effect, some raw materials are toxic or flammable and explosive, not environmentally friendly, and harmful to production and construction personnel, some light-emitting time at night is short, production investment is large, and the cost is high, so it is difficult to meet the diverse needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Luminescent architectural paint, made of the following raw materials in parts by weight: 20 parts of epoxy resin, 20 parts of acrylic resin, 7 parts of nano silicon dioxide, 6 parts of methoxyaniline, 3.5 parts of citronellal , 7 parts of calcined kaolin, 17 parts of diatom mud, 1.1 parts of cellulose ether, 10 parts of active admixture, 12 parts of titanium dioxide, 3 parts of bridging agent, 6 parts of gelatin, 200 parts of Carborundum, 1.3 parts of ammonium persulfate, 0.8 parts of composite flame retardant and 3 parts of titanium dioxide.

Embodiment 2

[0015] Luminescent architectural paint, made of the following raw materials in parts by weight: 40 parts of epoxy resin, 40 parts of acrylic resin, 15 parts of nano silicon dioxide, 12 parts of methoxyaniline, 7 parts of citronellal , 10 parts of calcined kaolin, 21 parts of diatom mud, 1.8 parts of cellulose ether, 20 parts of active admixture, 22 parts of titanium dioxide, 5 parts of bridging agent, 13 parts of gelatin, 600 parts of Carborundum, 2.7 parts of ammonium persulfate, 1.5 parts of composite flame retardant and 7 parts of titanium dioxide.

Embodiment 3

[0017] Luminescent architectural paint, made of the following raw materials in parts by weight: 30 parts of epoxy resin, 30 parts of acrylic resin, 11 parts of nano silicon dioxide, 9 parts of methoxyaniline, 4.5 parts of citronellal , 8 parts of calcined kaolin, 19 parts of diatom mud, 1.5 parts of cellulose ether, 15 parts of active admixture, 17 parts of titanium dioxide, 4 parts of bridging agent, 9 parts of gelatin, 400 parts of Carborundum, 2 parts of ammonium persulfate, 1.1 parts of composite flame retardant and 5 parts of titanium dioxide.

[0018] By adding pearlescent powder, the present invention can effectively maintain brightness, high brightness lasts for a long time, and has strong weather and alkali resistance, can adapt to different climate changes, and at the same time is environmentally friendly, energy-saving, does not cause harm to the environment and human body, and satisfies market diversification Requirements: The present invention can effectively impr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light-emitting type building coating material, which is prepared from the following raw materials by weight: 20-40 parts of an epoxy resin, 20-40 parts of an acrylic resin, 7-15 parts of nano-silica, 6-12 parts of methoxyaniline, 3.5-7 parts of citronellal, 7-10 parts of calcined kaolin, 17-21 parts of diatom mud, 1.1-1.8 parts of cellulose ether, 10-20 parts of an active admixture, 12-22 parts of titanium dioxide, 3-5 parts of a bridging agent, 6-13 parts of gelatin, 200-600 parts of corundum, 1.3-2.7 parts of ammonium persulfate, 0.8-1.5 parts of a composite flame retardant agent, and 3-7 parts of titanium dioxide. According to the present invention, by adding the pearl powder, the brightness can be effectively maintained, and the high brightness lasting time is long; the obtained coating material has strong weathering resistance and strong alkali resistance, can adapt to different climate changes, has characteristics of environmental protection and energy saving, cannot damage environment and human body, and meets the diversified market requirements; and by using the diatom mud and the calcined kaolin, the stain resistance and the self-cleaning performance can be effectively improved.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to luminous building coatings. Background technique [0002] Coating is a material that can be coated on the surface of an object by different construction techniques to form a solid film with strong adhesion, certain strength and continuity. The film formed in this way is commonly called a coating film, also known as a paint film or a coating. Because most of the early paints used vegetable oil as the main raw material, they are also called paints. Now synthetic resins have mostly or completely replaced vegetable oils, so they are called paints. [0003] Architectural coatings include water-based architectural coatings and solvent-based architectural coatings. Solvent-based architectural coatings are restricted in architectural coatings because they release toxic solvents during the curing process and do not meet environmental protection requirements. However, due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D133/00C09D101/02C09D189/00C09D5/22C09D5/16C09D5/36C09D7/12
CPCC09D163/00C08K2201/011C08K2201/014C08L2205/035C09D5/1687C09D5/22C09D5/36C09D133/00C08L33/00C08L1/02C08L89/00C08K13/02C08K3/36C08K5/18C08K3/346C08K3/34C08L63/00
Inventor 朱杰
Owner RUGAO CHANGJIANG SCI & TECHCAL IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products