High strength plastic steel tile and preparation method thereof

A high-strength, plastic-steel technology, applied in the field of plastic-steel tiles, can solve the problems of insufficient physical strength and sound insulation effect of plastic-steel tiles, and achieve the effects of increasing rigidity, improving surface brightness, and simple preparation method.

Inactive Publication Date: 2017-12-01
温州月煌科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the physical strength and sound insulation effect of the current plastic-steel tiles are still insufficient, and further improvement is needed to increase the market competitiveness of plastic-steel tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of high-strength plastic-steel tile of the present embodiment comprises the following raw materials in parts by weight:

[0027] 60 parts of polyvinyl chloride resin, 20 parts of polyacrylic resin, 8 parts of urea-formaldehyde resin, 5 parts of nitrile rubber, 5 parts of light calcium carbonate, 4 parts of diatom mud, 3 parts of polyester fiber, 1 part of steel fiber, titanium dioxide 4 parts, 1 part of heat stabilizer, 2 parts of lubricant, 0.5 part of ACR processing modifier, 6 parts of CPE impact modifier, 0.5 part of light stabilizer, 0.5 part of fluorescent whitening agent.

[0028] In this embodiment, the thermal stabilizer is a mixture of calcium-zinc composite stabilizer, barium-zinc composite stabilizer, and potassium-zinc composite stabilizer.

[0029] In this embodiment, the lubricant is a mixture of polyethylene wax, calcium stearate, stearic acid, glyceryl stearate, and paraffin.

[0030] In this embodiment, the light stabilizer includes a UV absorb...

Embodiment 2

[0039] A kind of high-strength plastic-steel tile of the present embodiment comprises the following raw materials in parts by weight:

[0040] 65 parts of polyvinyl chloride resin, 25 parts of polyacrylic resin, 10 parts of urea-formaldehyde resin, 6 parts of nitrile rubber, 7 parts of light calcium carbonate, 4.5 parts of diatom mud, 4.5 parts of polyester fiber, 3 parts of steel fiber, titanium dioxide 4.5 parts, heat stabilizer 2 parts, lubricant 2.5 parts, ACR processing modifier 0.8 parts, CPE impact modifier 8 parts, light stabilizer 0.7 parts, fluorescent whitening agent 0.6 parts.

[0041] In this embodiment, the thermal stabilizer is a mixture of calcium-zinc composite stabilizer, barium-zinc composite stabilizer, and potassium-zinc composite stabilizer.

[0042] In this embodiment, the lubricant is a mixture of polyethylene wax, calcium stearate, stearic acid, glyceryl stearate, and paraffin.

[0043] In this embodiment, the light stabilizer includes a UV absorber a...

Embodiment 3

[0052] A kind of high-strength plastic-steel tile of the present embodiment comprises the following raw materials in parts by weight:

[0053] 70 parts of polyvinyl chloride resin, 30 parts of polyacrylic resin, 12 parts of urea-formaldehyde resin, 7 parts of nitrile rubber, 8 parts of light calcium carbonate, 5 parts of diatom mud, 6 parts of polyester fiber, 4 parts of steel fiber, titanium dioxide 5 parts, heat stabilizer 3 parts, lubricant 3 parts, ACR processing modifier 1 part, CPE impact modifier 10 parts, light stabilizer 1 part, fluorescent whitening agent 0.8 parts.

[0054] In this embodiment, the thermal stabilizer is a mixture of calcium-zinc composite stabilizer, barium-zinc composite stabilizer, and potassium-zinc composite stabilizer.

[0055] In this embodiment, the lubricant is a mixture of polyethylene wax, calcium stearate, stearic acid, glyceryl stearate, and paraffin.

[0056] In this embodiment, the light stabilizer includes a UV absorber and a free rad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high strength plastic steel tile and belongs to the technical field of plastic steel tiles. The high strength plastic steel tile comprises the following raw materials in parts by weight: 60-70 parts of polyvinyl chloride resin, 20-30 parts of polyacrylic resin, 8-12 parts of urea resin, 5-7 parts of nitrile rubber, 5-8 parts of light calcium carbonate, 4-5 parts of diatom ooze, 3-6 parts of polyester fibers, 1-4 parts of steel fibers, 4-5 parts of titanium dioxide, 1-3 parts of a heat stabilizer, 2-3 parts of a lubricant, 0.5-1 part of an ACR processing modifier, 6-10 parts of a CPE impact modifier, 0.5-1 part of a light stabilizer and 0.5-0.8 part of a flourescent brightener. The invention also discloses a preparation method of the high strength plastic steel tile. The high strength plastic steel tile disclosed by the invention is simple to prepare and has relatively excellent physical strength and sound-isolating effect.

Description

technical field [0001] The invention relates to the technical field of plastic-steel tiles, in particular to a high-strength plastic-steel tile and a preparation method thereof. Background technique [0002] New building materials are new types of building materials that are different from traditional bricks, tiles, limestone and other building materials. The scope of new building materials has been clearly defined in the industry, that is, new building materials mainly include new wall materials and new waterproof sealing materials. , new thermal insulation materials and decoration materials four categories. [0003] Plastic steel tile is a new type of building material that can replace color steel plates. It is also called pvc tile. The name is similar to the concept of plastic steel doors and windows. The main material is PVC, and other additives are added to improve product performance or processing performance, such as stabilize Agents, lubricants, fortifiers, etc. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L33/00C08L61/24C08L9/02C08L23/28C08L67/02C08L33/04C08K13/04C08K7/06C08K3/22C08K3/26C08K7/26C08K5/098E04D1/00
CPCC08L27/06C08K2003/2241C08K2003/265C08K2201/003C08K2201/004C08L2201/08C08L2205/02C08L2205/025C08L2205/035C08L2205/16E04D1/00C08L33/00C08L61/24C08L9/02C08L23/286C08L67/02C08L33/04C08K13/04C08K7/06C08K3/22C08K3/26C08K7/26C08K5/098
Inventor 刘东升
Owner 温州月煌科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com