High-elasticity environment-friendly polyvinyl chloride material composition as well as preparation method and application thereof

A material composition and polyvinyl chloride technology, applied in the field of new materials, can solve the problems of large environmental impact, poor thermal stability and high price, and achieve the effects of good gloss, improved stability and low cost

Active Publication Date: 2017-12-12
无锡宏义高分子材料科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PVC itself has poor thermal stability, and stabilizers need to be added during processing. At present, in order to ensure the mechanical properties of PVC hard materials, the PVC stabilizers used mainly include lead salts and organotin stabilizers, of which lead salts are poisonous and harmful. Heavy metal compounds have gradually withdrawn from the market; organotin stabilizers have a great impact on the environment during processing, and the price is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-elasticity environment-friendly polyvinyl chloride material composition as well as preparation method and application thereof
  • High-elasticity environment-friendly polyvinyl chloride material composition as well as preparation method and application thereof
  • High-elasticity environment-friendly polyvinyl chloride material composition as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The present embodiment is a highly elastic environment-friendly polyvinyl chloride material composition, which includes the following raw material components:

[0029]

[0030]

[0031] The preparation method of the above-mentioned highly elastic environment-friendly polyvinyl chloride material composition comprises the following steps:

[0032] Step 1: Weighing various raw materials according to the mass / number ratio;

[0033] Step 2: Add the PVC, stabilizer, processing aid, modifier, lubricant, filler and colorant into a hot mixer, and mix thoroughly for 5-10 minutes;

[0034] The third step: the uniformly mixed material in the second step is extruded through a star-shaped screw extruder at a temperature of 150-180°C, sheared and pre-plasticized, and further plasticized at a temperature of 130-160°C in an open mill, and then pressed by a calender The sheet is formed, drawn out by a stretching machine, cooled and shaped, and rolled to obtain a PVC hard material,...

Embodiment 2

[0036] The present embodiment is a highly elastic environment-friendly polyvinyl chloride material composition, which includes the following raw material components:

[0037] raw material

[0038] The preparation method of the above-mentioned highly elastic environment-friendly polyvinyl chloride material composition is the same as that in Example 1.

Embodiment 3

[0040] The present embodiment is a highly elastic environment-friendly polyvinyl chloride material composition, which includes the following raw material components:

[0041] raw material

[0042] The preparation method of the above-mentioned highly elastic environment-friendly polyvinyl chloride material composition is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-elasticity environment-friendly polyvinyl chloride material composition as well as a preparation method and application of the composition. The composition contains the following raw material components in parts by weight: 100 parts of polyvinyl chloride resin, 0.5-15 parts of a stabilizer, 0.5-20 parts of a processing aid, 1-20 parts of a mass modifier, 0.1-10 parts of a lubricant, 0.5-20 parts of a filler and 0-5 parts of a pigment, wherein the K value of the polyvinyl chloride resin is 60-65; the stabilizer is at least one of a zinc-calcium stabilizer and a magnesium-aluminum-zinc stabilizer. According to the high-elasticity environment-friendly polyvinyl chloride material composition, a tin-containing stabilizer or a lead-containing stabilizer is not used, and meanwhile, the high-elasticity environment-friendly polyvinyl chloride material composition has excellent elasticity and strength performance and is good in color and luster and low in cost.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to a high-elasticity environment-friendly polyvinyl chloride material composition and a preparation method and application thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the five general-purpose plastics, divided into soft and hard PVC, among which rigid PVC has been widely used in building materials, packaging materials, Christmas trees and other fields. European and American countries are used to adding Christmas trees to their families every Christmas to increase the festive atmosphere. The growth rate of natural trees is slow, and the price increases sharply every year, which cannot meet the market demand. The Christmas tree is made of PVC hard material, and its color, gloss and elastic recovery are similar to natural trees, and it is realistic and practical. [0003] According to market demand analysis, the market demand for PVC hard glue mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08L33/12C08K13/02C08K5/00
CPCC08L27/06C08L2205/025C08L2205/03C08L2205/035C08L51/04C08K13/02C08K5/005C08L33/12
Inventor 张焱赖仲平周程波刘宇亮凡永德张兴中张红杰高初林张秀林陈艳邹学义
Owner 无锡宏义高分子材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com