Quick repairing material and preparation method
A repair material and fast technology, applied in the field of rapid repair materials and preparation, can solve problems such as poor repair effect and poor toughness, and achieve the effect of fast hardening, high strength and toughness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0035] The preparation process of the quick repair material of the present invention comprises the following steps:
[0036] Step 1: Add sulfoaluminate cement, fly ash, intermediate sand and polyvinyl alcohol fiber into the mixing tank, and stir evenly at 300-600 rpm for 5-10 minutes;
[0037] Step 2: Add water and chemical admixture to the mixture in Step 1, and stir evenly at 1000-1500 rpm for 2-3 minutes. In parts by mass, 26-28 parts per 100 parts of sulphoaluminate cement portion of water;
[0038] Step 3: Reduce the rotational speed to 300-600 rpm, stir for 2-3 minutes, and then pour the mixture into a mold for curing to obtain a quick repair material.
Embodiment 1
[0040]When the service temperature of the quick repair material is -15°C, mix 1000g of sulphoaluminate cement and 1000g of intermediate sand, stir at 300-600rpm for 5 minutes, add 260g of water, 12g of naphthalene-based high-efficiency water reducer, and 15g of carbonic acid Lithium and 20g of sodium chloride, stirred at 1000-1500rpm for 2 minutes, then stirred at 300-600rpm for 2 minutes, then poured the evenly stirred mixture into a mold for curing, and the initial setting time was 24min, and the final setting time was 34min, 2h compressive strength of 16MPa, 7d compressive strength of 48MPa quick repair material.
Embodiment 2
[0042] When the service temperature of the quick repair material is -10°C, mix 1000g of sulphoaluminate cement and 1000g of intermediate sand, stir at 300-600rpm for 5 minutes, add 260g of water, 10g of naphthalene-based high-efficiency water reducer, and 12g of carbonic acid Lithium and 15g of calcium nitrate, stirred at 1000-1500rpm for 2 minutes, then stirred at 300-600rpm for 2 minutes, then poured the evenly stirred mixture into a mold for curing, and the initial setting time was 23 minutes, and the final setting time was 34 minutes , 2h compressive strength of 18MPa, 7d compressive strength of 51MPa quick repair material.
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com