Manufacturing method of glass wine bottle

A manufacturing method and glass technology, which is applied in the field of combination of glass and glass or other materials, can solve the problems of poor high-temperature and low-temperature resistance of wine bottles, glass is easy to cause harm to people, and the strength of wine bottles is not strong enough, etc. The effect of chemical temperature resistance, low cost and convenient operation

Inactive Publication Date: 2018-01-12
安徽九亿包装科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the production of domestic liquor bottles is mainly made of crystal white materials, high white materials, and ordinary white materials. The strength of the wine bottle is not strong enough, the anti-drop ability is weak, it is easy to break, and the broken glass is easy to cause harm to people; and the ordinary wine bottle has poor resistance to high temperature and low temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The invention relates to a method for manufacturing a glass wine bottle, comprising a raw material formula of the glass wine bottle, the raw material formula is composed of the following raw materials in parts by weight: 200 parts of crushed glass, 30 parts of three types of sand, 20 parts of soda ash, and 10 parts of limestone 1 part, 1 part of alumina, 0.5 part of calcium phosphate, 0.5 part of titanium oxide, 1 part of clarifying agent, 1 part of combustion enhancer.

[0028] The present invention is a kind of manufacturing method of glass wine bottle, described manufacturing method comprises the following steps:

[0029] Step 1: Clean the broken glass and crush it into granules with a crusher after cleaning.

[0030] Then send it to the freeze dryer for 0.5 hour, and take it out after the glass particles are dry without moisture;

[0031] Step 2: Mix the dried glass particles with three types of sand, soda ash, limestone, alumina, calcium phosphate, titanium oxide,...

Embodiment 2

[0035] The invention relates to a method for manufacturing a glass wine bottle, which includes a raw material formula for the glass wine bottle, and the raw material formula is composed of the following raw materials in parts by weight: 400 parts of crushed glass, 40 parts of three types of sand, 30 parts of soda ash, and 15 parts of limestone 1 part, 2 parts of alumina, 1 part of calcium phosphate, 1 part of titanium oxide, 1 part of clarifying agent, 1 part of combustion aid.

[0036] The present invention is a kind of manufacturing method of glass wine bottle, described manufacturing method comprises the following steps:

[0037] Step 1: Clean the broken glass and crush it into granules with a crusher after cleaning.

[0038] Then send it to the freeze dryer for 1 hour, and take it out after the glass particles are dry and free of moisture;

[0039] Step 2: Mix the dried glass particles with three types of sand, soda ash, limestone, alumina, calcium phosphate, titanium oxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a glass wine bottle. The method comprises a raw material formula of the glass wine bottle, wherein the raw material formula comprises the following raw materials: broken glass, third-class sand, sodium carbonate, limestone, alumina, calcium phosphate, titanium oxide, a clarifying agent and a combustion improver. The manufacturing method comprises the following steps: (1) breaking the glass into granular glass and performing freeze drying; (2) mixing the granular glass and other raw materials and performing ball-milling on the mixture into powder; (3) drying the powder and pouring the dried powder into a smelting furnace for melting, so as to obtain solution; (4) feeding the solution into a forming machine for forming, and cooling to room temperature, so as to obtain a finished product. The manufacturing method is reasonable in design and convenient in operation, the manufactured glass wine bottle is strong in breaking resistance, high temperature resistance and low temperature resistance and good in quality.

Description

technical field [0001] The invention belongs to the technical field of combining glass with glass or with other materials, and in particular relates to a method for manufacturing a glass wine bottle. Background technique [0002] In the production of glass products, the quality of medicinal glass products depends on the difference of raw materials. Raw materials can be divided into ordinary white materials, high white materials, super white materials, and crystal white materials, which directly affect the transparency of glass products. And brittleness, the better the quality of glass products produced by raw materials, the better. At present, the production of domestic liquor bottles is mainly made of crystal white materials, high white materials, and ordinary white materials. High-quality wine bottles are not strong enough, their drop resistance is weak, they are easy to break, and broken glass is easy to cause harm to people; and ordinary wine bottles have poor resistanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03C1/02C03B19/02
Inventor 朱立军
Owner 安徽九亿包装科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products