Floating colored sand self-leveling floor coating and preparation method thereof

A coating and colored sand technology, which is applied in the field of floating colored sand self-leveling floor coatings and its preparation, can solve problems such as high cost, pollute the environment, and endanger human health, and achieve the effects of improved physical and mechanical properties, simple operation, and convenient construction

Active Publication Date: 2018-01-16
HUNAN NAISSANT PLASTIC ENGINEERING MATERIALS CO LTD
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's industrial floor coatings are basically solvent-based and solvent-free epoxy floor coatings at present. Solvent-based epoxy floor coatings contain more organic solvents. These organic solvents are discharged into the atmosphere during the production and construction stages of coatings, polluting The environment, while endangering human health; solvent-free epoxy floor coatings contain a small amount of reactive diluents, commonly used reactive diluents are butyl glycidyl ether (with certain toxicity), self-leveling construction method, coating film thickness of 1 ~5mm, high cost and contains a small amount of volatile organic solvents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Floating colored sand self-leveling floor coating and preparation method thereof
  • Floating colored sand self-leveling floor coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0071] Various high-speed mixers are required in the preparation process of the paint, and spraying, flow coating and other methods are used for painting. In these processes, the paint will generate foam. The air in the foam will not only hinder the dispersion of pigments and fillers, but also make the utilization rate of the equipment insufficient and affect the output. The air bubbles generated during construction will cause surface defects of the paint film, which will not only damage the appearance, but also affect the corrosion resistance and weather resistance of the paint film. . Therefore, in order to prevent foaming during use, a defoamer should be added to the paint. The defoamer should have the following characteristics: 1. The surface tension of the defoamer should be smaller than that of the liquid to be defoamed; 2. The solubility in the liquid that needs to be defoamed should be as small as possible; 3. It should have good dispersibility ; 4. It cannot react wi...

Embodiment 1

[0095] Preparation method of component A:

[0096] a) Weigh the BPA type epoxy resin of Hunan Yuehua Chemical Co., Ltd. (brand name: CYD-127, epoxy equivalent g / eq is 185, hydrolyzable chlorine % (mass fraction) ≤ 0.10, viscosity mpa.s (25 ℃) greater than 9000 and less than 10000, volatile matter % (mass fraction) ≤% 0.20, chromaticity (Gardner number) ≤ 2.5) 140kg, BPA type epoxy resin of Hunan Yuehua Chemical Co., Ltd. (brand: CYD- 128, epoxy equivalent g / eq is 190, hydrolyzable chlorine % (mass fraction) ≤ 0.10, viscosity mpa.s (25 ° C) is greater than 12000 and less than 13000, volatile % (mass fraction) ≤ % 0.20, chromaticity ( Gardner number) ≤ 0.5) 220kg, Hunan Yuehua Chemical Co., Ltd.'s diluted epoxy resin (brand: CYD-115) 306kg, put into the dispersion tank, and disperse evenly at high speed;

[0097] b) Weigh 330kg of 100# floating colored sand in Guangzhou Haofeng sand field, put it into the dispersion tank, and disperse evenly at high speed;

[0098] c) Weigh 2k...

Embodiment 2

[0105] Preparation method of component A:

[0106] a) Weigh 140kg of BPA-type epoxy resin (brand: NPEL-127, viscosity mpa.s (25°C) greater than 9000 and less than 10000) from Nanya Epoxy Resin (Kunshan) Co., Ltd., Nanya Epoxy Resin (Kunshan) Co., Ltd. The company's BPA-type epoxy resin (brand: NPEL-128, viscosity mpa.s (25 ℃) greater than 12000 and less than 13000) 220kg, Nanya Epoxy Resin (Kunshan) Co., Ltd.'s diluted epoxy resin (brand: NPEK- 115) 306kg, put into the dispersion tank, and disperse evenly at high speed;

[0107] b) Weigh 330g of S80-100 mesh floating colored sand from Jiangmen Mingzhicai Chemical Co., Ltd., put it into the dispersion tank, and disperse evenly at high speed;

[0108] c) Weigh 2kg of EFKA's 2721 defoamer and 2kg of EFKA's 3777 leveling agent, and disperse evenly at high speed;

[0109] d) filtering the mixture obtained in c) for impurity removal and packaging.

[0110] Preparation method of component B:

[0111] a) Weigh 998kg of 3233 epoxy ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
amine valueaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a floating colored sand self-leveling floor coating and a preparation method thereof. The coating is composed of two components A and B. The component A comprises, by weight, 10to 40 parts of BPA-type epoxy resin, 5 to 30 parts of diluted epoxy resin, 5 to 30 parts of floating colored sand, 0.1-2 parts of a leveling agent and 0.1-2 parts of a defoaming agent. The componentB comprises, by weight, 50 to 100 parts of an alicyclic amine curing agent and 0.1 to 3 parts of an accelerator. In use, a mass ratio of the component A to the component B is 6 to 6.5: 1. The floatingcolored sand self-leveling floor coating is suitable for floor coating having high requirements on decoration, compressive resistance, abrasion resistance and load. The coating film has excellent compressive strength, wear resistance and chemical resistance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a floating colored sand self-leveling floor coating and a preparation method thereof. Background technique [0002] Floor coatings are a building material that has entered China in recent years. It has gradually been recognized and accepted by the majority of users, and is widely used in civil and industrial buildings and facilities such as hospitals, parking lots, sports fields, and pharmaceutical factory workshops. [0003] According to the classification of film-forming substances, floor coatings can be divided into inorganic, polyurethane, polyurea, acrylic, epoxy and other types. Among them, epoxy flooring is the most widely used, accounting for about 50% of the market share. [0004] Epoxy resin materials have excellent bonding strength to the surface of metal and non-metal materials, good dielectric properties, small shrinkage, good dimensional stability, and high hardness. Many e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/28C09D7/61
Inventor 章卫国谢静英范国栋
Owner HUNAN NAISSANT PLASTIC ENGINEERING MATERIALS CO LTD