Method for preparing shape memory cyanate ester prepreg

A cyanate ester and prepreg technology, which is applied in the field of preparation of shape memory prepregs for fiber composite materials, can solve the problems of inability to prepare prepregs, poor processability, single structure, etc., and achieve excellent mechanical properties and space resistance Effects of environmental performance, long storage period, and high physical and chemical properties

Inactive Publication Date: 2018-02-02
HARBIN INST OF TECH
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the existing cyanate ester resin has a single structure, high melting point, poor manufacturability, and cannot prepare prepregs, and provides a preparation method for shape memory cyanate ester prepregs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing shape memory cyanate ester prepreg
  • Method for preparing shape memory cyanate ester prepreg
  • Method for preparing shape memory cyanate ester prepreg

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0027] Embodiment 1: This embodiment is a preparation method of shape memory cyanate ester prepreg, which is specifically completed according to the following steps:

[0028] 1. Synthesis of cyanate ester prepolymer: put the cyanate ester monomer in a container, stir at a temperature of 80°C to 250°C until the cyanate ester monomer is completely melted, then add modifier I and polymerization Catalyst, the mass ratio of the modifier I to the cyanate monomer is (0.2~20):100, the mass ratio of the polymerization catalyst to the cyanate monomer is (0.0002~1):100, and in The temperature is 60°C-200°C, stirring and reacting at a constant temperature for 0.25h-10h, and then cooling to room temperature at a cooling rate of 0.5°C / min-5°C / min to obtain a modified cyanate resin prepolymer; the modified Agent Ⅰ is bisphenol A epoxy resin, novolac epoxy resin, p-aminophenol triglycidyl epoxy resin, amino tetrafunctional epoxy resin or bis-horse resin, polyethylene glycol, polyalkylene glyc...

specific Embodiment approach 2

[0039] Specific embodiment two: the difference between this embodiment and specific embodiment one is: the cyanate ester monomer described in step one is bisphenol A cyanate, dicyclopentadiene bisphenol type cyanate, bisphenol F Type cyanate or bisphenol M type cyanate. Others are the same as the first embodiment.

specific Embodiment approach 3

[0040] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is: in step one, stir at a temperature of 80°C-250°C and a stirring speed of 500r / min-2500r / min until the cyanate body completely melted. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing shape memory cyanate ester prepreg, relates to a method for preparing shape memory prepreg for a fiber composite material, and aims to solve the problemsthat a conventional cyanate ester resin is single in structure, relatively high in melting point and relatively poor in manufacturability and cannot be adopted to prepare prepreg. The method comprises the following steps: I, preparing a modified cyanate ester resin prepolymer; II, preparing a shape memory cyanate ester resin; III, preparing a cyanate ester resin colloid membrane; IV, performing preimpregnation, thereby obtaining the shape memory cyanate ester prepreg, wherein the continuous fiber is a one-way continuous fiber or a fiber fabric. The method has the advantages that not only is the shape memory cyanate ester prepreg successfully prepared from a cyanate ester monomer, but also the cyanate ester prepreg has the characteristic of shape memory, and an appropriate material is provided for preparing high-performance intelligent composite materials. The mehtod is mainly used for preparing shape memory cyanate ester prepreg.

Description

technical field [0001] The invention relates to a preparation method of a shape-memory prepreg for fiber composite materials. Background technique [0002] Cyanate resin (Cyanate resin referred to as CE) is a new type of high-performance resin containing two or more cyanate functional groups (-OCN), which has a high glass transition temperature (240 ° C ~ 280 ° C), low Dielectric constant (2.8~3.2) and dielectric loss (0.002~0.008), high thermal stability and low moisture absorption (<1.5%), these excellent properties make it meet the requirements of structural / functional composite materials in the aerospace field Strict requirements, it is a high-performance matrix resin with good prospects. However, due to the high melting point of the current cyanate ester monomer, the manufacturability is poor, and the cured product is relatively stable due to the presence of a triazine ring with a high degree of crosslinking, and often needs to be modified. Therefore, cyanate resin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J5/24C08L79/04C08G73/06
CPCC08G73/0644C08J5/24C08J2379/04
Inventor 冷劲松刘彦菊赵寒星兰鑫刘立武
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com