Method for preparing double medicine-carrying composite fibrous membrane through emulsion electrospinning technology

A composite fiber membrane, double drug-loading technology, which can be used in electrospinning, fiber processing, pharmaceutical formulations, etc., can solve unseen problems and achieve the effect of good cell compatibility

Active Publication Date: 2018-02-09
TIANJIN POLYTECHNIC UNIV
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no research on the fiber with "coexistence of silk beads" as a drug carrier.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing double medicine-carrying composite fibrous membrane through emulsion electrospinning technology
  • Method for preparing double medicine-carrying composite fibrous membrane through emulsion electrospinning technology
  • Method for preparing double medicine-carrying composite fibrous membrane through emulsion electrospinning technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A research method for preparing double drug-loaded composite fiber membranes by emulsion electrospinning comprises the following steps:

[0038] The polylactic acid (PLA) that takes by weighing 0.5g is dissolved in the mixed solution of 10mL acetone and DMF (V Ace =V DMF =5mL), stirred at 300rpm for 15min, and dissolved completely. Add 0.5mL of Span80, continue to stir for 20min, then add 0.005g of hydrophobic drug CPT, continue to stir, this is the O phase.

[0039] Weigh 1g of gelatin and dissolve it in 40mL of distilled water, heat and stir until completely dissolved, filter, add 10mL of emulsifier styrene-maleic anhydride copolymer, stir until it is completely miscible with the gelatin aqueous solution, and then add 0.005g of hydrophilic drug CPT , continue to stir, this is W phase.

[0040] Add the W phase into the O phase drop by drop, continue to stir for 2 hours, and the stirring speed is 900rpm. With the dropwise addition of the W phase, the system will comp...

Embodiment 2

[0066] The difference from Example 1 is that the hydrophobic model drug is replaced by sinomenine, and the other steps are the same.

Embodiment 3

[0068] The difference from Example 1 is that PEG is replaced by polyvinyl alcohol (PVA), the hydrophobic model drug is replaced by sinomenine, and other steps are the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing double medicine-carrying composite fibrous membrane through an emulsion electrospinning technology. The method includes the following steps that 1, a polylactic acid solution is prepared, an emulsifying agent I is added, the mixture is stirred evenly, hydrophobic medicine is added, an oil-phase solution is obtained after stirring, a gelatin solution is prepared, filtering is performed, an emulsifying agent II is added, the mixture is stirred evenly, hydrophilic medicine is added, and a water-phase solution is obtained after stirring; 2, under thecondition that stirring speed is 800 rpm-1000 rpm, the water-phase solution is dropwise added into the oil-phase solution, stirring is continued after dripping is completed, and then O / W emulsion is obtained; 3, PEG or PVA with the molecular weight being 8000 is added, and a spinning solution is obtained after even mixing is performed; 4, by the utilization of the electrostatic spinning method, the spinning solution is prepared into the double medicine-carrying composite fibrous membrane of a yarn and bead coexisting structure. In the method, the oil-in-water type emulsion is prepared througha phase reversal method; by adjusting polyethylene glycol, yarn-bead coexisting fibers can be prepared through emulsion electrospinning, the preparation method is simple, and the medicine-carrying effect is good.

Description

technical field [0001] The invention relates to the fields of textile and medicine, in particular to a method for preparing double drug-loaded composite fiber membranes by using emulsion electrospinning technology. Background technique [0002] Electrospinning is currently one of the most important technologies for preparing polymer fibers. It has attracted much attention in recent years. At present, a wide variety of fibers can be prepared, including organic, inorganic and organic / inorganic composite fibers, and are used in drug-loaded, biological Many fields such as dressings and tissue engineering scaffolds have the characteristics of porous structure and large specific surface area. [0003] Emulsion electrospinning replaces the traditional spinning solution with an oil-in-water emulsion or a water-in-oil emulsion, and can prepare bicomponent micro-nano fibers with a certain composite structure. Polylactic acid (PLA) is a synthetic aliphatic polyester polymer material w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H3/005D04H3/011D01D5/00A61K9/70A61K47/34A61K47/42
CPCA61K9/70A61K47/34A61K47/42D01D5/003D04H3/005D04H3/011
Inventor 张雯高燕张华李祥鹏岳盼李婵
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com