A technology of chlorinated polyethylene and cable materials, which is applied in circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problems of poor electrical properties and mechanical and physical properties of cable materials, achieve excellent electrical properties, and improve environmental performance , Improve the effect of vulcanization efficiency

Inactive Publication Date: 2018-03-09
嘉兴创奇电缆有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Aiming at the problems of poor electrical performance and mechanical and physical properties of existing cable materials, the present invention has been developed and designed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] It consists of the following components by weight: 34 parts of chlorinated polyethylene; 2 parts of EPDM rubber; 10 parts of active calcium carbonate; 20 parts of superfine talc; 10 parts of superfine kaolin; 1 part of carbon black; 1 part of bis-tert-butylperoxycumene; 1 part of triallyl isocyanurate; 3 parts of dioctyl adipate or diester of adipate; 3 parts Active magnesium oxide; 0.5 parts of calcium stearate; 0.5 parts of antioxidant, 0.5 parts of PE wax.

Embodiment 2

[0016] Comprising the following components by weight: 38 parts of chlorinated polyethylene; 5 parts of EPDM rubber; 15 parts of active calcium carbonate; 25 parts of superfine talc; 15 parts of superfine kaolin; carbon black; 1.5 parts of bis-tert-butylperoxycumene; 1.5 parts of triallyl isocyanurate; 6 parts of dioctyl adipate or diester of adipate; 6 parts of Activated magnesium oxide; 1 part of calcium stearate; 1 part of antioxidant, 1 part of PE wax.

Embodiment 3

[0018] Components comprising the following parts by weight: 36 parts of chlorinated polyethylene; 4 parts of EPDM rubber; 13 parts of active calcium carbonate; 22 parts of superfine talcum powder; 13 parts of superfine kaolin; Carbon black; 1.2 parts of cumene; 1.2 parts of triallyl isocyanurate; 4 parts of dioctyl adipate or diester of adipate; 5 parts of active Magnesium oxide; 0.8 parts of calcium stearate; 0.7 parts of antioxidant, 0.9 parts of PE wax.

[0019] The product prepared by the above method has the following technical indicators: tensile strength ≥ 10 N per square millimeter, elongation at break ≥ 50%, specific gravity ≤ 1.4 grams per cubic centimeter, Mooney viscosity ML (1+4 / 100) 70± 5. Sulfur change (T90 185℃*12min) for 3 minutes to 5 minutes and 30 seconds, oxygen index ≥ 33, oil aging test (121±2℃ / 18H) meets the requirements, oven aging test (136±2℃ / 168H) meets the requirements Requirements, no cracks in the ozone aging test (25°C / 24H 260PPM), and no crack...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chlorinated polyethylene cable material. The cable material comprises the following components in parts by weight: 34-38 parts of chlorinated polyethylene, 2-5 parts of ethylene-propylene-diene monomer, 10-15 parts of active calcium carbonate, 20-25 parts of ultra-fine talc powder, 10-15 parts of ultra-fine kaolin, 3-5 parts of carbon black, 1-1.5 parts of bis(tert-butylperoxyisopropyl)benzene, 1-1.5 parts of triallyl isocyanurate, 3-6 parts of dioctyl adipate or bis(2-ethylhexyl)adipate, 3-6 parts of active magnesium oxide, 0.5-1 part of calcium stearate, 0.5-1 partof an antioxidant and 0.5-1 part of PE wax. The cable material produced by utilizing the formula provided by the invention has good electrical performance and mechanical physical properties, and goodweathering resistance and high-temperature resistance.

Description

technical field [0001] The invention relates to a cable material, in particular to a chlorinated polyethylene cable material. Background technique [0002] Aiming at the problems of poor electrical properties and mechanical and physical properties of existing cable materials, the invention is developed and designed. Contents of the invention [0003] Aiming at the state of the prior art, the invention provides a chlorinated polyethylene cable material. The cable material produced by using the formula has good electrical properties, mechanical and physical properties, good weather resistance and high temperature resistance. [0004] In order to solve the above-mentioned technical problems, a technical solution adopted by the present invention is: a kind of chlorinated polyethylene cable material, comprising the following components by weight: 34-38 parts of chlorinated polyethylene; 2-5 parts of terpolymer Propylene rubber; 10-15 parts of activated calcium carbonate; 20-25...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L23/16C08L23/06C08K13/02C08K3/26C08K3/34C08K3/04C08K3/22C08K5/098H01B3/44
CPCH01B3/441C08L23/286C08L2201/08C08L2205/03C08L2203/202C08K2003/222C08K2003/265C08K2201/003C08L23/16C08L23/06C08K13/02C08K3/26C08K3/34C08K3/346C08K3/04C08K3/22C08K5/098
Inventor 巢生杨金元郑海林陈秀兰
Owner 嘉兴创奇电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap