Anti-calcification biological patch preparation method

A technology of biological patch and water injection, applied in the field of biomedical materials, can solve the problems of inability to enhance the antibacterial and bacteriostatic function of cross-linked materials, dark color of cross-linked materials, and difficulty in large-scale production, and achieves excellent anti-calcification ability, good Anti-degradation performance, excellent effect of hemostatic performance

Active Publication Date: 2018-03-23
SICHUAN UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, genipin is expensive, the color of the cross-linked material is dark, and it is not easy to achieve large-scale production, which limits its application
In addition, genipin has limitations in functionalization, it cannot enhance or endow cross-linked materials with better hemostatic, antibacterial and antibacterial functions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Weigh 100 grams of acellular porcine dermal matrix into the conical flask, add 100 grams of injection water into the conical flask, then place the conical flask in a temperature-controlled cradle filled with water, and turn on the heating switch , adjust the temperature to 37°C and shake for 10 minutes;

[0022] 2. Weigh 8 grams of epoxy chitosan quaternary ammonium salt and add it to the Erlenmeyer flask, shake for 20 minutes until the epoxy chitosan quaternary ammonium salt dissolves completely and penetrates into the acellular porcine dermal matrix;

[0023] 3. Weigh 10 grams of sodium hydroxide and dissolve it in 50 grams of water to obtain a sodium hydroxide solution;

[0024] 4. Slowly add sodium hydroxide solution dropwise, adjust the pH of the reaction solution to 10.0±0.5, keep warm and shake for 72 hours;

[0025] 5 Slowly add lactic acid dropwise, adjust the pH of the reaction solution to neutral, and pour off the reaction solution;

[0026] 6. Add 300 g...

Embodiment 2

[0030] 1. Weigh 10Kg fetal cowhide acellular dermal matrix into the drum, add 30Kg of water for injection, turn on the heating switch, adjust the temperature of the drum to 47°C, and rotate for 30 minutes;

[0031] 2. Add 2Kg epoxy chitosan quaternary ammonium salt to the drum and rotate for 60 minutes;

[0032] 3. Weigh 1Kg of sodium carbonate, slowly add it into the drum, and continuously check the pH value of the reaction, until the pH reaches 9.0-9.5, do not add sodium carbonate; then continue to rotate, and react for 24 hours;

[0033] 4. Weigh 1Kg of ammonium chloride, slowly add it into the drum, and continuously check the pH value of the reaction until the pH reaches 7.0±0.5, then pour off the reaction solution;

[0034] 5. Add 10Kg of water for injection, rotate for 120 minutes, and pour off the reaction solution;

[0035] 6. Then add 10Kg of water for injection, rotate for 120 minutes, and pour off the reaction solution;

[0036] 7. Add 1Kg RPMI-1640 medium, rotate...

Embodiment 3

[0040] 1. Weigh 50Kg of fetal calfskin acellular dermal matrix and put it into the drum, add 25Kg of water for injection, turn on the heating switch, adjust the temperature of the drum to 20°C, and rotate for 20 minutes;

[0041] 2. Add 1Kg epoxy chitosan quaternary ammonium salt to the drum and rotate for 30 minutes;

[0042] 3. Add boric acid-borax buffer solution, adjust the pH to 8.0±0.5, and rotate for 48 hours;

[0043] 4. Slowly add acetic acid dropwise, while continuously checking the pH value of the reaction until the pH reaches 7.0, then pour off the reaction solution;

[0044] 5. Add 50Kg of water for injection, rotate for 60 minutes, and pour off the reaction solution;

[0045] 6. Add 150Kg of water for injection, rotate for 120 minutes, and pour off the reaction solution;

[0046] 7. Add 10Kg RPMI-1640 medium, rotate for 2 hours, pour out the medium;

[0047]8. Add 250Kg of water for injection, wash for 2 hours, pour off the cleaning solution; then add 250Kg of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-calcification biological patch preparation method. Epoxy chitosan quaternary ammonium salt is added into a raw material namely acellular dermal matrix or small intestinal submucosa to prepare an anti-calcification biological patch through reaction for a while under an alkaline condition. Due to adoption of epoxy chitosan quaternary ammonium salt as a cross-linking agent, a cross-linking effect between a molecular epoxy group and acellular dermal matrix or small intestinal submucosa can be realized, and the defect that a traditional formyl group cross-linking method is prone to causing patch calcification is overcome. Due to introduction of the chitosan quaternary ammonium salt structure into the biological patch, great antibacterial, bacteriostasis and hemostasis functions are achieved. The biological patch prepared according to the method is a new-generation multifunctional implant material and can be widely applied to the field of medicine.

Description

technical field [0001] The invention relates to a preparation method of an anti-calcification biological patch, which is applied in the field of biomedical materials. Background technique [0002] Biological patch refers to a material that is taken from the same or heterogeneous tissue, removes various cells contained in the tissue after decellularization, and retains the three-dimensional framework structure of the extracellular matrix intact, and can be used to repair human soft tissue. As a bioengineered scaffold, biopatch can repair defective tissue through spatial induction and tissue replacement. Because all components that cause host immune rejection are removed, it has good tissue biocompatibility, and has been widely used in the fields of clinical incisional hernia and abdominal wall defect repair and reconstruction, and has achieved good results. [0003] In order to reduce the immunogenicity of biological patches, improve their degradation resistance, and improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/50A61L27/58A61L27/20A61L27/36
CPCA61L27/20A61L27/3629A61L27/3633A61L27/50A61L27/58A61L2400/04C08L5/08
Inventor 但年华但卫华陈一宁郑欣
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com