Preparation method of retardant paper with high durability

A technology of durable flame retardant and preparation steps, which is applied in the field of preparation of high durable flame retardant paper, which can solve the problems of poor flame retardant and durable performance of flame retardant paper, achieve enhanced electrostatic adsorption, increase retention rate, and long-lasting flame retardant effect Effect

Inactive Publication Date: 2018-04-27
陈建峰
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is to provide a preparation method of high-durability flame-retardant paper for the defect of poor flame-retardant durability of flame-retardant paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024]In parts by weight, 20 parts of aluminum chloride hexahydrate and 10 parts of magnesium chloride hexahydrate are dissolved in 80 parts of deionized water to obtain a salt solution, and 30 parts of sodium hydroxide and 30 parts of sodium carbonate are dissolved in 90 parts of deionized water , to obtain the alkali solution, seal the alkali solution and the salt solution respectively and put them into an ultrasonic cleaning machine for ultrasonic treatment for 15 minutes, and control the power of the ultrasonic cleaning machine to 180W; under the protection of nitrogen, 300mL of the salt solution and 200mL of the alkali solution were dripped at the same rate. Add it into the mist-making reactor, control the dropping rate to 8mL / min, and the pH of the reactor system is 10. After the dropwise addition, start the high-speed agitator and stir the reaction at a speed of 2000r / min for 30min to obtain a reaction slurry; Transfer the reaction slurry to a water bath, heat up to 90°C...

example 2

[0026] In parts by weight, 25 parts of aluminum chloride hexahydrate and 13 parts of magnesium chloride hexahydrate were dissolved in 85 parts of deionized water to obtain a salt solution, and 35 parts of sodium hydroxide and 32 parts of sodium carbonate were dissolved in 95 parts of deionized water , to obtain the alkali solution, seal the alkali solution and the salt solution respectively and put them into an ultrasonic cleaner for ultrasonic treatment for 17 minutes, and control the power of the ultrasonic cleaner to 190W; under the protection of nitrogen, 315mL of the salt solution and 210mL of the alkali solution were dripped at the same rate. Add it to the fog-making reactor, control the dropping rate to 9mL / min, and the pH of the reactor system is 10.5. After the dropping, start the high-speed stirrer and stir the reaction at a speed of 2250r / min for 33min to obtain a reaction slurry; Transfer the reaction slurry to a water bath, heat up to 95°C, and keep warm for 8.5 ho...

example 3

[0028] In parts by weight, 30 parts of aluminum chloride hexahydrate and 15 parts of magnesium chloride hexahydrate are dissolved in 90 parts of deionized water to obtain a salt solution, and 40 parts of sodium hydroxide and 35 parts of sodium carbonate are dissolved in 100 parts of deionized water , to obtain the alkali solution, seal the alkali solution and the salt solution respectively and put them into an ultrasonic cleaner for ultrasonic treatment for 20 minutes, and control the power of the ultrasonic cleaner to 200W; under the protection of nitrogen, 330mL of the salt solution and 220mL of the alkali solution were dripped at the same dropping rate. Add it to the fog-making reactor, control the dropping rate to 10mL / min, and the pH of the reactor system is 11. After the dropping, start the high-speed stirrer, stir the reaction at a speed of 2500r / min for 35min, and obtain the reaction slurry; Transfer the reaction slurry to a water bath, heat up to 100°C, keep warm and c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of preparation of flame retardant paper, and concretely relates to a preparation method of a piece of flame retardant paper with high durability. Magnesium-aluminium hydrotalcite is prepared, and twice filtering, paper making, and drying are carried out in order to obtain a piece of flame retardant paper with high durability; paper pulp fiber is treated, a two-layer membrane structure is formed on the surface, electrostatic absorption is enhanced between magnesium-aluminium hydrotalcite positive charges and paper pulp fiber negative charges, adhesive attraction of magnesium-aluminium hydrotalcite in the paper pulp fiber is improved, retention of magnesium-aluminium hydrotalcite is improved, flame retardation effects of the flame retardant paperis lasting, polyacrylamide can substantially increase steric hindrance of the paper, the surface of magnesium-aluminium hydrotalcite has positive electricity, organic polymer polyacrylamide has negative electricity, magnesium-aluminium hydrotalcite is uniformly dispersed in the paper pulp fiber, paper pulp fiber has enhanced physical anchoring effects in magnesium-aluminium hydrotalcite apertures,retention of magnesium-aluminium hydrotalcite which plays flame retardation effects in the flame retardant paper is improved, flame retardation and durability performance are improved, and the application prospects are wide.

Description

technical field [0001] The invention relates to the technical field of preparation of flame-retardant paper materials, in particular to a preparation method of high-durability flame-retardant paper. Background technique [0002] Paper and paper products are the most common items in human's daily life. They are generally made of plant fibers and are flammable substances. The flammability of plant fibers determines the flammability of paper products. Due to its flammability, it often causes fires. In order to eliminate fire hazards, the research on the flame retardant properties of paper products is also increasing day by day, and the research on flame retardant paper has also received people's attention. [0003] Flame retardant paper is made by adding flame retardants to the inside of paper or coating on the surface of paper through processing techniques such as pulp addition, impregnation and coating. Flame retardants achieve the purpose of flame retardancy by hindering ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D06M11/44D06M11/45D06M15/285
CPCD06M11/44D06M11/45D06M15/285D06M2200/30D21H27/00
Inventor 陈建峰何少雄张建初
Owner 陈建峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com