Hydrophilic polyester and preparation method thereof
A water polyester and hydrophilic technology, applied in the field of polymers, can solve the problems of easy yellowing of hydrophilic polyester, large viscosity drop, etc., achieve good product quality stability, low production energy consumption, and shorten high temperature residence time Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0046] Example 1
[0047] The hydrophilic polyester is prepared according to the preparation method provided by the present invention, and the steps are as follows:
[0048] (1) Prepare a slurry of terephthalic acid and ethylene glycol in a molar ratio of 1:1.15;
[0049] (2) The slurry prepared in step (1) is continuously added to the esterification system consisting of a vertical first esterification tank and a vertical second esterification tank for esterification reaction. The reaction temperature of the first esterification tank is The reaction temperature is 260°C, the reaction pressure is 500kPa, the reaction temperature of the second esterification tank is 265°C, and the reaction pressure is 120kPa. When the degree of polymerization of the ethylene terephthalate oligomer reaches 5, the oligomer is continuously and stably extracted from the esterification kettle through the oligomer pump;
[0050] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 235°...
Example Embodiment
[0053] Example 2
[0054] The hydrophilic polyester is prepared according to the preparation method provided by the present invention, and the steps are as follows:
[0055] (1) Prepare a slurry with terephthalic acid and ethylene glycol in a molar ratio of 1:1.05;
[0056] (2) The slurry prepared in step (1) is continuously added to the esterification system consisting of a vertical first esterification tank and a vertical second esterification tank for esterification reaction. The reaction temperature of the first esterification tank is The reaction temperature is 275°C, the reaction pressure is 400kPa, the reaction temperature of the second esterification tank is 275°C, and the reaction pressure is 200kPa. When the degree of polymerization of ethylene terephthalate oligomer reaches 8, the oligomer is continuously and stably extracted from the esterification kettle through the oligomer pump;
[0057] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 250°C ...
Example Embodiment
[0060] Example 3
[0061] The hydrophilic polyester is prepared according to the preparation method provided by the present invention, and the steps are as follows:
[0062] (1) Prepare a slurry of terephthalic acid and ethylene glycol in a molar ratio of 1:2.0;
[0063] (2) The slurry prepared in step (1) is continuously added to the esterification system composed of a vertical esterification kettle for esterification reaction. The reaction temperature of the esterification kettle is 240°C and the reaction pressure is 100kPa. When the degree of polymerization of the ethylene glycol dicarboxylate oligomer reaches 1, the oligomer is continuously and stably extracted from the esterification kettle through the oligomer pump;
[0064] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 200°C through a heat exchanger with polyethylene glycol with a molecular weight of 200 and glycerol / phosphorous acid added online Triphenyl ester / N,N'-bis-(3-(3,5-di-tert-butyl-4-hy...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap