Aqueous antistatic acrylate waterproof coating and preparation method thereof

An acrylate and waterproof coating technology, applied in conductive coatings, coatings, etc., can solve problems such as poor antistatic properties, unsatisfactory mechanical properties, and limit the promotion and application of coatings, and achieve the effect of excellent electrical conductivity and mechanical properties.

Inactive Publication Date: 2018-06-08
SICHUAN SHUYANG WATERPROOF MATERIAL
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Acrylate waterproof coating is a one-component water-based architectural waterproof coating made of acrylate emulsion as the main raw material, adding appropriate amount of high-quality fillers and additives. Because of its excellent weather resistance and ultraviolet resistance, it can There is basically no change in performance within the temperature range. The waterproof layer has both decoration and heat insulation effects. It is environmentally friendly, non-toxic, and easy to construct. It is suitable for waterproof and anti-seepage projects such as roofs, walls, toilets, and basements. It can also be used as Ad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous antistatic acrylate waterproof coating and preparation method thereof
  • Aqueous antistatic acrylate waterproof coating and preparation method thereof
  • Aqueous antistatic acrylate waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation method of above-mentioned a kind of waterborne antistatic acrylate waterproof paint comprises the following steps:

[0034] (1) In terms of parts by mass, take 40 parts of acrylate emulsion, 3 parts of graphene oxide, 7 parts of emulsified environmental protection plasticizer, 1.5 parts of defoamer, 3 parts of dispersant, 1.5 parts of wetting agent, 1.5 parts of more Functional additive APM-95, 1 part of preservative, 1.5 parts of thickener diluent, 37 parts of heavy calcium carbonate, 15 parts of quartz powder and 6 parts of water, set aside;

[0035] (2) Add graphene oxide and water into the dispersion tank and stir evenly, then add acrylate emulsion, defoamer, dispersant, wetting agent, multifunctional additive APM-95 and preservative in turn, and 400r / min Stir at a high speed for 15 minutes, then slowly add emulsified environmentally friendly plasticizers, keep the speed constant, continue stirring for 10 minutes, increase the speed to 1000r / min, and...

Embodiment 2

[0037] The preparation method of above-mentioned a kind of waterborne antistatic acrylate waterproof paint comprises the following steps:

[0038] (1) In terms of parts by mass, take 35 parts of acrylate emulsion, 0.2 parts of graphene oxide, 3 parts of emulsified environmental protection plasticizer, 1 part of defoamer, 2 parts of dispersant, 1 part of wetting agent, and 1 part of more Functional additive APM-95, 0.5 parts of antiseptic, 0.5 parts of thickener diluent, 35 parts of heavy calcium carbonate, 10 parts of quartz powder and 4 parts of water, set aside;

[0039] (2) Add graphene oxide and water into the dispersion tank and stir evenly, then add acrylate emulsion, defoamer, dispersant, wetting agent, multifunctional additive APM-95 and preservative in turn, and 300r / min Stir at a high speed for 15 minutes, then slowly add emulsified environmentally friendly plasticizers, keep the speed constant, continue to stir for 10 minutes, increase the speed to 900r / min, and sti...

Embodiment 3

[0041] The preparation method of above-mentioned a kind of waterborne antistatic acrylate waterproof paint comprises the following steps:

[0042] (1) In terms of parts by mass, take 45 parts of acrylate emulsion, 5 parts of graphene oxide, 12 parts of emulsified environmental protection plasticizer, 2 parts of defoamer, 4 parts of dispersant, 2 parts of wetting agent, 2 parts of more Functional additive APM-95, 1.5 parts of antiseptic, 3 parts of thickener diluent, 40 parts of heavy calcium carbonate, 20 parts of quartz powder and 8 parts of water, set aside;

[0043] (2) Add graphene oxide and water into the dispersion tank and stir evenly, then add acrylate emulsion, defoamer, dispersant, wetting agent, multifunctional additive APM-95 and preservative in sequence, and with 500r / min Stir at a high speed for 15 minutes, then slowly add emulsified environmentally friendly plasticizers, keep the speed constant, continue stirring for 10 minutes, increase the speed to 1100r / min, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of building waterproof materials and particularly relates to an aqueous antistatic acrylate waterproof coating and a preparation method thereof. The aqueous antistatic acrylate waterproof coating comprises, by mass, 35 to 45 parts of an acrylate emulsion, 0.2 to 5 parts of graphene oxide, 3 to 12 parts of an emulsified eco-friendly plasticizer, 1 to 2 parts of adefoamer, 2 to 4 parts of a dispersant, 1 to 2 parts of a wetting agent, 0.5 to 1.5 parts of a preservative, 0.5 to 3 parts of a thickener diluent, 35 to 40 parts of heavy calcium carbonate, 10 to 20parts of quartz powder, 1 to 2 parts of a multifunctional aid APM-95 and 4 to 8 parts of water. The aqueous antistatic acrylate waterproof coating significantly improves the antistatic performances ofa waterborne acrylic waterproof coating and has tensile strength of greater than or equal to 1.22MPa and the elongation at break of greater than or equal to 359%.

Description

technical field [0001] The invention relates to the field of waterproof coatings, in particular to a water-based antistatic acrylate waterproof coating and a preparation method thereof. Background technique [0002] Acrylate waterproof coating is a one-component water-based architectural waterproof coating made of acrylate emulsion as the main raw material, adding appropriate amount of high-quality fillers and additives. Because of its excellent weather resistance and ultraviolet resistance, it can There is basically no change in performance within the temperature range. The waterproof layer has both decoration and heat insulation effects. It is environmentally friendly, non-toxic, and easy to construct. It is suitable for waterproof and anti-seepage projects such as roofs, walls, toilets, and basements. It can also be used as Adhesives or exterior wall decorative coatings, but currently there are problems such as unsatisfactory mechanical properties and poor antistatic prop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/24C09D7/61C09D7/63C09D7/65
CPCC08K2003/265C08K2201/001C08L2201/04C09D5/24C09D133/04C08L71/02C08K13/04C08K7/00C08K3/26C08K3/36C08K5/17
Inventor 杜勇
Owner SICHUAN SHUYANG WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap