HDPE chemical bonding type self-adhesive waterproof coiled material

A self-adhesive waterproof membrane and chemical bonding technology, applied in the direction of adhesive types, adhesives, polymer adhesive additives, etc., can solve the problems of inconvenient construction on site and easy bonding of construction personnel, and achieve easy construction, The effect of high peel strength

Active Publication Date: 2018-06-22
武汉市恒星防水材料有限公司
View PDF9 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the specific construction, after the isolation film is torn off, because the hot-melt pressure-sensitive adhesive of the adhesive layer has too strong adhesion, it is easy to bond the construction personnel, which causes a lot of inconvenience to the on-site construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] First, prepare the self-adhesive layer, and its preparation process is as follows:

[0028] Weigh the following amounts of raw material components:

[0029] Diblock SDS thermoplastic elastomer 21g, wherein, the mass of diblock S-D in the diblock SDS thermoplastic elastomer accounts for 10%;

[0030] SIS thermoplastic elastomer 2g, wherein, SIS thermoplastic elastomer Shore hardness is 60;

[0031] C5 petroleum resin 35g;

[0032] C5 petroleum resin 3g;

[0033] Terpene phenolic resin 4g;

[0034] Polyisobutylene 1g, polyisobutylene molecular weight distribution: 3.0, Staudinger index: 21.5, dynamic viscosity at 160°C: 50000 Pa S;

[0035] Naphthenic oil 10g;

[0036] Anti-aging agent 1g,

[0037] Among them, the mass ratio of each component of anti-aging agent is: 2,6-di-tert-butyl-4-methylphenol: dioctadecyl alcohol pentaerythritol diphosphite: hindered amine light stabilizer: ultraviolet absorber =1:1.5:1.5:1.5.

[0038] Secondly, prepare the self-adhesive lay...

Embodiment 2

[0047] First, prepare the self-adhesive layer, and its preparation process is as follows:

[0048] Weigh the following amounts of raw material components:

[0049]Diblock SDS thermoplastic elastomer 29g, wherein, the mass of diblock S-D in the diblock SDS thermoplastic elastomer accounts for 17.5%;

[0050] SIS thermoplastic elastomer 4g, wherein, SIS thermoplastic elastomer Shore A hardness is 70;

[0051] C5 petroleum resin 42.5g;

[0052] C5C9 copolymerized petroleum resin 4g;

[0053] Darmar resin 4.5g;

[0054] Polyisobutylene 8g, polyisobutylene molecular weight distribution: 3.0, Staudinger index: 28, dynamic viscosity at 160°C: 90000m Pa S;

[0055] Naphthenic oil 17.5g;

[0056] Anti-aging agent 2g,

[0057] Among them, the mass ratio of each component of anti-aging agent is: 2-tert-butyl-6-(3-tert-butyl-5-methyl-2-hydroxyphenyl)-4-methylphenyl acrylate: polymer Type phosphite or multifunctional phosphite: hindered amine light stabilizer: ultraviolet absorber =...

Embodiment 3

[0067] First, prepare the self-adhesive layer, and its preparation process is as follows:

[0068] Weigh the following amounts of raw material components:

[0069] Diblock SDS thermoplastic elastomer 37g, wherein, the mass of diblock S-D in the diblock SDS thermoplastic elastomer accounts for 25%;

[0070] SIS thermoplastic elastomer 6g, wherein, SIS thermoplastic elastomer Shore A hardness is 80;

[0071] C5 petroleum resin 50g;

[0072] C9 petroleum resin 5g;

[0073] Terpene resin 5g;

[0074] Polyisobutylene 15g, polyisobutylene molecular weight distribution: 3.0, Staudinger index: 33.0, dynamic viscosity at 160°C: 130000m Pa S;

[0075] Naphthenic oil 25g;

[0076] Anti-aging agent 4g,

[0077] Secondly, prepare the self-adhesive layer, comprising the following steps:

[0078] Step 1: Heat the reactor to 165°C, add naphthenic oil, polyisobutylene and terpene resin according to the amount, and stir until the materials melt;

[0079] Step 2: Add C5 petroleum resin, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an HDPE chemical bonding type self-adhesive waterproof coiled material. According to the invention, through arrangement of a self-adhesive adhesive layer and a matrix, the adhesive layer can be firmly adhered to a concrete layer and has high peel strength; through arrangement of an isolation layer and a non-adhesive coating layer, easy construction and no adhesion to construction personnels are realized; through addition of a diblock SDS thermalplastic elastomer and an SIS thermoplastic elastomer, a hot-melt pressure-sensitive adhesive has meltability and thermoplasticity of plastic and elasticity and toughness of rubber; through limitation of shore hardness of the SIS thermoplastic elastomer, the hot-melt pressure-sensitive adhesive has meltability and thermoplasticity of the plastic and elasticity and toughness of the rubber; through limitation of the type of a compatibilizer, a product has widened construction temperature range; through limitation of carbon-5petroleum resin, the waterproof coiled material has good construction temperature, and the hot-melt pressure-sensitive adhesive has better adhesiveness; and through limitation of the type of a tackifier, the hot-melt pressure-sensitive adhesive can maintain good peel strength at a normal temperature.

Description

technical field [0001] The invention relates to a waterproof coiled material, in particular to a HDPE chemically bonded self-adhesive waterproof coiled material. Background technique [0002] Since the 21st century, pre-paved anti-adhesive construction technology has been mostly used in the construction of waterproof membrane paving in subway tunnels. During pre-paving anti-adhesive construction, it is necessary to tear off the surface isolation film, and then pour the freshly mixed liquid post-cast concrete on it, and wait for the post-cast concrete to solidify. However, in the specific construction, after the isolation film is torn off, because the hot-melt pressure-sensitive adhesive of the adhesive layer has too strong adhesion, it is easy to bond the construction personnel, which causes a lot of inconvenience to the on-site construction. Contents of the invention [0003] In view of this, the present invention proposes a HDPE chemically bonded self-adhesive waterproo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/38C09J157/02C09J11/08C09J11/06
CPCC08L2205/025C08L2205/035C09J11/06C09J11/08C09J157/02C09J2423/046C09J2301/122C09J2301/302C09J2301/408C08L53/02C08L23/22C08L91/00C08K5/13C08K5/524C08L57/02C08K5/1345C08L45/00
Inventor 张卫张帆
Owner 武汉市恒星防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com