Anti-cracking unsaturated polyester paint and preparation method thereof

An unsaturated polyester paint technology, applied in the preparation of anti-cracking unsaturated polyester paint, in the field of anti-cracking unsaturated polyester paint, it can solve the problems of easy cracking of thick coating and insufficient toughness of the coating film, and achieve the effect of the board surface Good, fullness, flexibility

Inactive Publication Date: 2018-06-29
ZHONGSHAN DOIT PAINT CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the shortcomings of conventional PE unsaturated polyester products, such as insufficient film toughness and easy cracking of thick coatings, and provide a PE paint that can adapt to large changes in temperature difference and has high construction tolerance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-cracking unsaturated polyester paint and preparation method thereof
  • Anti-cracking unsaturated polyester paint and preparation method thereof
  • Anti-cracking unsaturated polyester paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Anti-cracking unsaturated polyester paint raw materials: 35 parts of unsaturated polyester resin, 5 parts of short oil modified alkyd resin, 0.2 part of dispersant, 0.3 part of defoamer, 0.5 part of fumed silica, 8 parts of titanium dioxide, Zinc stearate 2 parts, talcum powder 20 parts, calcium carbonate 20 parts, leveling agent 0.2 parts, styrene 3 parts, ethyl acetate 5 parts.

[0023] The preparation steps of anti-cracking unsaturated polyester paint:

[0024] (1) After mixing unsaturated polyester resin, short oil modified alkyd resin, dispersant and defoamer, disperse at 800r / min for 5min;

[0025] (2) Add fumed silica, titanium dioxide, talcum powder, calcium carbonate, zinc stearate, and disperse at 1500r / min for 20min;

[0026] (3) After the fineness is ≤55μm detected by the fineness plate, add leveling agent, styrene and ethyl acetate, and disperse at 800r / min for 5min to obtain unsaturated polyester paint 1#.

[0027] During construction, mix the above-ment...

Embodiment 2

[0029] Anti-cracking unsaturated polyester paint raw materials: 30 parts of unsaturated polyester resin, 10 parts of short oil modified alkyd resin, 0.2 part of dispersant, 0.3 part of defoamer, 0.5 part of fumed silica, 8 parts of titanium dioxide, Zinc stearate 2 parts, talcum powder 30 parts, calcium carbonate 15 parts, leveling agent 0.2 parts, styrene 3 parts, ethyl acetate 5 parts.

[0030] The preparation steps of anti-cracking unsaturated polyester paint:

[0031] (1) After mixing unsaturated polyester resin, short oil modified alkyd resin, dispersant and defoamer, disperse at 800r / min for 5min;

[0032] (2) Add fumed silica, titanium dioxide, talcum powder, calcium carbonate, zinc stearate, and disperse at 1500r / min for 20min;

[0033] (3) After the fineness is less than or equal to 55 μm detected by the fineness plate, add leveling agent, styrene and ethyl acetate, disperse at 800r / min for 5min, and disperse evenly to obtain unsaturated polyester paint 2#.

[0034]...

Embodiment 3

[0036] Anti-cracking unsaturated polyester paint raw materials: 40 parts of unsaturated polyester resin, 10 parts of short oil modified alkyd resin, 0.2 part of dispersant, 0.3 part of defoamer, 0.5 part of fumed silica, 8 parts of titanium dioxide, 2 parts of zinc stearate, 10 parts of talc, 35 parts of calcium carbonate, 0.2 parts of leveling agent, 3 parts of styrene, 5 parts of ethyl acetate.

[0037] The preparation steps of anti-cracking unsaturated polyester paint:

[0038] (1) Disperse unsaturated polyester resin, short oil modified alkyd resin, dispersant and defoamer at 800r / min for 5min;

[0039] (2) Add fumed silica, titanium dioxide, talcum powder, calcium carbonate TD-230, zinc stearate, and disperse at 1500r / min for 20min;

[0040] (3) After the fineness is ≤55μm by the fineness plate, add leveling agent, styrene, ethyl acetate, and disperse at 800r / min for 5min to get unsaturated polyester paint 3#.

[0041] During construction, mix the above-mentioned unsatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-cracking unsaturated polyester paint and a preparation method thereof. The anti-cracking unsaturated polyester paint is prepared from the following raw materials in partsby mass: 25 to 40 parts of unsaturated polyester resin, 5 to 10 parts of short oil modified alkyd resin, 0.1 to 1 part of dispersing agents, 0.1 to 1 part of anti-foaming agents, 0.1 to 1 part of leveling agents, 0.3 to 0.6 part of fused silicon oxide, 40 to 60 parts of pigments and fillers and 5 to 30 parts of solvents. The anti-cracking unsaturated polyester paint has the advantages that the product toughness is good; the internal stress release is fast; the problem of cracking at the later period can be greatly reduced to the maximum degree. Compared with the PE paint in the market, the paint has the advantages that the use tolerance is better; the anti-cracking unsaturated polyester paint is very suitable for being used as easy-shrinkage substrates suitable for Northeast China regionswith great diurnal temperature variation; for other performance, the smell is lower than that of other PE paint in the market; the grinding is easy; the plate surface effect is good; the fullness degree is high; the glossiness is higher; the comprehensive performance is excellent.

Description

technical field [0001] The invention relates to an unsaturated polyester paint, in particular to an anti-cracking unsaturated polyester paint, and also relates to a preparation method of the anti-cracking unsaturated polyester paint. Background technique [0002] In the mature furniture production industry, the degree of centralized production is becoming more and more obvious, and the efficiency of furniture production and shipment has become one of the required indicators pursued by many enterprises. The coating film made of unsaturated polyester resin furniture paint (referred to as "PE paint") can be thickly coated at one time, and it takes longer to use polyurethane paint (PU paint) or nitro (NC) paint and water-based, UV, etc. Short construction drying time and multiple spraying and polishing, one thick coating of PE paint improves production efficiency and greatly shortens the delivery cycle, so PE unsaturated polyester paint is widely favored by furniture companies. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D7/61C09D7/63C09D7/65
CPCC09D167/06C08K2003/265C08L67/08C08K13/02C08K3/36C08K3/34C08K5/098C08K3/26
Inventor 沈金星李卫强周志盛方涣润甘文华张海星
Owner ZHONGSHAN DOIT PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products